磷石膏晶须白度高、密度小,具有成为造纸颜料的可能.本文将磷石膏晶须作为涂布颜料,研究制备60%固含量的低黏度且涂布效果好的晶须涂料.通过分析晶须涂料的性质和涂布纸的性能发现,相比羧基丁苯胶乳和苯丙胶乳,在同等条件下添加占涂料总固含量12%的丙烯酸胶乳胶黏剂,涂布纸的表面强度较高且涂料黏度较低.在胶黏剂占涂料固含量不变的情况下,添加2%的阳离子糊化淀粉代替胶黏剂,有利于提高涂布纸的表面强度,但平滑度和白度有所降低.添加质量为绝干颜料质量5%的尿素作为晶须涂料的降黏剂,涂料的黏度可达824 m Pa·s,降黏效果较明显.晶须涂料与碳酸钙涂料相比,虽然涂布纸的光泽度较低,但油墨吸收值和表面强度较高.     

阳离子淀粉改性碳酸钙在纸页抄造中的应用

采用新工艺使形成凝胶的阳离子淀粉颗粒均匀包覆沉淀碳酸钙(PCC)表面,得到一种新型的改 性PCC,并对改性PCC的各个性质尤其对纸页的增强效果进行研究。探索两种PCC的改性方法,一种是 使用糊化好的高浓度淀粉溶液包裹PCC;另一种是先混合未糊化淀粉乳液和PCC,再蒸煮混合物。结 果表明：第1种方法淀粉溶解率较低,并且淀粉糊化浓度对淀粉溶解和手抄片各种性质有较大影响。 分别对糊化淀粉溶液质量分数为20 %、30 %、40 %、50 %、60 %的淀粉进行试验比较,发现糊化淀 粉溶液质量分数30 %改性PCC不仅具有均匀的颗粒大小,较低的淀粉溶解率,而且抗张指数提高41.1 %,耐破指数提高50 %,表面强度提高45.3 %,灰分提高37.5 %。     

改性淀粉-合成树脂聚合物乳液的性能测试

改性淀粉-合成树脂聚合物乳液是一种性能较好、价廉、无污染的多用途产品.参考合成树脂乳液的性能测试方法,结合改性淀粉-合成树脂乳液的性能,探讨该共聚乳液的性能测试方法,重点讨论了物理性能、工艺性能、力学性能、化学性能的测试.以乳液基涂料、胶黏剂为例,对乳液性能测试项目及测试方法的选择进行了比较说明.     

转移式涂布放卷机线速度协调张力控制系统

在转移式涂布放卷机工作过程中,纸张需要恒定的张力。放卷张力不稳定会给后级张力造成干扰,出现走纸不稳。此情况极易使纸张出现皱褶、涂料不匀而成为废品。针对以上情况,分析了转移式涂布纸加工过程中放卷电机的工作性能,给出了一种线速度协调式恒张力控制系统模型,提出了由PLC和西门子6RA70直流电机调速器对系统的实现方法。系统利用6RA70自带的S00软件完成控制系统的计算,使系统结构更简单,放卷张力稳定。     

Nd_20_3表面包覆对LiC_oO_2电化学性能与结构的影响

采用研磨的方法以稀土氧化物Nd_rO_3对LiCoO_2进行表面修饰.扫描电镜(SEM)表明,Nd_2O_3包覆在LiC_oO_2的表面.对包覆后的LiC_oO_2:正极材料的电化学性能进行了研究,充放电循环测试表明,表面包覆2%Nd_rO_3的LiC_oO_2正极材料的电化学性能最好,以1 C倍率充放电循环(3.0～4.4 V)80周后,放电容量仍可达到141 mAh/g.X射线衍射(XRD)和循环伏安(CV)测试表明,包覆后提高了LiC_oO_2的结构稳定性.     

磷酸铁锂/石墨烯复合正极材料的制备与电化学性能研究

介绍了一种将石墨烯(Graphite)引入锂离子电池正极材料磷酸铁锂(LiFePO_4)中获得LiFePO_4/graphite复合材料的制备方法。首先以碳酸锂、草酸亚铁、磷酸氢二铵和葡萄糖为原材料,采用高温固相法合成了碳包覆的LiFePO_4前躯体,再通过固相粉体混合的工艺加入不同百分比的石墨烯,制备出磷酸铁/石墨烯锂离子电池正极复合材料;对所制备的复合材料组装成纽扣电池进行性能测试;结果表明:复合材料的电化学性能显著提高,在0.1C放电倍率条件下,LiFePO_4+1wt%graphite复合材料的首次放电容量从LiFePO_4基体材料的131.75mAh/g提高到146.51mAh/g,LiFePO_4+1wt%graphite复合材料的充电性能和放电性能分别提高了5.8%和4.8%。     

不同预处理方法对棉秆酶水解的影响

研究稀硫酸法、亚硫酸法、亚硫酸盐法预处理的化学药品添加量对棉秆酶水解的影响,对预处理前后的棉秆进行扫描电镜观察,并对3种方法进行了比较.在固液比1∶4、温度180,℃、保温20,min的预处理条件下,纤维素酶用量(相对于绝干底物)10 U/g、纤维二糖酶用量(相对于绝干底物)3.6 U/g的酶水解条件下,稀硫酸法预处理在98%浓硫酸添加量为5.52%时,棉秆的酶水解转化率为42.63%;亚硫酸法预处理在亚硫酸添加量7%时,棉秆的酶水解转化率为81.25%;亚硫酸盐法预处理在98%浓硫酸添加量0.92%、亚硫酸氢钠添加量为8%时,棉秆的酶水解转化率为70.06%.     

可拓评价在线路板回收方法综合性能比较中的应用

为了能够综合评价现有印刷线路板回收方法的优劣,文章对超临界CO2法、热处理法、机械处理法及化学溶剂法4种印刷线路板的回收方法的特点进行了研究.将可拓评价方法引入到由专家打分而定的全定性指标、既有最大值最优又有最小值最优的印刷线路板回收方法综合性能评价中,从环境、能源、资源、经济4种属性出发,建立了含有16个指标项的评价体系,得到了印刷线路板回收方法的综合性能排序,为印刷线路板回收的方法选用及性能改进提供了参考依据.     

建筑外墙隔热保温涂料的实验研究

研究了建筑外墙隔热保温涂料的制备及隔热性能的测试,采用太阳热反射模拟试验方法,研究不同功能填料(粉煤灰漂珠、硅藻土以及沸石分子筛)的添加量及涂膜厚度对涂料隔热性能的影响,并通过对功能填料进行SEM表征及导热系数的测定,分析比较以上几种功能填料的隔热效果。结果表明:制备的涂料均符合国家标准;涂层厚度对涂料的隔热性能影响相对较小;粉煤灰漂珠、硅藻土和沸石分子筛对涂料的隔热性能都有一定影响,其中沸石分子筛添加量为9%的隔热效果最好,其平衡温度比空白降低了12℃。     

乳化剂对SAE表面施胶剂合成及应用的影响

乳化剂是乳液聚合体系的重要组成部分,并对聚合物乳液的应用性能具有一定的影响。以苯乙烯丙烯酸酯(SAE)表面施胶剂的合成为例,研究了乳化剂的用量对SAE合成及性能的影响。以苯乙烯、丙烯酸丁酯和丙烯酸为单体,硫酸亚铁-过氧化氢作为引发体系,十二烷基硫酸钠(SDS)和壬基酚聚氧乙烯醚(OP-10)作为乳化剂,并加入适量的淀粉,合成了苯乙烯丙烯酸丁酯(SAE)聚合乳液。利用正交实验的方法,比较了乳化剂用量、淀粉用量、SDS占乳化剂的比例及预乳化转速等因素对苯乙烯丙烯酸酯(SAE)表面施胶剂合成效果的影响,并且探讨了采用不同的表胶添加量对纸张性能的影响。结果表明,对表面施胶剂性能影响最大的因素是乳化剂用量;最佳工艺方案为乳化剂总用量为单体量的2%、预乳化转速为600 r/min、淀粉用量为单体量的20%、SDS占乳化剂用量的1%;以最佳方案合成的表面施胶剂对纸张进行表面施胶,Cobb值可达到39.2 g/m2;表胶添加量为淀粉绝干量的5%时,相对于未添加时的纸张,Cobb值下降了58.4%,表面强度上升了57.7%。     

STUDY ON FACTORS INFLUENCING INK ABSORPTION OF COATED PAPER

1.PREFACECoated paper, which is made up of fiber network andcoating pores, is porous printed material. The ink wastransferred to the sheet during printing. Inkabsorption, which determined the permeability of inkonto the sheet, is an important factor to coated paper.Many printing faults were caused by the unsuiTableof ink absorption of sheet and the printing conditionsused. The more ink absorption could lead to mattedprint, even soaking print or pulverization. While theless ink absorption c…     

INK-JET PRINT QUALITY IMPROVEMENT THROUGH THE USE OF CATIONIC SMA RESIN ADDITIVE IN PAPER COATING

Ink-jet printing technology is a prominent feature of any home office as it is more economical when compared with other printing technologies. The base paper for this study was a commercial fine paper, coated on one side with a typical formula of 100 pph pigment: 30 pph binder: ≤ 1 pph additive at 25% solids content. The focus of this paper was to evaluate a cationic resin additive in the coating formulation and its effect on print image sharpness. The print image sharpness was assessed based on the measured parameters of mean grey scale, area and perimeter of the image. Compared with a typical coating additive (i.e. Poly-dadmac), the coatings with SMA resin additives showed good grey scale ink density on the sheet. Compared to uncoated samples, the ink deposited on the SMA containing coated sheets was not absorbed into the paper, allowing for better print areas to be produced. The results of this study demonstrated the potential of further developing this cationic resin as a paper coating additive.     

一种基于图像的套印参数测量方法

提出了一种新的基于图像套印参数的检测方法.该方法在应用蜂窝分裂法实现图像量化的基础上,确定色标分割的颜色中心和阈值距离.经过计算色标质心间横向和纵向距离得到印刷套印偏差参数.经过计算色标与标准图像颜色的色差,建立色度与密度的转换关系,将色度值转换为对应的密度值,由网点参数与供墨系统的数学模型,计算出被检测处的实际墨量.理论分析与实验结果均表明:套印偏差检测精度高,有利于提高套印的准确性,油墨的质量和供墨量的实时检测,有利于实现墨量的自动控制,保证印刷图像整个画面阶调和色调的正确复制.     

导电油墨印刷转移率及其影响因素研究进展

 伴随印刷电子产业化技术发展,导电油墨及其应用技术获得了长足进步。为了获得高导电性高精度印刷线路,必须保证导电油墨在印刷过程的高转移率;导电油墨的印刷适性、承印物表面性能和印刷工艺技术,都会影响油墨转移率及印品性能。针对常用接触式印刷方式,例如凹版印刷、柔版印刷、丝网印刷和胶版印刷,分析了影响导电油墨印刷转移率的一系列因素,探讨了提高导电油墨印刷转移率的方法。研究表明,导电油墨印刷转移过程受油墨材料、印刷工艺和印刷装备影响,影响导电油墨转移率的关键因素在于油墨流变性和承印物表面与油墨相容性的改进及印刷工艺技术调整。     

THE EFFECTS OF BINDER ON COATING RHEOLOGICAL PROPERTIES *

胶粘剂是影响涂料流变特性的主要因素．本文对常用的氧化淀粉、羧基丁苯胶乳和聚乙烯醇在不同的添加量情况下配成的涂料进行了系统的研究．研究结果表明,涂料都呈剪切稀化特性,认为可用修改的幂律方程表达,其中幂指数为剪切速率的函数,该方程体现了流体流动类型对剪切速率的依赖性;当胶粘剂为聚乙烯醇时稠度系数Ｋ最大,为氧化淀粉时次之,为羧基丁苯胶乳时最小．同时也对氧化淀粉、羧基丁苯胶乳、ＣＭＣ和ＰＶＡ混合配制的涂料进行了研究,在剪切速率为１０３／ｓ以下时,体系都呈剪切稀化特性,表观粘度与剪切速率呈幂指数函数关系,且幂指数为剪切速率的函数．在相同条件下,涂料表观粘度在含有ＣＭＣ时最大,含有ＰＶＡ时次之,含有羧基丁苯胶乳时最小．     

2021年结构色打印研究热点回眸

结构色是一种环保且稳定的呈色方式,在新型显示、信息加密、色度传感、防伪标签等领域具有广泛的应用前景.打印技术是实现结构色快速图案化、发挥结构色功能的重要途径.2021年,结构色打印在原理突破、技术发展及功能拓展等方面均取得了重要进展.回顾了2021年结构色打印领域的研究热点和代表性成果,包括透明墨水的全彩结构色打印、胶...     

AN AUTOMATIC MEASURING SYSTEM FOR PRINT QUALITY OF COATED INK-JET PAPER

An automatic visual measuring system designed for evaluating the print quality of coated ink-jet paper is presented. Based on the degree of wicking,feathering, strike-through and color-to-color bleeding, Ink-jet Print Quality Index (IPQI), which was calculated with Area Spread Ratio (ASR), Edge Raggedness (ER), and Roundness Deviation (RD) of the printed dots, was used to evaluate the print quality. An iterative repetition interpolation threshold segmentation algorithm was performed with the aid of magnifying glass, charge coupled device (CCD)camera, frame grabber, image software and computer. Seven kinds of coated glossy photo papers were tested with a constant ink and ink-jet printer,the optical print resolution of each kind was obtained and their performance was ranked. It was shown that the system can meet the requirements ofpapermakers and can provide an objective and quantitative method both for evaluating the print quality, determining the optical print resolution and optimizing the coating process for coated ink-jet paper.     

油墨配色的理论与实验研究

根据混色系统理论、色度学及样条插值方法,提出了一种计算专色油墨配方的方法。在二维空间中用样条插值对专色油墨配色问题进行了研究,探索了“相同主波长具有相同色相”原则在专色油墨配色中的应用问题。实验结果表明,该算法具有一定的精确性,基本实现了胶印油墨配色,能满足一般胶印对印品颜色的要求。     

印刷油墨配色实验系统的设计与实现

为满足高校印刷工程类本科生实验教学需要,开发了印刷油墨配色实验系统。该系统在确保配色精度的基础上依据实验教学的需要,采用模块化设计方案,并同时进行配色算法和软件的研究和设计。利用该系统能进行印刷油墨的配色实验教学,有效模拟实际配色实验流程,通过修改其中的模块可以进行油墨和色彩相关实验的设计和验证,有助于提高学生的创新实践能力。     

胶印机匀墨胶配方改进的研究

以环保无毒物质柠檬酸三丁酯（TBC）为增塑剂，聚氨酯为胶液，研制了一种无毒环保的胶印机匀墨胶的新配方．分别在匀墨棒上用新配方和原配方进行上胶，比较匀墨棒上胶后的性能及固化时间．结果表明，采用新配方所做的匀墨胶层制件拉伸粘合强度优于原配方且手感光滑，经厂家试用，效果良好．