高锰钢形变过程中加工硬化机理的研究

采用Gleeble-3500试验机对ZGMn13Cr2高锰钢进行0.1s-1应变速率下的室温压缩实验,应变量分别为5%,30%和50%.利用金相显微镜、维氏显微硬度机、XRD和TEM等方法,研究了压缩变形量对ZGMn13Cr2显微组织衍变及加工硬化机制的影响.结果表明:高锰钢压缩变形后晶粒内出现大量变形带,变形带相互交叉、缠结、割截.压缩变形量为5%时,高密度位错相互缠结呈位错胞或者位错墙,压缩变形量为30%时,基体内出现形变孪晶,随着变形量的进一步增大,孪晶的密度和体积分数增大,水韧态高锰钢在压缩变形量为50%的条件下,其显微硬度与初始态相比提高了125%,达到HV560.8.XRD结果显示,压缩变形后基体组织为奥氏体和少量的碳化物,未发现相变诱发马氏体组织.随着变形量的增大,高锰钢加工硬化机理由位错强化机制向形变孪晶强化为主、位错+少量层错强化机制为辅的机制转变.     

温度对3%Cr管线钢CO_2腐蚀产物膜的影响

经济型低Cr合金钢具有较好的抗CO2腐蚀性能,利用高温高压反应釜研究了3%Cr管线钢的CO2腐蚀行为,采用X射线衍射(XRD)、扫描电镜(SEM)和能谱仪(EDS)等对腐蚀产物膜的微观形貌、化学成分以及结构进行分析,探讨了温度对3%Cr管线钢腐蚀产物膜的影响.结果表明,CO2分压0.8 MPa、液体流速1.0 m.s-1时,在40～140℃范围内,3%Cr管线钢均未发生局部腐蚀,其平均腐蚀速率呈先升高后降低的趋势,峰值温度在100℃左右.3%Cr管线钢的腐蚀产物膜具有两层结构:内层膜为致密的富Cr层(Cr富集程度可高达Cr/Fe=8/5),主要由含Cr化合物和非晶态FeCO3构成,并随着温度的升高,Cr富集程度增加,内层膜厚度降低;外层膜则由晶态FeCO3堆积而成.     

燃煤锅炉水冷壁硫化物高温腐蚀试验

为了选择合适的燃煤锅炉水冷壁管材以减少高温腐蚀,模拟了燃煤锅炉的条件,对管材20G和45CT涂层进行了腐蚀试验研究.通过腐蚀增重量得出腐蚀动力学曲线,利用X射线衍射仪和能谱分析仪的扫描电镜,对试样腐蚀后的形貌结构、元素含量以及腐蚀产物的组成进行分析.试验结果表明,500℃以下45CT涂层的抗腐蚀性能明显优于20G.     

碳钢高温高压CO2腐蚀产物膜的形成机制

利用高温高压反应釜模拟了N80钢在CO2分压1MPa、温度90℃、流速1ms-1条件下地层水中不同时间的腐蚀行为,并应用SEM、EDS和XRD等微观分析手段研究了腐蚀产物膜的微观形貌、成分和结构特征,探讨了腐蚀产物膜的形成机制. 结果表明:在腐蚀开始阶段(8h),腐蚀产物主要为Fe3C,并有少量的FeCO3形成. 随着腐蚀的进行(72h后),腐蚀产物膜基本上为FeCO3. 腐蚀产物膜由内外两层构成:内层膜是溶液中HCO-3不断透过膜进入膜/基界面与基体反应形成,并使膜/基界面不断向内推进;外层膜是由于溶液中Fe2 和CO2-3的浓度超过FeCO3的容度积,FeCO3晶体在内层膜表面形核并长大而形成. 外层膜的晶粒比较细小、致密. 内层膜与外层膜的界面结合比较弱,而内层膜与基体的结合比较强.     

固溶处理对AP65镁合金阳极放电活性的影响

采用熔炼铸造法制备AP65镁合金阳极材料,采用扫描电镜(SEM)结合能谱分析(ESA)研究不同状态下试样的显微组织和腐蚀形貌,采用X线衍射仪(XRD)分析不同状态下试样的相结构,采用动电位极化扫描法、恒电流氧化法和交流阻抗法研究不同状态下试样在3.5%NaCl溶液中的电化学行为。研究结果表明:铸态试样在晶界处存在不连续分布的第二相Mg17Al12,该第二相能增强试样的耐蚀性,但导致试样局部腐蚀严重且放电活性较弱;经400℃固溶24 h后第二相溶解,试样的耐蚀性减小,腐蚀相对铸态试样均匀且放电活性增强。     

快速凝固工艺对AZ91HP镁合金腐蚀性能的影响

通过铜模铸造制备快速凝固的AZ91HP镁合金.利用失重法及动电位极化曲线研究了常规铸造AZ91HP和快速凝固AZ91HP镁合金样品在NaCl腐蚀介质中的耐腐蚀性能;通过金相显微镜（OM）、扫描电镜（SEM）及X射线衍射（XRD）分析了腐蚀后合金微观组织及相结构.结果表明,快速凝固的AZ91HP镁合金具有更好的耐腐蚀性能.其主要原因是经快速凝固工艺后：①β-Mg17Al12相近似连续地分布于细小的α-Mg晶界上;②合金的元素分布更加均匀;③合金显微缩松减少.     

铝合金表面电镀镍的耐腐蚀性能

在铝合金表面电镀镍,考察镀液温度、电流密度和镀液pH值等因素对镀层耐蚀性能的影响,获得最佳电镀条件下的镍镀层.选择3.50%NaCl溶液作为腐蚀介质,采用稳态阳极极化曲线法研究镀层的耐蚀性能.用SEM和XRD研究镍镀层在腐蚀前后的微观结构和表观形貌的变化.结果表明镀镍的最佳工艺条件为温度50℃、电流密度30mA/cm2、镀液pH值3.82.XRD测试表明镍镀层的结构为立方晶系,晶面择优取向为(111),腐蚀前后晶面择优取向不变,但(111)晶面的织构系数由35.35%增至61.73%,说明低指数晶面(111)具有较好的耐蚀性能.SEM测试表明最佳条件下制备的半光亮镍镀层均匀致密,具有较好的耐腐蚀性能.     

Mg-Zn-Ca合金的性能及降解速率控制

以经过铸造和热挤压的Mg-Zn-Ca合金为研究对象，利用光学显微镜、万能试验机对合金的微观组织以及机械性能进行了分析测试.采用仿生法在该合金表面形成了羟基磷灰石(HA)涂层.利用X射线衍射仪和扫描电子显微镜对涂层结构和形貌进行分析与观察，并对有、无涂层试样进行腐蚀实验研究.结果表明:采用铸造和热挤压技术制备的Mg-Zn-Ca合金抗拉强度和抗压强度与人骨接近，分别为365MPa和338MPa；屈服强度为360MPa，延伸率为1025%，弹性模量为4169GPa.HA涂层能一定程度上降低合金试样的降解速率.     

双辊铸轧奥氏体不锈薄带显微组织分析

对在异径双辊铸轧机上进行铸轧实验所得不锈钢薄带进行了显微组织分析·结果表明,铸轧不锈钢薄带的组织与常规铸造相比有很大不同,晶粒组织得到显著细化,组织形态和分布均有异于常规铸造组织·但是从其组织分布特征及奥氏体和铁素体的质量分数来看,铸轧薄带的组织与焊缝中的铸态组织相比有极大的相似性,这是由于其熔池的热力学特点的相似性决定的,因而可以用分析焊缝中组织特征的一些方法来分析铸轧薄带的组织特征     

高温浓硫酸泵用新型不锈钢的研究

设计了用于高温浓硫酸泵用新型不锈钢的化学成分，采用金相显微镜、Ｘ射线衍射仪，扫描电镜和多种腐蚀试验方法新型铸造不锈钢的组织、腐蚀形貌和耐蚀性能，试验了钢的机械性能，冶炼工艺，铸造性能与焊接性能，研究结果表明，新型铸造不锈钢具有优良的耐蚀性，较高的强度与良好的塑韧性，具有较好的工艺性能。     

喷射沉积H13钢的组织和硬度

用传统铸造和喷射成形工艺制备了H13钢,然后再进行锻造加工,利用光学金相显微镜(OM)、扫描电子显微镜(SEM)、X射线衍射分析(XRD)等分析方法及硬度测试对不同工艺制备的H13钢的显微组织和硬度进行分析.研究结果表明,喷射成形及其锻造加工的H13钢的组织及硬度明显的优于传统工艺制备的H13钢.     

铸造方法制备铸钢/碳纳米管复合材料

使用铸造技术制备了碳纳米管铸钢复合材料.将碳纳米管与铝粉球磨混合,冷压成饼状预制块.将钢水浇注在粉碎成颗粒度为2mm的预制块粉末上,制得样品.拉伸试验结果表明碳纳米管添加量为0.1％的复合材料样品拉伸强度较未添加碳管的铸钢试样提高11％.复合材料使用扫描电镜观察样品断口,发现碳纳米管存在,显示碳纳米管被成功加入到钢基体中.     

连铸结晶器铜板电沉积Ni-Co-Mo技术的研究

结晶器是钢材连铸技术过程中非常重要的组成部件.结晶器铜板长时间经受钢水冲刷,必须具有很高的耐摩擦磨损、耐腐蚀性能.现研究了钼酸钠含量、电流密度对结晶器铜板电沉积Ni-Co-Mo合金的影响,并对镀层的成分、硬度、耐腐蚀性能进行了测试.在确定镀液成分后通过极化曲线和循环伏安法测试研究了电沉积Ni-Co-Mo合金的机理.用SEM、EDX方法研究了镀层形貌、成分.利用磨损试验机研究了镀层的耐磨损性能.     

加热温度对TRIP钢连续冷却转变曲线及室温组织的影响

采用膨胀法在DIL805热膨胀仪上测定了不同加热温度下实验钢的连续冷却转变(CCT)曲线,通过光学显微镜和扫描电镜分析不同加热温度对CCT曲线和冷却试样显微组织的影响.结果表明:当加热温度由完全奥氏体化温度降低到两相区内较高温度时,CCT曲线中铁素体转变区左移;当加热温度处在两相区范围内时,随着加热温度的降低,铁素体转变被推迟,使得CCT曲线右移;新生铁素体外延生长方式和奥氏体中碳富集程度的差异是导致上述变迁的主要因素.     

Intergranular precipitation of copper-nickel alloys induced by seawater corrosion

This paper presents the observed grain boundary structure of Cu：Ni 70：30 alloy tubes before and after exposure to seawater. The results show that the thin platelet precipitates along grain boundaries of the alloys nucleated in the process of heat treatment and coarsened when they were exposed to seawater, indicating that the coarsening was induced by seawater corrosion. The diffraction image of the precipitate is fringe structure and possessed its own wave lengths. The fine scale structure is susceptible to intergranular corrosion, which could be confirmed by corrosion morphology observation of specimens after a long-time seawater exposure. The experiments were carried out by means of scanning electron microscopy （SEM）, transmission electron microscopy （TEM）, optical metallography （OM） and tensile testing etc., detecting corrosion morphology, microstructure and the mechanical property change due to the precipitation coarsening induced at grain boundaries of the specimens during exposure in seawater.     

复配缓蚀剂在油水混合液中的缓蚀性能

以2-巯基苯并咪唑（MBI）为缓蚀剂,MBI与十六烷基三甲基溴化铵(CTAB)为复配缓蚀剂,考察其在模拟油田情况下对20#钢的缓蚀性能的影响。采用SEM和AES考察缓蚀剂使用前后碳钢的表面形貌和各元素含量,利用腐蚀速率快速评定仪对20#钢材料的腐蚀速率进行测定,由电化学工作站测试20#钢的极化曲线和交流阻抗曲线。实验结果表明,当测试温度为30℃时,单独使用MBI对20#钢有一定缓蚀效果, MBI质量浓度为1.98g/L时缓蚀效率最高,为86.04%;当采用MBI+CTAB复配缓蚀剂时,缓蚀效果优于单独使用MBI时的缓蚀效果, CTAB质量浓度为0.3g/L时缓蚀效率达到95.87%。     

镍-磷-纳米SiO2化学复合镀层耐腐蚀特性研究

研究了镍-磷-纳米SiO2化学复合镀层的机理，用SEM和XRD等技术分析了，复合镀层的微观结构，比较了传统的化学镀镍-磷层和纳米复合镀层的沉积速度和耐蚀性，结果表明，纳米SiO2颗粒的引入加快了化学镀层的沉积速度，在同等条件下可降低化学镀的反应温度，镀层在酸、碱、盐水溶液中表现出了良好的耐蚀性能。     

AgCu28对Be/HR-1不锈钢热静压接头组织性能的影响

以AgCu28合金作为中间层材料,进行Be/HR—I不锈钢热静压扩散连接。利用光学金相、扫描电镜(SEM)、俄歇电子能谱(AES)和X射线衍射仪(XRD)及材料试验机分析了热静压扩散连接接头的显微组织、元素和物相分布以及力学性能,探讨了扩散区成分、组织结构与性能的关系,以及AgCu28合金作为中间层材料的作用。研究表明:采用AgCu28合金作为中间层材料,能够实现Be/HR—I不锈钢的扩散连接,能有效地减少铍、不锈钢间的元素互扩散,减少了Be与Fe和不锈钢中其他合金元素的脆性金属间化合物的大量生成,接头质量较好。     

Effect of welding process on the microstructure and properties of dissimilar weld joints between low alloy steel and duplex stainless steel

To obtain high-quality dissimilar weld joints, the processes of metal inert gas (MIG) welding and tungsten inert gas (TIG) welding for duplex stainless steel (DSS) and low alloy steel were compared in this paper. The microstructure and corrosion morphology of dissimilar weld joints were observed by scanning electron microscopy (SEM); the chemical compositions in different zones were detected by energy-dispersive spectroscopy (EDS); the mechanical properties were measured by microhardness test, tensile test, and impact test; the corrosion behavior was evaluated by polarization curves. Obvious concentration gradients of Ni and Cr exist between the fusion boundary and the type II boundary, where the hardness is much higher. The impact toughness of weld metal by MIG welding is higher than that by TIG welding. The corrosion current density of TIG weld metal is higher than that of MIG weld metal in a 3.5wt% NaCl solution. Galvanic corrosion happens between low alloy steel and weld metal, revealing the weakness of low alloy steel in industrial service. The quality of joints produced by MIG welding is better than that by TIG welding in mechanical performance and corrosion resistance. MIG welding with the filler metal ER2009 is the suitable welding process for dissimilar metals jointing between UNS S31803 duplex stainless steel and low alloy steel in practical application.     

含铌TRIP钢连续退火后的组织性能及强化机理

在实验室模拟了含铌与无铌TRIP钢的连续退火工艺过程,通过金相显微技术(OM)、扫描电镜(SEM)、透射电镜(TEM)、背散射电子衍射技术(EBSD)、X射线衍射(XRD)和拉伸实验等检测手段研究了TRIP钢的组织性能,分析了TRIP钢中残余奥氏体稳定性的影响因素及强化机理.结果表明:在连续退火工艺条件下,Nb的存在细化了TRIP钢的微观组织,与未添加Nb的钢相比,添加Nb可以提高TRIP钢中残余奥氏体含量和残余奥氏体碳含量.含铌TRIP钢中残余奥氏体主要以团块状或薄膜状分布于铁素体与贝氏体晶界,极少部分以细小球状分布于铁素体晶内.含铌TRIP钢热轧后的主要析出物为Fe3C和(Nb,Ti)(C,N),退火后的主要析出物为(Nb,Ti)(C,N).细小含铌析出物的析出强化导致了随着退火温度的升高,屈服强度和抗拉强度升高.