Photocatalytic Reduction of Carbon Dioxide with Modify Pd, Ru on TiO2 Surface

Photocatalytic reduction of CO2 to organic compounds was reduction in semiconductor suspension system under simulated solar in laboratory. TiO2 load catalysts were prepared in different ways, and they were used in photocatalytic reduction of CO2 . Experimental results show that the photocatalytic activity can be improve by dressing Pd, Ru on TiO2 Surface and is obvious different when catalysts were prepared in different ways. The photocatalytic mechanism of dressing Pd on TiO2 Surface; dressing Pd and Ru on TiO2 Surface were also discussed in this paper.     

高分散负载Pd催化剂上CO氧化性能

制备高分散的负载型催化剂是充分利用在自然界中储量极为有限的贵金属资源的重要手段.采用不同方法制备一系列负载Pd催化剂,考察了不同载体负载Pd催化剂的CO氧化性能.发现以乙酰丙酮钯为前驱体制得的Pd/TiO2催化剂活性远高于Pd/SiO2和Pd/Al2O3催化剂的活性,在室温下就表现出较好的CO氧化活性,且在无气相O2条件下CO可以与Pd/TiO2催化剂表面的氧物种(晶格氧)反应生成一定量的CO2.分散度测试、CO吸附的原位红外光谱和程序升温还原的结果表明Pd/TiO2催化剂上Pd物种以高分散Pd0形式存在,并与载体之间存在强相互作用,这可能是Pd/TiO2催化剂具有低温活性的主要原因.     

Atomic layer deposition on Pd nanocrystals for forming Pd-TiO2 interface toward enhanced CO oxidation

Pd typically exhibits relatively low catalytic activity in CO oxidation, as CO is apt to be adsorbed on Pd to poison the surface for O2 activation. In this Letter, we report that this limitation can be overcome by integrating Pd with TiO2. The TiO2 was coated on Pd nanocubes with a controllable thickness using atomic layer deposition (ALD) method. Given the different work functions of TiO2 and Pd, the electrons in TiO2 semiconductor will flow toward Pd. With the electron density increased on Pd, the adsorption of CO to Pd will be weakened while the oxygen activation can be facilitated. Meanwhile, the interface-confined sites at Pd-TiO2 may further enhance the oxygen activation. As the species adsorption and activation are strongly correlated with electron density, the performance of Pd-TiO2 in CO oxidation turns out to depend on the TiO2 thickness, which determines the number of transferred electrons, within a certain range (<1.8 nm). This work provides a new strategy for enhancing catalytic performance through tailoring charge densities in hybrid catalysts.     

Ag/TiO2,Pd/TiO2和TiO2对庚烷的光催化氧化活性

用光沉积法制备Ag/TiO2和Pd/TiO2催化剂样品,然后用表面光电压谱(SPS)和紫外可见吸收光谱(UV-Vis)对样品进行表征.以气态庚烷为反应体系,来比较上述两种催化剂的光催化活性.与纯TiO2比较,Ag和Pd的存在提高了TiO2的光催化活性;其原因可解释为金属Ag或Pd捕获电子,从而提高了电子-空穴对的分离效率;结果还表明与Pd/TiO2催化剂相比,Ag/TiO2表现出较高的光催化活性,这主要是Ag比Pd具有较强的捕获电子的能力.     

微波-二元醇技术制备Au/TiO2及其光催化消除臭氧

以TiO2为载体,利用微波加热HAuCl4的乙二醇溶液,制得了负载型的Au/TiO2催化剂,采用透射电子显微镜(TEM)、漫反射光谱(DRS)、X射线光电子能谱(XPS)等现代表征技术对Au/TiO2催化剂进行了表征,并考察了其光催化分解臭氧的性能.结果表明,微波辅助制备的Au/TiO2催化剂具有较高的光催化消除臭氧活性.     

多壳层TiO2/石墨烯复合纳米材料的制备及其在光催化还原CO2中的应用

使用碳球作为模板,利用水热-煅烧的方法制备了多壳层TiO_2。以多壳层TiO_2和氧化石墨烯为原料,利用水热法制备了多壳层TiO_2/还原氧化石墨烯(r-GO)光催化剂。运用XRD,TEM,FT-IR,DRS等测试手段对制备的样品进行表征;并探究其在可见光下对光催化还原CO_2的活性。表征结果表明粒径均匀的多壳层TiO_2纳米球均匀地分布在r-GO表面,r-GO的引入拓宽了光响应的范围。光催化结果表明,复合r-GO后TiO_2的光催化性能显著地提升。     

微波辅助水相合成二氧化钛及其催化活性研究

以四氯化钛为原料,采用微波辅助溶胶-凝胶法在水相中制备二氧化钛,用XRD、TEM对所制得的二氧化钛的性质进行表征。用15W紫外灯作为光源,以甲基橙为模拟污染物进行光催化降解实验,探讨不同反应温度和反应时间得到的二氧化钛光催化效果。实验结果表明在120℃、30min的条件下制备的二氧化钛光催化活性最高。并利用液质联用技术对降解反应机理进行了研究。     

海藻酸钠负载Ru掺杂TiO2太阳光催化降解染料废水

采用溶胶-凝胶法制备钌掺杂型二氧化钛,并用海藻酸钠固定化制成凝胶微球.以甲基橙为模拟染料废水,太阳光作为能源,研究钌离子的掺杂量、催化剂用量、甲基橙初始浓度和光照时间对掺杂二氧化钛的光催化性能的影响.结果表明,掺杂钌能明显改善二氧化钛的可见光催化性质.钌掺杂质量分数为1.5%,催化剂用量为3.0 g/L,甲基橙初始浓度20.0 mg/L条件下,染料溶液的降解率达90%.     

担载型钅了催化剂对二氧化碳甲烷化的催化性能

采用水溶液浸渍法制备了多种无机氧化物担载的钅了催化剂，并对其在二氧化碳甲烷化反应中的催化性能作了研究。结果表明，无机氧化物担载的钅了催化剂具有高活性；不同载体担载的体系有如下的活性次序：ＴｉＯ２＞ＺｒＯ２＞海泡石＞Ａｌ２Ｏ３＞ＳｉＯ２；反应条件及第二组份的添加对催化性能均有影响；催化剂作用下的反应活化能大小顺序与活性变化规律相符     

Pd/TiO_2等负载型钯催化剂中载体和金属间的相互作用研究

用热分析实验证实了TiO_2在温和的条件下就存在部分还原现象;结合TiO_2上负载了Pd后对CO_2吸附能力显著减弱之结果,支持了Pd/TiO_2中存在着载体和金属间强相互作用的观点;借助热分析结果,认为催化剂中各组分间存在着相互作用是一个普遍现象。     

固体超强酸SO2— 4／TiO2制备及其光催化氧化性能

采用沉淀－浸渍法制备固体超强酸催化剂SO2－ 4／TiO2纳米粒子,并用XRD,BET,XPS,UV－Uis漫反射光谱等对其特性进行表征,NO-2以为降解目标物,考察了SO2－ 4／TiO2光催化氧化性能,结果表明,SO2－ 4／TiO2在高温下相结构稳定,TiO2的超强酸化可增大表面,有利于反应物吸附,同时产生吸附带边蓝移及禁带宽度增加,从而,产生较大的氧化还原势,与TiO2相比,光催化氧化活性显著提高,焙烧温度600度时催化剂活性最好。     

程序升温还原和定温吸附法研究负载钯催化剂中的金属—载体强相互作用

以不同载体的钯催化剂来研究金属——载体之间的强相互作用(SMSI)。利用程序升温还原法(TPR)和定温吸附(TRS)相结合的技术来研究这些催化剂的还原情况和对氢的吸附情况。发现钯在低于200℃时就被还原。在较高温度下氢从Pd到载体有溢流,高温氢处理也会导致SMSI和熔结现象。这些溢流、熔结和SMSI的程度决定于载体。而SMSI也抑制着Pd对氢的大量吸附。在相同还原条件下,负载Pd催化剂有下列熔结趋势:Pd/C>Pd>TiO_2>Pd/Al_2O_3>Pd/SiO_2。     

Photocatalytic oxidation of gaseous benzene over nanosized TiO2 prepared by solvothermal method

Nanosized TiO2 particles were prepared by solvothermal method using tetrabutyl titanate as precursor,ethanol and water as solvents,and a facile immobilization method of nanosized TiO2 particles on woven glass fabric was developed. The samples obtained under various preparation conditions were charac-terized by means of thermo gravimetric analysis(TG) and differential scanning calorimetry(DSC) ,X-ray diffraction(XRD) ,transmission electron microscopy(TEM) ,high resolution-transmission electron mi-croscopy(HR-TEM) ,and Brunauer-Emmett-Teller(BET) . The results show that the cube-shape of TiO2 prepared by solvothermal method has good crystallinity of(101) surface,higher thermal stability and large specific surface area. Scanning electron microscopy(SEM) images confirmed that the immobi-lized TiO2 film was uniformly distributed and clung to the substrate firmly. The photocatalytic activity of the catalysts was tested using photocatalytic oxidation of gaseous benzene. The results show that the TiO2 calcined after solvothermal treatment suffers from lower specific surface area,and hence de-creases its photocatalytic activity. The photocatalytic activities of the TiO2 by solvothermal treatment with or without calcination in degradation 400 mg/m3 benzene are 3.7 and 4.1 times as high as catalyst without solvothermal treatment,respectively.     

不同方式合成纳米TiO2载体在SCR脱硝催化剂制备中的应用

通过不同方式合成纳米TiO2,并以此为载体负载活性物质制得1%V2O5-10%WO3/TiO2的SCR脱硝催化剂.纳米TiO2制备方式包括溶胶凝胶法、TiCl4水解法、直接沉淀及均相沉淀法.试验结果表明,用这4种方法制备得到的TiO2均为锐钛型,以均相沉淀法合成的纳米TiO2为载体制得的催化剂具有较高的比表面积及脱硝性能,并表现出明显的活性温度窗口.进一步引入超声作用优化均相沉淀反应条件,结果表明,相比同类型传统方法,超声均相沉淀工艺能够明显提高纳米TiO2产品的比表面积与分散度,缩小二次颗粒尺寸,并使得所制备催化剂脱硝性能得到显著提高,且具有较好的抗水、抗硫特性.     

不同络合剂对Pd/MWCNTs催化剂的甲酸电催化氧化性能影响

以添加Na2CO3和NH3.H2O为络合剂的微波多元醇法制备碳纳米管载Pd催化剂(Pd/MWCNTs),并考察了络合剂对催化剂甲酸电催化氧化性能的影响。结果表明,NH3.H2O络合剂制备的Pd/MWCNTs催化剂,其Pd晶粒平均粒径最小(5.2 nm),对甲酸氧化的催化活性和稳定性最好。NH3.H2O与PdCl2能形成络合物,可能会促进微波合成中碳纳米管上形成均匀分散且较小粒径的Pd粒子,因此提高了催化剂的甲酸氧化催化性能。     

MgFe_2O_4/TiO_2催化剂光催化还原CO_2的实验研究

CO2的化工利用是节能减排的方法之一。光催化还原CO2合成有用的化工产品,具有绿色化工的特点。采用溶胶-凝胶法制备MgFe2O4/TiO2催化剂,通过XRD、IR、UV-Vis、SPS、SEM、NH3-TPD和BET等表征手段,对催化剂的结构和光化学性质进行分析,对所制备的MgFe2O4/TiO2光电性质、微观结构以及光催化CO2合成甲酸的性能进行研究。结果表明:复合后的MgFe2O4晶型未发生改变,复合的光敏化作用使MgFe2O4吸收边蓝移,提高光生载流子分离效率,增大脱附峰面积和比表面积。在模拟日光灯照射下,MgFe2O4/TiO2光催化还原CO2的性能高于未复合的MgFe2O4催化剂。     

锐钛矿相纳米TiO_2的拉曼光谱表征及光催化活性的研究

为了研究锐钛矿型纳米TiO2光催化活性,本文以钛酸四丁酯为原料,利用溶胶—凝胶法制备了纯锐钛矿型TiO2纳米粉体及不同金属离子掺杂的锐钛矿型TiO2纳米粉体,采用XRD、Raman光谱对纳米TiO2进行了表征,考察了不同金属离子掺杂对TiO2光催化降解甲基橙活性的影响。结果表明:不同离子掺杂后的TiO2与纯TiO2相比,拉曼谱峰强度降低,平均粒径变小,光催化活性提高。     

掺银TiO2薄膜的制备及其光催化性能

采用Ｓｏｌ－ｇｅｌ法在玻璃板表面制得均匀的ＴｉＯ２薄膜,并利用光催化还原法镀银得到掺银ＴｉＯ２薄膜。用掺银的ＴｉＯ２薄膜和未掺银的ＴｉＯ２薄膜在高压汞灯和太阳光的照射下,对有机物苯酚水溶液进行催化光解研究。结果表明掺银ＴｉＯ２薄膜的光催化活性明显大于未掺银ＴｉＯ２薄膜,这是提高ＴｉＯ２光催化效率的可行方法。     

熔融-分相法制备纳米TiO2的光催化性能

利用熔融-分相法制备了以多孔玻璃为载体的纳米TiO2光催化材料,以甲基橙为被降解物,研究了不同条件下的光催化活性,并与用溶胶一凝胶法制备的纳米TiO2的光催化活性进行了对比.实验结果表明：不同的光源、光照时间和催化剂颗粒粒度对光催化活性都有较大的影响;与用溶胶一凝胶法制备的纳米TiO2有类似的光催化活性.     

退火温度对磁控溅射Ti02薄膜结构及性能的影响

采用对向靶磁控溅射法在FTO导电玻璃基底上制备了Ti02薄膜,分别在450℃、500℃和550℃条件下对Ti02薄膜进行退火处理;利用X射线衍射（XRD）和扫描电镜（SEM）测试手段分析了不同退火温度对TiO,薄膜晶体结构与表面形貌的影响以异丙醇（iso—propanol,IPA）为目标物,研究了所制备Ti02薄膜的光催化性能,并分析了该气相光催化反应机理．同时在氙灯照射下,测试了Ti02薄膜的光电流以分析其光电性能．结果表明：当退火温度由450℃升至550℃时,Ti02薄膜由纯锐钛矿结构转变为金红石与锐钛矿型混晶结构,其表面形貌则变化不大;Ti02薄膜光催化性能与光电性能均随退火温度的升高而提高,经550℃退火的Ti02薄膜可将IPA高效降解为丙酮和C02,其光电流可达0．7mA并保持稳定．