g-C_3N_4负载磷钨酸的表征及光催化性能

采用超声——浸渍法制备了磷钨酸/g-C_3N_4(PWCN)复合光催化剂,并利用XRD,IR及UV-Vis吸收光谱对其进行了表征.考察了其在紫外光和太阳光照射下催化降解甲基橙的性能,并对其重复使用性、降解动力学及光催化机理进行研究.结果表明:复合材料的光响应与PW相比发生红移,且吸光值增大.在接受紫外光和可见光照射2h条件下,该复合物光催化剂对甲基橙的光降解率分别达到96.81%和80.24%,同时具有良好的循环稳定性.PW对g-C_3N_4光生电子的捕获是提高复合物催化活性的主要原因.     

Binder-free heterostructure(g-C_3N_4/PPy) based thin film on semi-flexible nickel foam via hybrid spray technique for energy storage application

A semi-flexible binder-free graphitic carbon nitride(g-C_3N_4) intercalated polypyrrole(PPy) nanocomposite thin film was prepared via hybrid electrospray technique. A homogeneous thin film was achieved by the controlled spray process. A deposited thin film illustrated the amorphous nature of composite with high surface purity and good chemical composition. The surface analysis confirmed the smoother surface with well-defined distinct phases of g-C_3N_4 and PPy matrix in the composite thin film. The electrochemical studies exhibited that a maximum areal capacity of the thin film was achieved to be 289.6 mF/cm~2 at a current density of 0.4 mA/cm~2,which is higher than that of pristine PPy(194.8 mF/cm~2). The heterostructure electrode illustrated that the life cycles of 99% could be up to 10,000 cycles with low resistance due to the synergetic effect of g-C_3N_4 and PPy matrix with strong material adhesion(hybrid spray process) on the surface. A binder-free heterostructure thin film will play a significant role in the energy storage application.     

CdS / TiO2复合半导体的表面态及光催化性能

采用浸渍法制备了CdS／TiO2复合半导体光催化剂．使用XPS和UV-Vis扩散—反射谱对样品的表面组成及光吸收特性进行了分析．结果表明,样品中的硫主要以CdS形式存在,其外层包裹了一层CdSO4;由于在TiO4表面修饰了CdS,使样品的吸收带边由400nm(3．1eV)红移至530nm(2．3eV)．采用粉末电导装置对CdS／TiO2薄膜的表面态能级进行了测试,并以活性艳红X-3B水溶液的光催化脱色为指标反应,对CdS／TiO2的活性进行了评价．与单一TiO2相比,CdS／TiO2的表面态更靠近TiO2的导带,有利于电子在表面的捕获,从而提高了样品中自由电荷的浓度,加速了活性艳红X-3B水溶液的光催化脱色反应。     

纳米TiO2光诱导产生羟基自由基的ESR研究

在纳米TiO2光催化氧化体系中，添加无机氧化物，能有效地捕获电子，增加溶液中羟基自由基浓度，提高纳米TiO2的光催化氧化能力.该文以DMPO为羟基自由基捕获剂，利用自旋捕捉－电子自旋共振（ESR）方法研究无机氧化物K2S2O8对纳米TiO2光催化氧化体系中产生羟基自由基的关系，在此基础上探讨了甘氨酸光催化氧化反应的机理.     

阴离子掺杂TiO2气相光催化降解正己烷的研究

利用钛酸丁酯水解浸渍方法制备了多种阴离子掺杂改性TiO2纳米催化剂并作了XRD,BET等表征,研究了它们对气相光催化降解正己烷反应的活性,并和阳离子K 掺杂TiO2、未掺杂TiO2及市售TiO2DegussaP 25作了比较.结果表明,在适当的掺杂浓度下,多数阴离子的掺杂对TiO2的光催化活性略有降低,但仍优于P 25,活性最差的是钾离子掺杂TiO2,H3PO4和NH4H2PO4的掺杂则对TiO2的光催化活性有明显的促进作用.     

石墨烯纳米复合物的制备及其可见光催化性能

采用水热法制备出TiO_2及其TiO_2/石墨烯纳米复合物,通过XRD、SEM、TEM等对材料晶型、TiO_2纳米颗粒在体系中的微观结构及分散状态进行了表征,利用紫外-可见漫反射谱对材料在可见光区的响应进行了研究,并通过在可见光照射下降解甲基橙溶液评价了TiO_2/石墨烯纳米复合物具有比纯TiO_2更高的光催化活性.结果表明,水热反应温度为200℃,反应时间为24h制备出的TiO_2/石墨烯纳米复合物具有最高的可见光催化活性,当TiO_2/石墨烯纳米复合物在12mg/L甲基橙溶液中的投入量为1g/L时,在3min内的降解率达99.9%.     

铝片TiO2薄膜在降解4BS染料中的应用

采用溶胶-凝胶(sol-gel)工艺在铝片表面制得了均匀透明的TiO2薄膜,考查了其光催化降解4BS染料的活性,研究了热处理温度、涂覆层数、以及溶液改性等因素对TiO2薄膜的光催化性能的影响.结果表明:该薄膜能有效降解4BS染料,热处理温度、涂覆层数影响薄膜的性能,层数为5,热处理温度为600 ℃的薄膜具有较高的光催化活性.TiO2薄膜对加入Fe3+的4BS溶液的降解率明显提高.     

双元素掺杂纳米TiO2光催化降解亚甲基蓝的研究

以浸渍法、共沉淀法和溶胶-凝胶法制备得到了双元素钕和铁掺杂的纳米TiO2光催化剂,考察了它们对光降解亚甲基蓝的催化活性.结果表明,亚甲基蓝的光催化降解可用假一级动力学方程表示.以一定比例掺杂钕、铁离子可提高TiO2的光催化活性,尤其是在自然光下TiO2的光催化活性.在一定比例钕、铁掺杂后,共沉淀法制备的掺杂型TiO2的光催化活性接近于用溶胶-凝胶法制备的掺杂型TiO2.     

纳米二氧化钛粉末离子掺杂研究

采用溶胶-凝胶法制备了13种离子掺杂的纳米TiO2光催化剂．系统的考察了它们光催化降解甲基橙的催化活性．并且对其可能的光催化活性的影响因素进行了全面的分析．发现其催化活性的变化与这些离子的掺杂浓度、离子半径、离子的电子亲和势、离子的电子构型、离子掺杂对TiO2造成的晶格畸变以及离子在TiO2晶体中的能级位置等因素有关．其中,掺杂V^5 、Ag^ 、Ni^2 、La^3 、Fe^3 及W^6 能够有效提高光催化降解甲基橙的脱色率;而对于Cr^3 以及闭壳型的Zn^2 、Al^3 等对TiO2光催化活性的影响较小．甚至有所降低．     

Co/TiO_2粒子的制备及其光催化降解罗丹明B的研究

通过溶胶—凝胶法制备掺杂Co2+的纳米TiO2,并用XRD和TEM进行了分析和表征.以汞灯为光源,通过对罗丹明B的降解反应,考察了Co2+/TiO2的光催化活性.结果表明,Co2+的掺杂减小了TiO2颗粒的粒径,提高了TiO2的光催化活性,Co2+惨杂量为1.0%时的光催化活性最高.另外,本文还研究了催化剂投加量对罗丹明B光催化降解效率的影响.     

Pt@g-C_3N_4/CeO_2 photocatalyst for the remediation of low concentration NO_x at room temperature

Pt@g-C_3N_4/CeO_2 photocatalyst was prepared by calcination of g-C_3N_4/CeO_2 mixture followed by impregnating Pt. Under the irradiation of visible light with the presence of water vapor at room temperature, Pt@g-C_3N_4/CeO_2 showed significant performance for remediation of NO_x. The deNO_x mechanism was studied by modified in-situ FTIR. The results proved that NO was prone to adsorb on the surface of Pt@CeO_2 and oxidized to nitrite for storage. Then, the photoinduced hydrogen on Pt@g-C_3N_4 component could diffuse into the vicinity of nitrite through the spillover effect of Pt and reacted with nitride to produce N_2 and H_2O.     

微波反应制备纳米TiO2-Fe2O3复合材料及其光催化性能

以TiCl4,FeCl3为原料,尿素为沉淀剂,采用微波加热,均相沉淀法合成了一系列纳米TiO2-Fe2O3复合材料.XRD分析证明反应前驱体为非晶态,500 ℃以上转变为锐钛矿结构.TEM形貌观察,粒子基本为球形,平均粒径为20 nm.EDS分析证明产品中Ti∶Fe的分析测定值与实际的投料值基本一致,并且掺杂均匀性好.光吸收及光催化实验发现Fe的摩尔分数为5%时,光催化效果最好,在日光照射180 min后,此TiO2-Fe2O3复合材料对藏蓝染料溶液降解率接近100%.     

稀土掺杂TiO2纳米微粒的合成、表征及光催化活性

采用溶胶-凝胶法制备纯的及掺杂不同量铈的TiO2纳米粒子,利用UV-Vis漫反射光谱及XRD等对所制备样品进行表征.以高压汞灯为光源、甲基橙水溶液的脱色为模型反应,研究了CeO2/TiO2的光催化降解反应活性.实验发现: 掺杂Ce的TiO2纳米粒子反射光谱特性向可见光方向红移到500.nm,比纯的TiO2纳米粒子对光的吸收率高、吸收能力强;掺杂的Ce4 仅有少量进入TiO2晶格中,大部分的Ce4 是以小团簇的CeO2形态均匀地分散在TiO2纳米粒子中或者是覆盖在其表面上.说明掺杂Ce能提高TiO2光催化反应活性,且掺杂Ce摩尔分数最佳值为2.0%.     

POMs/TiO2复合催化剂光催化降解染料废水的研究

采用溶胶-凝胶方法表面修饰TiO2制备了几种POMs/TiO2复合光催化剂,考察了催化剂在紫外光照射下对模拟染料废水(茜素红溶液)的光催化降解行为.结果表明:POMs/TiO2复合催化剂较纯TiO2光催化降解茜素红活性明显提高,其中复合催化剂Cr3OSiW12/TiO2光催化降解模拟染料废水(茜素红溶液)效果最佳.反应最佳条件:催化剂为Cr3OSiW12/TiO2,多酸质量分数为0.5%,催化剂用量为15 mg,茜素红溶液浓度为0.1mmol/L.茜素红降解质量分数可达74.6%.     

掺钇纳米TiO2的制备及其光催化降解性能

以价廉易得的TiCl4为原料,采用低温水解法制备出掺钇纳米TiO2光催化剂,进行了XRD分析,研究了掺钇纳米TiO2对甲基橙的光催化降解性能,结果显示:掺钇阻碍了晶粒生长,抑制了TiO2由锐钛矿向金红石晶型的转变,使粒径减小,光催化降解能力增强.实验条件下,掺钇纳米TiO2光催化剂降解甲基橙的最佳投加量为2.0g/L.     

TiO2/SiO2复合粉体的制备及催化性能的研究

文章采用XRD和FT-IR等方法对用Sol-Gel法制备的TiO2/SiO2复合粉体进行了表征,考察了原料组成和焙烧温度对复合物相变温度和晶型转变的影响,以及掺杂对甲基橙光催化降解的影响。研究表明,TiO2微粒以锐钛矿相高度分散在SiO2基质中,并与其形成了Ti-O-Si桥氧结构,提高了TiO2的表面积和表面缺陷,有利于有机物的吸附及半导体光生电子-空穴的分离,从而提高了半导体的光催化活性。     

纳米TiO2对有机污染物的光催化降解机理及发展趋势

光催化降解有机污染物消除其对环境的污染是目前环境领域中的新兴研究课题.通常情况下,纳米二氧化钛只能在紫外光范围内降解某些有机物.作者提出了通过施主半导化掺杂的方式使纳米二氧化钛在可见光范围具有光催化降解有机污染物的能力,并介绍了纳米二氧化钛光催化降解有机污染物的机理及把它应用于消除有机农药残余污染的研究进展和发展趋势.     

Fe3 掺杂对纳米TiO2薄膜光催化降解苯酚活性的影响

通过溶胶-凝胶法制备纳米TiO2薄膜,在制备过程中分别掺杂一定量的Fe3 .以高压汞灯做光源,用制得的纳米TiO2薄膜对苯酚作光催化降解实验,结果表明:掺杂Fe3 的纳米TiO2催化剂光催化性能明显提高.并探讨了Fe3 掺杂浓度和pH值对光催化的影响.     

Pt/TiO2催化剂上苯的光催化降解

以TiO2、Pt TiO2为光催化剂,光催化降解苯为模型反应,比较了两者的光催化活性,并利用在线气相色谱及原位红外考察了反应中间物及产物分布.结果表明铂的负载有利于反应中间产物的进一步降解,从而提高光催化降解效率.     

负载TiO2的碳纳米管光催化降解腈纶废水的研究

采用溶胶-凝胶法制备了负载二氧化钛的多壁碳纳米管,对其结构进行了X-射线粉末衍射(XRD)、透射电镜表征, 并且还探讨了负载二氧化钛的碳纳米管用于腈纶废水的处理.实验结果表明,该种催化剂具有很好的光催化活性.以300 W中压汞灯为光源,在250 mL的腈纶废水中加入100 mg负载有TiO2的碳管光催化处理1h,废水的CODcr去除率达22%;经Fenton试剂进行预处理后,加入150 mg载有TiO2 的碳纳米管进行光催化实验,经光催化氧化3 h后,CODcr去除率达到90%,处理效果非常明显.可见Fenton试剂预处理与TiO2光催化联合使用,对含腈废水中的难降解有机物去除效果好,具有一定的实用性.