Fe3O4磁性纳米颗粒的RAFT试剂化研究

通过反相微乳液法制备四氧化三铁纳米颗粒(Fe₃O₄ NPs),并用硅烷偶联剂KH570对其改性,以期在Fe₃O₄ NPs表面引入C==C双键,再利用引入的C==C双键与三硫代十二烷酸-2-氰基异丙酯(RAFT试剂)进行反应,得到RAFT试剂化的Fe₃O₄ NPs(Fe₃O₄-g-KH570-RAFT NPs),并对不同阶段的Fe₃O₄ NPs产物的结构与形貌等进行表征.研究中以RAFT试剂接枝率(Gr_RAFT)为指标,考察了反应时间等工艺条件对Gr_RAFT的影响.结果表明:制备的Fe₃O₄-g-KH570-RAFT NPs的平均粒径为10.4 nm,当反应时间为14 h,反应温度为65 ℃,n_KH570/n_RAFT为1/2时,接枝率Gr_RAFT最高达到79.34%.     

动态反应釜制备超顺磁性Fe3O4粒子及其DNA提取

使用动态反应釜制备得到磁性粒子,与静态反应釜相比单次制备量提高20倍;通过扫描电子显微镜（SEM）、傅立叶红外光谱（FT-IR）、X射线衍射（XRD）、振动样品磁强计（VSM）等手段对产物进行表征,证明获得了粒径200 nm左右的单分散Fe₃O₄粒子,并具有超顺磁性;对其表面进行SiO₂包覆,获得具有良好分散性的Fe₃O₄@SiO₂粒子。研究发现Fe₃O₄@SiO₂对DNA提取具有可重复利用性,并且质粒DNA吸附到Fe₃O₄@SiO₂上后可直接加入聚合酶链式反应（PCR）体系作为扩增模板。     

Fe3O4/Ag复合纳米颗粒的制备及其抑菌性能研究

首先用水热法制备了Fe₃O₄纳米球,然后以制备的磁性Fe₃O₄纳米粒子为磁核,在高温高压反应釜中与葡萄糖反应,使其表面包覆一层聚糖,利用聚糖的还原性,让包覆后的粒子与AgNO₃反应,制备出Fe₃O₄/Ag纳米复合粒子。用透射电镜（TEM）、X射线衍射仪（XRD）对所制备的材料的形貌和结构进行了表征。通过抑菌实验的测定,结果表明Fe₃O₄/Ag复合材料具有良好的抑菌活性。     

磁性煤矸石地质聚合物类芬顿降解苯酚

以煤矸石为原料，制备出磁性煤矸石地质聚合物(Fe₃O₄-CGGP),研究了其类芬顿氧化降解苯酚的性能和机制。表征显示，粒径为10～20 nm的Fe₃O₄均匀分散在煤矸石地质聚合物(CGGP)表面形成Fe₃O₄-CGGP,Fe₃O₄-CGGP的饱和磁化强度达到35.68 emu/g,这表明Fe₃O₄-CGGP具有良好的催化活性和磁响应性能。将其应用于降解苯酚废水，实验探讨了pH值、催化剂投加量、H₂O₂投加量以及苯酚初始浓度等条件对苯酚降解过程的影响。实验表明：反应最适宜pH值为3.5,催化剂最佳投加量为0.5 g/L,H₂O₂最佳投加量为10 mmol/L,在最优条件下60 min对苯酚去除率可达到100%.自由基淬灭实验认为在Fe₃O₄-...     

Fe3O4@CTAC粒子的制备及抗菌性能研究

采用溶剂热法合成了分散性良好的Fe₃O₄粒子,然后将油酸修饰到Fe₃O₄粒子表面,再通过疏水作用进行十六烷基三甲基氯化铵(CTAC)包覆,得到Fe₃O₄@CTAC粒子。采用扫描电子显微镜(SEM)、X射线光电子能谱(XPS)、X射线衍射(XRD)、Zeta电位和振动样品磁强计(VSM)对Fe₃O₄@CTAC粒子进行了表征,结果表明：Fe₃O₄粒子表面包覆CTAC后粒径无明显变化,并且仍保持良好的单分散性;Fe₃O₄@CTAC粒子具有超顺磁性和良好的磁响应性能;Fe₃O₄@CTAC粒子的Zeta电位较高,分散体系具有较好的稳定性。对Fe₃O₄@CTAC粒子进行了抗菌性能及磁分离去除菌体测试,结果显示：当Fe₃O_...     

超顺磁性Fe3O4微粒的尺寸调控与磁性回收

以乙二醇为溶剂,通过温和的溶剂热法制备了具有不同颗粒尺寸大小的Fe₃O₄微米粒子.研究发现,通过调节反应体系中水、聚乙二醇-20000和铁离子的浓度,能有效控制Fe₃O₄的成核与生长,从而能实现对Fe₃O₄在较大颗粒尺寸范围内的有效调控.另外,相比小尺寸的Fe₃O₄,较大颗粒尺寸的超顺磁性粒子表现出更优良的磁性回收性能.由此可见,Fe₃O₄颗粒尺寸的有效调控对拓展其在纳米材料磁性回收中的应用具有非常重要的意义     

阶梯热还原法制备Fe3O4/rGO复合膜

先用溶液共混法获得Fe₃O₄纳米颗粒与氧化石墨烯（GO）混合溶液, 再通过阶梯热还原过程（从室温逐渐升至160 ℃）制备Fe₃O₄和还原氧化石墨烯（rGO）复合膜, 并用X射线衍射仪、 Fourier变换红外光谱和扫描电子显微镜表征不同Fe₃O₄质量分数的Fe₃O₄/rGO复合膜的结构和形貌, 用矢量网络分析仪测试复合膜的电磁参数. 实验结果表明, 当Fe₃O₄质量分数为40％时, 复合膜的吸波效能为17.30 dB, 频率为10.72 GHz, 厚度为2 mm, 低于-10 dB[KG*8]的有效吸收带宽为3.28 GHz.     

阶梯热还原法制备Fe3O4/rGO复合膜

先用溶液共混法获得Fe₃O₄纳米颗粒与氧化石墨烯（GO）混合溶液, 再通过阶梯热还原过程（从室温逐渐升至160 ℃）制备Fe₃O₄和还原氧化石墨烯（rGO）复合膜， 并用X射线衍射仪、 Fourier变换红外光谱和扫描电子显微镜表征不同Fe₃O₄质量分数的Fe₃O₄/rGO复合膜的结构和形貌, 用矢量网络分析仪测试复合膜的电磁参数. 实验结果表明, 当Fe₃O₄质量分数为40％时, 复合膜的吸波效能为17.30 dB, 频率为10.72 GHz, 厚度为2 mm, 低于-10 dB[KG*8]的有效吸收带宽为3.28 GHz.     

铁精粉制备α-Fe2O3纳米粒子及其机理

采用商业磁铁矿铁精粉(Fe₃O₄),设计了提纯和制备工艺，成功制备出质量分数为99.5%以上、分散性良好的α-Fe₂O₃纳米粒子，对其提纯、制备工艺及机理进行了深入研究.结果表明：w_NaOH对除硅效果影响显著，当w_NaOH为39%时，可使原料矿粉中w_SiO2由1.11%降至0.032%,得到较纯铁精粉；随烧结温度的升高，α-Fe₂O₃颗粒的结晶度、形貌特征及磁性能随之发生变化；当烧结温度为670℃时，α-Fe₂O₃颗粒综合性能最佳，颗粒结晶度较高、分散性较好，具有亚铁磁性；通过对氢氧化铁沉淀物加热搅拌时间的控制，可有效调控α-Fe₂O₃的晶粒尺寸；当搅拌时间为60 min时，获得分散性好、平均粒径仅为35.3 nm的α-Fe₂O₃纳米粒子.     

Synthesis and characterization of Fe<Subscript>3</Subscript>O<Subscript>4</Subscript>@SiO<Subscript>2</Subscript> magnetic composite nanoparticles by a one-pot process

Fe₃O₄@SiO₂ core–shell composite nanoparticles were successfully prepared by a one-pot process. Tetraethyl-orthosilicate was used as a surfactant to synthesize Fe₃O₄@SiO₂ core–shell structures from prepared Fe₃O₄ nanoparticles. The properties of the Fe₃O₄ and Fe₃O₄@SiO₂ composite nanoparticles were studied by X-ray diffraction, transmission electron microscopy, energy dispersive spectroscopy, and Fourier transform infrared spectroscopy. The prepared Fe₃O₄ particles were approximately 12 nm in size, and the thickness of the SiO₂ coating was approximately 4 nm. The magnetic properties were studied by vibrating sample magnetometry. The results show that the maximum saturation magnetization of the Fe₃O₄@SiO₂ powder (34.85 A·m2·kg–1) was markedly lower than that of the Fe₃O₄ powder (79.55 A·m2·kg–1), which demonstrates that Fe₃O₄ was successfully wrapped by SiO₂. The Fe₃O₄@SiO₂ composite nanoparticles have broad prospects in biomedical applications; thus, our next study will apply them in magnetic resonance imaging.     

水相合成磁性Fe3O4纳米颗粒

采用化学共沉淀法制备Fe₃O₄纳米粒子, 选择NH₃·H₂O作为沉淀剂, 并与Fe²⁺和Fe³⁺的混合溶液同时同速滴加到由氨水和硝酸氨组成的缓冲溶液中, 制得了磁性Fe₃O₄纳米粒子. 考察了磁性纳米粒子合成的一些影响因素, 并用透射电镜(TEM)、 X射线粉末衍射(XRD)、 红外光谱等方法对其性质进行了初步表征.     

纳米Fe3O4/氟碳树脂磁场诱导自组装抗反射薄膜的制备及表征

为了获得高度取向的阵列材料,以水热合成的纳米Fe₃O₄磁性颗粒为功能物质,氟碳树脂为薄膜基体,在磁场作用下定向生长成具有磁性针状阵列结构的自组装抗反射薄膜,并考察不同Fe₃O₄含量对磁性阵列结构的影响;利用体视显微镜和扫描电镜（SEM）对薄膜表面结构进行了表征;采用紫外可见近红外分光光度计（UV/Vis/NIR）来表征自组装薄膜的反射率。结果表明:随着Fe₃O₄含量的增加,阵列高度逐渐增高;当粉体质量分数为10%时,阵列的间距为300～600μm,阵列中单个针状结构中间的直径约为100μm;薄膜表面的阵列结构对于反射率的降低有明显效果     

磁性微球的改性及其固定化铁还原菌的性能

以油酸、聚乙二醇、柠檬酸钠和3-氨丙基三乙氧基硅烷(APTES)为改性剂,采用化学共沉淀法制备4种改性磁性微球.通过粒度测定(PSD)、X射线衍射分析(XRD)、傅里叶红外光谱分析(FTIR)、热重分析(TGA)、磁强度测定(VSM)对各种磁性微球进行表征,并对比各微球固定化铁还原菌后还原Fe(Ⅲ)EDTA的性能,最终确定最佳的磁性微球改性条件.结果表明:APTES改性的Fe₃O₄磁性微球固定化铁还原菌效果优于其他改性微球,其最佳条件为APTES投加量8 mL,1 mg铁还原菌需1.5 g磁性微球进行固定化;APTES-Fe₃O₄固定化铁还原菌后连续使用5次,其Fe(Ⅲ)EDTA还原效率仍可保持在90%以上.     

P(MAA-co-AAm)/Fe_3O_4交联磁性复合微球的表征与药物释放研究

磁性高分子微球是利用微胶囊化方法,使有机高分子与无机磁性粒子Fe₃O₄结合起来形成的具有磁响应性的高分子微球.对以聚(甲基丙烯酸-co-丙烯酰胺)(P(MAA-co-AAm))为高分子基材、四氧化三体(Fe₃O₄)为磁性内核通过化学方法制备的 P(MAA-co-AAm)/Fe₃O₄磁性复合微球性能进行了表征.扫描电镜(SEM)照片显示,复合微球呈现明显的交联结构特征,分散性较好.将茶碱负载到P(MAA-co-AAm)/Fe₃O₄磁性交联复合微球上,对其药物释放情况研究表明,在pH值为7.4的碱性缓冲溶液及去离子水中茶碱释放速率较快,在8 h左右达到释放平衡; 而在pH值为1.4的酸性缓冲溶液中,茶碱的释放缓慢,表明P(MAA-co-AAm)/Fe₃O₄磁性复合微球有很好的pH值响应性.因此,载药交联微球在酸性胃液和碱性肠道液中能够自动调节药物释放速率,具有靶向药物释放效果,P(MAA-co-AAm)/Fe₃O₄交联磁性微球可做为靶向药物载体.     

添加铁氧化物和活性炭对玉米秸秆两相厌氧消化性能和微生物学特性影响研究

为了提高玉米秸秆厌氧消化性能,将铁氧化物（Fe₂O₃,Fe₃O₄）和活性炭分别添加到玉米秸秆两相厌氧消化系统中的酸化相和甲烷相进行试验。结果表明,在酸化相和甲烷相中分别添加Fe₃O₄粉末和活性炭粉末（PAC）的试验组效果最佳。Fe₃O₄粉末添加到酸化相后,挥发性脂肪酸（volatile fatty acids,VFAs）与乙醇的总含量比对照组中两者的总含量提高了25.4%。酸化结束后加入活性炭粉末继续进行甲烷化试验,玉米秸秆累积产甲烷量达到7 965 mL,比对照组提高了27.8%。与对照组相比,添加Fe₃O₄粉末和活性炭粉末试验组的t₈₀（累积产甲烷量达到总甲烷产量的80%所用的时间）缩短了8 d,电导率提高了33.3%。从微生物群落角度分析,在Fe₃O₄+PAC试验组中,细菌优势菌属为Clostridium_sensu_stricto_1,古菌优势菌属为Methanobacterium,可以提高H₂利用率并且促进厌氧过程中的直接种间电子传递（direct interspecies electron transfer,DIET）。因此,Fe₃O₄粉末和活性炭粉末的添加可以有效提高玉米秸秆厌氧消化产甲烷潜力。