TNTAs／g-C3 N4的制备及光催化降解罗丹明B

采用水热法制备了二氧化钛纳米管(TNTAs),以尿素为前驱体采用煅烧法制备了g-C_3N_4,然后通过超声制备了TNTAs/g-C_3N_4复合物,并研究了复合物对罗丹明B(RhB)的光催化降解活性.结果表明:TNTAs与g-C_3N_4的复合,增强了对可见光的利用率,复合物中异质结的形成,有效抑制了催化剂中光生电子和空穴对的复合,TNTAs/g-C_3N_4复合物光催化降解RhB的性能得到了明显提高,其中TNTAs/g-C_3N_4-1∶2具有最高的光催化降解活性.     

Ag/α-Fe_2O_3/g-C_3N_4光催化降解罗丹明B

为了使g-C_3N_4光生电子和空穴容易复合,改善可见光响应低等缺点,该实验中采用溶胶-凝胶法将g-C_3N_4和α-Fe_2O_3进行复合形成g-C_3N_4异质结光催化剂,再采用光沉积法将Ag沉积在α-Fe_2O_3/g-C_3N_4上,构建Z型机制Ag/α-Fe_2O_3/g-C_3N_4催化剂材料,改善光生电荷的分离和传输能力及可见光响应,进一步增强其光催化降解污染物活性.最后通过XRD、FT-IR、XPS、SEM、TEM、紫外-可见漫反射光谱表征光催化剂结构和性能,并以染料罗丹明B溶液模拟废水,研究催化剂的降解动力学特性,通过活性基团捕获实验探究光催化机制.实验结果表明:(1)α-Fe_2O_3和g-C_3N_4复合形成异质结,当α-Fe_2O_3负载量为3%时,α-Fe_2O_3/g-C_3N_4光催化性能比纯的g-C_3N_4有了明显的提高,光催化性能降解罗丹明B达到79%.(2)Ag负载在α-Fe_2O_3/g-C_3N_4,当Ag的负载量为3%时,在可见光下3.5 h能够对罗丹明B达到95%以上的降解.(3)Ag/α-Fe_2O_3/g-C_3N_4增强的光催化剂性归因于α-Fe_2O_3和g-C_3N_4形成异质结以及Ag加入后形成Z型异质结结构.     

AuPd/g-C_3N_4复合光催化剂可控制备及其光催化分解水产氢性能研究

采用两种不同的制备方法合成了AuPd/g-C_3N_4复合光催化剂,并采用透射电子显微镜、X射线光电子能谱、表面光电压谱等研究了材料组成成分及光生电荷的分离效率.研究结果表明,采用光还原原位制备的AuPd二元合金负载的光催化剂具有最优的光催化活性.当负载量为1.0wt%时,AuPd/g-C_3N_4(光)产氢速率是通过化学还原制备的7.4倍,达到了2 140μmol·g~(-1)·h~(-1).研究结果表明,AuPd纳米粒子有利于g-C_3N_4光催化剂产氢活性位点上光生电荷的有效分离.     

g-C_3N_4-P25有机-无机复合物制备及可见光诱导光催化转化CO_2性能研究（英文）

通过简单混合和热处理方法合成了不同g-C_3N_4含量的g-C_3N_4-P25有机—无机复合物。通过XRD、HRTEM、紫外-可见漫反射光谱、红外光谱、XPS光谱和比表面测试对复合光催化剂进行表征。测试结果表明在可见光照射下,含60%或80%g-C_3N_4的g-C_3N_4-P25复合光催化剂的光催化还原CO_2的活性高于单相的g-C_3N_4或P25。合成的有机—无机复合物具有高的光催化活性是由于提高了半导体界面和内部电子-空穴对的分离。     

氮掺杂碳点/富氮类石墨型氮化碳复合光催化剂的制备及产氢性能研究

通过自下而上的方法,以g-C_3N_5为基质、柠檬酸为前驱体,制备了氮掺杂碳点(N-CDs)掺杂g-C_3N_5复合光催化剂.通过X射线粉末衍射仪、扫描电子显微镜、X射线光电子能谱、N_2吸附-脱附等温线、紫外-可见光漫反射光谱及荧光光谱等对材料的组成、表面形貌和化学性能进行表征,以光分解水产氢实验研究了材料的光催化产氢性能.研究结果表明:0.125%N-CDs/g-C_3N_5复合光催化剂具有较多的活性位点,促进了光催化反应的电子传递过程,从而提高了材料的光催化产氢性能;N-CDs的掺杂提高了太阳光利用效率的同时进一步将电子-空穴对的高复合率降低,从而使光催化活性提高;在模拟可见光的光照射下,0.125%N-CDs/g-C_3N_5复合光催化剂的产氢量是g-C_3N_5的3.5倍.     

MOF衍化TiO_2修饰石墨相氮化碳的光催化性能研究

石墨相氮化碳(g-C_3N_4)材料是一种极具潜力的有机光催化材料,尤其是在可见光驱动的光催化分解水制氢方面的应用.然而,较差的光生载流子分离效率严重制约了其光催化活性.选择TiO_2作为修饰材料,在g-C_3N_4表面构建合理的异质结构可以有效解决该问题,但需要进行合理的设计.本文通过较为简单的工艺过程,以金属有机框架材料(MOFs)为牺牲模板,制备MOF衍化TiO_2修饰的g-C_3N_4复合光催化剂.制得的MOF衍化TiO_2的比表面积大,约为124.5 m2/g,并由锐钛矿相/金红石相两相混合组成,这会有效增加光催化剂的光生电子分离效率,并提供更多的催化反应活性位点.通过XRD、SEM、TEM、UV-Vis、PL等表征手段,对材料的物相及相关的光谱学、电化学性质进行了详细的表征,并通过成分调控确定了优化工艺参数.通过相关表征结果可以看出,MOF衍化TiO_2修饰的g-C_3N_4复合光催化剂随着TiO_2的负载量提高而表现更好的载流子分离效率,但其可见光响应会随之降低.因此,存在一个最优的负载量可以均衡二者的影响,从而表现出最高的光催化活性.实验发现,TiO_2的质量分数为6%的光催化剂,其光催化制氢活性在可见光(l≥420 nm)驱动下体现了最高的制氢速率,达836μmol/(g·h).实验结果表明:由MOF衍化TiO_2与g-C_3N_4构建的异质结构可以有效地抑制光生载流子的复合,从而显著提高光催化分解水制氢的性能.     

ZnO/g-C_3N_4复合材料的制备及其光催化性能研究

采用一步法成功制备了氧化锌/石墨相氮化碳(ZnO/g-C_3N_4)复合光催化材料,通过XRD,SEM,TEM,FT-IR和UV-vis DRS对所得样品的微观形貌和吸光特性进行了表征.结果表明,ZnO颗粒均匀分布在片状g-C_3N_4表面上,ZnO/g-C_3N_4最大光吸收边的位置相对于纯相ZnO发生了明显的红移.利用光催化降解甲基橙溶液评估了所得样品的光催化活性,发现ZnO/g-C_3N_4复合材料的光催化效率远高于纯相ZnO和纯相g-C_3N_4,分别达到ZnO的14倍和g-C_3N_4的9倍.复合材料光催化性能得以提升的主要原因有两点:复合样品材料具有比纯相ZnO更大的光吸收范围,提高了太阳光的利用率;ZnO纳米颗粒与g-C_3N_4紧密耦合形成的异质结构有效促进了光生电子-空穴对的分离.     

AgI/GdFeO_3/g-C_3N_4纳米光催化剂的制备及对诺氟沙星的降解研究

为了研究半导体光催化剂的光生载流子效率,增强光催化活性,采用超声辅助水热法制备AgI/GdFeO_3/g-C_3N_4纳米复合光催化剂,结合仪器分析手段对材料的晶体特征和化学性质进行表征,并进行诺氟沙星降解及机制研究.表征结果显示:复合光催化剂呈球片结构,其比表面积为57.93 m~2/g;在氙灯照射180 min时,其对诺氟沙星的降解达到了72.1%.双Z型体系在光催化过程中提高了光生载流子的分离效率,改善了光催化活性.     

g-C_3N_4/TiO_2@Ag复合材料的制备及可见光催化性能研究

以g-C_3N_4和表面沉积Ag的TiO_2微球为原料,超声混合制备了g-C_3N_4/TiO_2@Ag复合材料.采用FT-IR,XRD,XPS,SEM,DRS,UV-Vis和PL等表征手段对材料的结构、形貌及光学性能进行了表征,在可见光照射下测试了其对亚甲基蓝溶液(MB)的光催化活性.结果表明,该复合材料分离光生电子与空穴效率高,对MB的光降解率为97.4%,高于TiO_2@Ag(65.5%)和g-C_3N_4/TiO_2(89.7%)的降解率.     

TiO_2/g-C_3N_4复合物的光催化性能测试及机理研究

利用超声剥离法将块体g-C_3N_4剥离成少层g-C_3N_4,之后与TiO_2进行复合并将所得产物进行二次高温煅烧,得到一种界面间距更小,光生电子传递速率高,光催化性能强的TiO_2/g-C_3N_4的光催化剂。通过XRD,SEM,TEM和FT-IR对其结构进行表征,发现TiO_2是以化学键的形式均匀地附着在少层g-C_3N_4表面;UV-vis和PL分析表明,该催化剂实现了紫外区到可见区的全覆盖吸收,并能有效地抑制光生电子和空穴的复合;降解实验和分解水制氢实验表明TiO_2的负载量为3%时其光催化性能最好,100 min时对罗丹明B的降解率达到87.7%,光催化分解水制氢速率高达68.62μmol h~(-1)。探讨总结了该复合物的光催化机理。     

Relaxor behavior of (1-x)Pb(Mg1/3Nb2/3)O3-xPbTiO3 ceramics

n the present work, the phase transitions and relaxor behavior of (1−x)Pb(Mg_1/3Nb_2/3)O₃-xPbTiO₃ (PMN-PT, x = 0.2―0.4) ferroelectric ceramics have been investigated by means of X-ray diffraction, di-electric spectroscopy, the P-E hysteresis loop measurements and Raman scattering techniques. Structural analysis revealed that with the increase of PbTiO₃ content, PMN-PT ceramics experienced a gradual phase transition process from rhombohedral to tetragonal. It is usually believed that such kinds of phase transitions resulted in the linear decrease of relaxation degree. Surprisingly, our analy-sis of the dielectric spectra revealed that the indicator of the degree of diffuseness γ reached the maximum value near morphotropic phase boundary (MPB) (x = 0.32), then decreased with the further increase of PbTiO₃ content. The large dielectric relaxor feature near MPB may be attributed to the for-mation of ordered nanodomains, resulting from complex coexisting nanostructures. Further, the P-E hysteresis loop measurements and Raman analysis of the B-site cation order correlated well with the dielectric measurement results. It was found that the hysteresis loop squareness R_sq received the minimum value while the inverse of the value of full wide of half maximum (FWHM) of A_1g mode reached the maximum value at MPB composition, which showed similar trends to γ.     

Comparison study of chitosan/β-cyclodextrin and carboxymethyl chitosan/β-cyclodextrin microspheres

To compare two microspheres of chitosan/β-cyclodextrin and carboxymethyl chitosan/β-cyclodextrin loaded theophylline as pulmonary sustained drug delivery carriers, the characteristics and ciliotoxicity were studied. The drug loadings of chitosan/β-cyclodextrin and carboxymethyl chitosan/β-cyclodextrin microspheres were 21.09% and 21.42%, and the encapsulation efficiencies were 91.40% and 92.80%. The distributions of 50% (d _0.5) of chitosan/β-cyclodextrin and carboxymethyl chitosan/β-cyclodextrin microspheres were 4.89 and 5.83 μm, respectively. Both microspheres showed spherical shape with smooth or wrinkled surfaces. FT-IR of chitosan/β-cyclodextrin microspheres demonstrated that theophylline had formed hydrogen bonds with chitosan and β-cyclodextrin, while for the carboxymethyl chitosan/β-cyclodextrin microspheres theophylline had interaction with carboxymethyl chitosan. The moisture absorption showed that an equilibrium was reached within 24 h. The two microspheres possessed better adaptability. In vitro release of theophylline from chitosan/β-cyclodextrin microspheres was slower than that from carboxymethyl chitosan/β-cyclodextrin microspheres at pH 6.8. Biography: LI Ruobao(1968–), male, Associate professor, research direction: foundation research of respiratory system.     

完全图Kn的{P5,C5}分解

图分解问题已在很多邻域中得到了广泛的应用。用P₅表示5个顶点的路，C₅表示5个顶点的圈，本研究讨论了完全图K_n分解成5个顶点的路P₅和圈C₅的存在性，给出完全图K_n存在{P₅,C₅}-强制分解的充分必要条件是n≥7(n≠8)，以及完全图K_n存在{P₅,C₅}-分解的充分必要条件是n≥5(n≠6)。     

The concentration quenching characteristics of 5D3-7FJ and 5D4-7FJ (J=0―6) transitions of Tb3+ in YBO3:Tb3+ phosphor

The photoluminescence quenching behaviors of ^5D3-^7Fj and ^5D4-^7Fj （J = 0—6） transitions of Tb^3＋ in YBO3：Tb under 130—290 nm excitation were systematically investigated. The results revealed that the quenching concentrations of both ^5D3-^7Fj and ^5D4-^7Fj transitions of Tb^3＋ in YBO3：Tb were mainly dependent on excitation wavelength. Particularly, the quenching concentrations of ^5D4-^7Fj transitions of Tb^3＋ under 130—290 nm excitation were correlated with excitation bands of YBO3：Tb. The quenching concentrations of ^5D3-^7Fj transitions remained at low concentration （2%） under 186—290 nm excitation and then increased gradually with energy of incoming excitation photon when excited at 130—186 nm. This dependence should be involved in their excitation mechanisms and quenching pathway in particular excitation region.[第一段]     

KH_2PO_4催化Hantzsch反应合成4H-色烯衍生物(英文)

4H-色烯衍生物作为一种便宜易得的酸性无机盐,可有效催化Hantzsch反应合成4H-色烯衍生物.在优化条件下,4H-色烯衍生物可通过简单的过滤操作直接分离得到,含有催化剂的滤液则可以继续催化该反应,循环催化3次而不失活.这为4H-色烯衍生物的合成提供了一种实用且绿色化程度较高的方法,有潜在的工业化应用前景.     

小桐子生物碱粗提物杀虫抑菌活性的初步研究

目的 为了探索小桐子综合开发利用的价值,对小桐子生物碱粗提物杀虫抑菌活性进行初步研究。方法 以攀西地区2种农业主要害虫（甘蓝蚜虫、菜青虫）和3种病原菌（石榴干腐病菌、苹果腐烂病菌和草莓灰霉病菌）为试验材料,采用点滴法和生长速率法对小桐子生物碱粗提物的杀虫抑菌活性进行了生物测定。结果 在杀虫活性方面,小桐子生物碱粗提物对同翅目甘蓝蚜虫和鳞翅目菜青虫均具有较高触杀活性,其LC₅₀值范围为42.247 8~46.249 7 mg/L,LC₉₀值范围为331.714 0~342.491 7 mg/L,总体上与2.5%溴氰菊酯EC的杀虫效果相当;在抑制病原真菌方面,小桐子生物碱粗提物对石榴干腐病菌、苹果腐烂病菌和草莓灰霉病菌的EC₅₀分别为 70.635 5、52.400 6和133.412 2mg/L,其抑菌效果一定程度上优于对照药剂50%多菌灵WP。结论 小桐子提取物有较强的杀虫抑菌作用,在植物源农药的开发方面具有良好的应用前景。     

弱c*-正规子群与有限群的p-幂零性

引入弱c*-正规子群的定义,并利用此定义得到有限群p-幂零的两组充分条件.     

K3单群的新刻画

设G是有限群,t(G)为G的素图连通分支数.当t(G)≥2时,对K_3单群进行研究,得到了:(i)若G是有限群,M是除L_2(7),U_4(2)的K_3单群,则G■M当且仅当t(G)≥2且|G|=|M|;(ii)若G是有限群,M是L_2(7),U_4(2)单群,当t(G)≥2且|G|=|M|时,得到了群G的一些特征描述.