粉体粒度对K2O-Al2O3-SiO2系微晶玻璃析晶动力学的影响

采用烧结法制备了K_2O-Al_2O_3-SiO_2系微晶玻璃.研究了不同粒度分布的玻璃粉对K_2O-Al_2O_3-SiO_2系微晶玻璃的析晶及对其性能的影响,进而优化制备K_2O-Al_2O_3-SiO_2系微晶玻璃的粉体粒度.结果表明:玻璃粉体的细化有利于析晶,玻璃粉体平均粒径从38.09μm减小到1.80μm时,微晶玻璃的析晶温度从913.9℃降低至869.9℃.析晶活化能从320.5kJ/mol减小至234.7kJ/mol.微晶玻璃的析出晶相均为白榴石,玻璃粉体平均粒径为6.30μm时,微晶玻璃的微观结构较为均匀,密度为2.45g·cm~(-3),抗弯强度为74.93 MPa,热膨胀系数为14.32×10~(-6) K~(-1).     

Pr3+-Yb3+共掺氟氧化物微晶玻璃的显微结构及发光性能

制备了Pr2+-Yb2+共掺SiO2-AlO3-Na2O-CaF2体系玻璃,并通过优化热处理工艺获得了透明氟氧化物微晶玻璃.运用动力学方法分析了系统玻璃的析晶机制,探讨了热处理温度、玻璃析晶行为和显微结构的关系.采用XRD和SEM等方法研究了CaF2纳米晶的形成,晶粒大小为30 nm,且稀土离子进入CaF2纳米晶中,形...     

颗粒粒度及钾长石含量对矿渣微晶玻璃析晶能力的影响

利用k值法计算了不同颗粒粒度下不同钾长石添加量高炉渣微晶玻璃的晶化能和析晶动力学参数,采用DSC、XRD及SEM等测试手段研究了粉体粒度和钾长石含量对微晶玻璃析晶能力的影响。结果表明,颗粒粒度对微晶玻璃析晶能力影响显著,微晶玻璃析晶能力随颗粒粒度减小而增大;钾长石对微晶玻璃析晶能力有一定促进作用,但随着粉体粒度的减小而逐渐减弱,钾长石含量过高时,不利于微晶玻璃析晶,钾长石添加量应以5 wt%左右为宜。在5℃/min升温速度下,球磨60 h,添加5 wt%钾长石的样品具有较好的微观形貌,其主晶相为镁黄长石,晶体成颗粒状,晶粒均匀且结合紧密。     

热处理对CaO-Al2O3-SiO2系微晶玻璃性能影响

以CaO-Al2O3-SiO2为主要原料,采用烧结法制备出微晶玻璃.利用DSC确定了核化温度和晶化温度.利用XRD和SEM研究微晶玻璃的物相组成和显微结构.通过研究热处理温度对微晶玻璃性能的影响,可得出在780℃核化1h、948℃晶化2h时,微晶玻璃的性能最好.     

晶核剂对MgO-Al_2O_3-SiO_2系微晶玻璃析晶的影响

目的研究单掺和复掺晶核剂条件下主晶相为堇青石的Mg O-Al_2O_3-SiO_2微晶玻璃的析晶性能.方法以工业级化学试剂为主要原料,采用熔融法制备了Mg O-Al_2O_3-SiO_2系微晶玻璃.运用X射线衍射(XRD)、扫描电镜(SEM)等测试手段进行析晶分析.结果 TiO_2和ZrO_2单掺和复掺均有利于微晶玻璃析晶过程的进行,但并不会改变微晶玻璃主、次晶相的种类,主晶相为α-堇青石,次晶相为镁铝钛酸盐.随着ZrO_2含量的增加,析晶温度、析晶活化能逐渐降低,动力学析晶参数逐渐升高;随着TiO_2含量的增加,析晶温度、析晶活化能先降低后升高,动力学析晶参数先升高后降低.结论 TiO_2和ZrO_2均可作为Mg O-Al_2O_3-SiO_2系微晶玻璃的晶核剂,TiO_2较ZrO_2更有利于促进Mg O-Al_2O_3-SiO_2系微晶玻璃的析晶,且析出的晶体数量更多,柱状的α-堇青石晶体形态更为完整.当TiO_2和ZrO_2复掺时,最有利于促进体系析晶.     

CaO对CaO-Al_2O_3-SiO_2系微晶玻璃析晶行为的影响

利用烧结工艺制备微晶玻璃以CaO Al2O3 SiO2三元系微晶玻璃为研究对象,通过DTA,XRD,SEM分析方法,对玻璃析晶动力学进行研究·利用Kissinger方程来计算微晶玻璃析晶转变的活化能E,发现随着氧化钙含量的增加,析晶温度降低,析晶活化能降低,并最终推导出析晶机理参数n=2,体系属于整体析晶·实验结果发现:微晶玻璃的析晶相均为硅灰石结构;氧化钙含量的增加有利于微晶玻璃的晶化,但表面缺陷更明显,如:坑点、突起、断裂等·     

CaO对CaO-Al_2O_3-SiO_2系微晶玻璃析晶行为的影响

利用烧结工艺制备微晶玻璃以CaO Al2O3 SiO2三元系微晶玻璃为研究对象,通过DTA,XRD,SEM分析方法,对玻璃析晶动力学进行研究·利用Kissinger方程来计算微晶玻璃析晶转变的活化能E,发现随着氧化钙含量的增加,析晶温度降低,析晶活化能降低,并最终推导出析晶机理参数n=2,体系属于整体析晶·实验结果发现:微晶玻璃的析晶相均为硅灰石结构;氧化钙含量的增加有利于微晶玻璃的晶化,但表面缺陷更明显,如:坑点、突起、断裂等·     

锗酸盐微晶玻璃的显微结构与红外透过性能

用传统熔体冷却法制备含成核剂的CaO-BaO-Y2O3-Al2O3-SiO2-GeO2玻璃,并采用两步法工艺获得不同热处理条件下的微晶玻璃.采用DSC,XRD和SEM等分析测试方法研究不同热处理制度对锗酸盐微晶玻璃的析晶行为、显微结构以及红外透过性能的影响.研究结果表明:当晶化温度为930～1 010℃时,可以获得半透明的锗酸盐微晶玻璃,其单个晶粒粒径为40～100 nm;当晶化温度低于990℃时,锗酸盐微晶玻璃具有良好的光学透过性能,其透过波段为可见光区至5.0μm附近的中红外光区,透过率可达80％以上；影响微晶玻璃光学透明性的因素除了微晶体的粒径、晶体含量以及微晶体折射率与母体玻璃折射率之差外,微晶体的团聚可能也是决定微晶玻璃光学透过性的重要因素.     

一种新型钨尾矿微晶玻璃

介绍了以钨尾矿为主要原料制备微晶玻璃的方法。用X射线衍射和偏光显微镜分析了微晶玻璃的析晶相及显微结构,探讨了微晶化制度,并对其主要性能进行了测试。结果表明,钨尾矿微晶玻璃的各项性能优良,是一种新型的建筑装饰及耐磨、耐腐蚀材料。     

添加氧化锆对钢渣微晶玻璃显微结构的影响

采用熔融法制备微晶玻璃材料，探讨了钢渣微晶玻璃中引入ZrO2对其显微结构以及性能的影响。用X衍射仪和扫描电镜分析了微晶玻璃的主晶相和显微结构。实验结果表明：引入质量分数为1％的ZrO2时，微晶玻璃的晶粒最小，抗弯强度最大；当ZrO2的添加量进一步增多，晶粒无法发育完全且晶相含量下降，导致微晶玻璃的抗弯强度降低。在该钢渣微晶玻璃中，ZrO2最佳添加量的质量分数为1％。     

钢渣基高碱度微晶玻璃的一步法制备及工艺参数研究

为了提高微晶玻璃原料中高钙冶金渣的掺量,需要制备出碱度更高的微晶玻璃. 本文采用一步法,以钢渣为主要原料,制备碱度( CaO与SiO2的质量比)为0. 9的钢渣基高碱度微晶玻璃. 通过X射线衍射分析、扫描电镜和性能测试等手段,研究热处理条件对微晶玻璃微观形貌及线收缩率、体积密度和抗折强度等性能的影响规律. 研究表明,高碱度微晶玻璃适合采用一步法制备工艺,当在1100℃保温120 min时,微晶玻璃烧结过程基本完成,此时获得最大体积密度2. 4 g·cm-3 ,最高抗折强度56. 4 MPa. 微晶玻璃的主晶相为钙铝黄长石,副晶相为辉石. 基础玻璃颗粒在升温过程中完成了成核和析晶过程,而在保温过程中主要进行的是基础玻璃颗粒的烧结致密化和晶体的进一步发育. 升温至1100℃保温30 min,微晶玻璃的抗折强度超过45 MPa,微晶玻璃内部晶体呈方柱状交织排列并构成晶体骨架分布在残余的玻璃基体中;随着保温时间的增加,微晶玻璃的线性烧结收缩率、体积密度和抗折强度均逐渐增大,而晶相的含量基本保持不变,晶体逐渐由球形颗粒状和短柱状发育为长柱状. 晶体的形状以及与残余玻璃相构成的整体致密结构是导致高碱度微晶玻璃力学性能提高的主要因素.     

Influence of CeO<Subscript>2</Subscript> addition on the preparation of foamed glass-ceramics from high-titanium blast furnace slag

Foamed glass-ceramics doped with cerium oxide (CeO₂) were successfully prepared from high-titanium blast furnace slag by one-step sintering. The influence of CeO₂ addition (1.5wt%–3.5wt%) on the crystalline phases, microstructure, and properties of foamed glass-ceramics was studied. Results show that CeO₂ improves the stability of the glass phase and changes the two-dimensional crystallization mechanism into three-dimensional one. XRD analysis indicates the presence of Ca(Mg, Fe)Si₂O₆ and Ca(Ti, Mg, Al)(Si, Al)₂O₆ in all sintered samples. Added with CeO₂, TiCeO₄ precipitates, and crystallinity increases, leading to increased thickness of pore walls and uniform pores. The comprehensive properties of foamed glass-ceramics are better than that of samples without CeO₂. In particular, the sample added with a suitable amount of CeO₂ (2.5wt%) exhibits bulk density that is similar to and compressive strength (14.9 MPa) that is more than twice of foamed glass-ceramics without CeO₂.     

晶核剂对Li2O-ZnO-SiO2系玻璃析晶行为及性能的影响

采用差热分析、X射线衍射及傅里叶红外吸收光谱等测试手段，分析不同晶棱剂对Li2O-ZnO-SiO2系统玻璃析晶行为和性能的影响。研究结果表明：要获得高热膨胀性微晶玻璃Li2O-ZnO-SiO2，关键在于基础玻璃中方石英晶相的析出，晶棱剂P2O5在该系统玻璃中具有成棱作用，并能促进方石英固溶体的析出，使微晶玻璃获得较好的力学性能（抗弯强度为133MPa，雏氏硬度为638MPa）；晶棱剂TiO2对于促进方石英晶相析出的能力较差，且当玻璃中不舍Al2O3时，TiO2的成核效果不明显，获得的晶粒较粗。     

由熔融高炉渣制备微晶玻璃

采用熔融法,由熔融高炉渣制备性能稳定的基础玻璃.通过对基础玻璃的差热分析确定微晶玻璃的热处理工艺制度.结合X射线衍射分析、扫描式电子显微镜观察等现代研究方法,确定了微晶玻璃热处理制度的最佳工艺参数,并研究了微晶玻璃的晶体生长方式.微晶玻璃的热处理最佳工艺参数为：核化温度850℃,保温1.5 h;晶化温度935℃,保温1 h.玻璃首先从表面开始析晶,然后逐步向内部生长.实验所得微晶玻璃的力学性能,如抗折强度、耐酸碱性和硬度,均优于天然大理石.     

钙硅氧化物的质量比对10%Al2 O3高炉渣--尾矿--粉煤灰微晶玻璃性能的影响

利用高炉渣、尾矿和粉煤灰各自成分特点,在未添加任何晶核剂和其他化学试剂条件下,使用烧结法制得了不同CaO/SiO2质量比的10%Al2 O3(质量分数)矿渣微晶玻璃.通过差热分析、X射线衍射、扫描电子显微镜等分析手段,分析了CaO/SiO2质量比和析晶温度对高炉渣-尾矿-粉煤灰微晶玻璃样品的晶相变化规律、析晶行为和主要力学性能的影响.随着CaO/SiO2质量比增大,析晶活化能不断减小,Si-O四面体连接强度下降,质点移动加强,各组开始析晶温度和晶化温度逐渐减小.当玻璃样品中钙硅氧化物的质量比为0.4时,分别在886℃和982℃形核、析晶保温1 h 后,可以得到抗折强度103.59 MPa、显微硬度5.3 GPa、耐酸性0.25%(质量损失率)、耐碱性小于0.1%,主晶相为透辉石的最佳力学性能的微晶玻璃样品.     

玻璃组成对CaO-Al2O3-SiO2系玻璃烧结、晶化和性能的影响

采用烧结法制备以钙长石为主晶相的微晶玻璃.采用差热分析(DTA)、X射线衍射(XRD)、扫描电镜(SEM)和性能测试研究玻璃组成对玻璃的烧结、晶化特性和性能的影响.结果表明:随着CaO含量的增加,玻璃转变温度和析晶放热峰温度逐渐降低,而且析晶放热峰变得尖锐;增加氧化钙降低玻璃的析晶活化能,有利于玻璃的析晶;随着SiO2量的增加,玻璃转变温度和析晶放热峰温度移向高温,使玻璃的析晶困难;玻璃样品的烧结温度随CaO含量的增加而降低, 但过多的CaO促进硅酸钙的析出,增加样品的介电常数和热膨胀系数;增加SiO2能够降低微晶玻璃样品的热膨胀系数,改善其介电性能;所制备的微晶玻璃具有相对密度高(≥98.3%),介电常数适中(6.9～7.5),介电损耗低(≤0.1%),热膨胀系数低(3.8×10-6～4.5×10-6 /℃),烧结温度(900～1 000 ℃)低,及介电常数温度稳定性低(66×10-6～113×10-6 /℃).     

CaO-ZrO2-TiO2-Al2O3-B2O3-SiO2玻璃陶瓷的制备及化学稳定性研究

玻璃陶瓷是固化处理中、高放废物和α废物较为理想的候选材料之一。研究了特定条件下制备的CaO-ZrO2-TiO2-Al2O3-B2O3-SiO2体系玻璃陶瓷在水淬和空气中自然冷却的两种冷却制度对其结晶行为和显微结构的影响,用粉末浸泡实验方法测试了其化学稳定性。结果表明:自然冷却形成的玻璃陶瓷晶相主要是ZrSiO4和ZrTiO4;在25～70℃范围内,温度对玻璃陶瓷浸出率无明显影响,90℃下浸出率比25℃,40℃,70℃的浸出率高一个数量级;7 d元素总的归一化浸出为1.87 g/m2。     

热处理时间对赤泥粉煤灰微晶玻璃抗压强度影响

以94％的赤泥和粉煤灰为原料,采用烧结法制备了微晶玻璃,利用XRD、SEM等测试手段分析试样的物相及形貌,根据DTA曲线显示,考查热处理时间对微晶玻璃抗压强度的影响。结果表明：微晶玻璃的主晶相为钙铝黄长石;随着核化和晶化时间的延长,微晶玻璃的抗压强度呈现了先增加后减小的趋势;最佳核化时间为2h,晶化时间为2h;最大抗压强度为102．84MPa。     

B_2O_3-TiO_2掺杂堇青石微晶玻璃制备及其晶化行为

按照堇青石化学计量配比,掺杂B2O3-TiO2,采用溶胶-凝胶法配合回流制备了以α-堇青石为主晶相的微晶玻璃.利用差热分析、X射线衍射、扫描电镜等测试手段,对该玻璃样品的晶化过程进行了试验观察,探讨了B2O3-TiO2在堇青石基微晶玻璃晶化过程中的作用.结果表明:样品在从无定形态到堇青石微晶玻璃的转变过程中,过渡相为镁铝尖晶石和β-石英固溶体,该结果说明B2O3起到了抑制μ-堇青石形成的作用.另外,TiO2作为形核剂,通过先在玻璃相中形成富钛小液滴来诱导非均匀成核,从而促进α-堇青石析晶.断面扫描电镜图像显示所得微晶玻璃为整体析晶.     

利用油页岩渣制备微晶玻璃

以油页岩渣为主要原料制备了微晶玻璃,探讨了微晶玻璃组成、主晶相确定和晶核剂选择等问题.采用DTA,XRD和SEM等测试手段,分析了晶核剂和热处理制度对微晶玻璃的影响.结果表明:复合晶核剂(TiO2+P2O5)能有效促进油页岩渣玻璃晶化;最佳热处理制度为:850℃核化100 min,980℃晶化80 min.微晶玻璃的主晶相为钙铁透辉石,次晶相为钙长石;晶体呈纤维状结构并且交错分布;性能明显优于同类的瓷质砖、大理石和花岗岩等建筑装饰材料.