| 16Mn(HIC)钢硫化物应力腐蚀开裂实验研究 | |
| 引用本文： | 李明,李晓刚,陈钢,刘智勇.16Mn(HIC)钢硫化物应力腐蚀开裂实验研究[J].北京科技大学学报,2007,29(3):282-287. |
| 作者姓名： | 李明 李晓刚 陈钢 刘智勇 |
| 作者单位： | 1. 北京科技大学材料科学与工程学院,北京,100083;中国特种设备检测研究中心,北京,100013 2. 北京科技大学材料科学与工程学院,北京,100083 3. 中国特种设备检测研究中心,北京,100013 |
| 基金项目： | 中国石油化工集团公司资助项目 , 国家重点基础研究发展计划(973计划) |
| 摘 要： | 采用恒应变和慢应变速率拉伸实验的方法,研究了16Mn(HIC)和16Mn钢母材、焊缝在H2S环境中应力腐蚀开裂.结果表明:两种材料在酸性H2S介质中均发生穿晶型硫化物应力腐蚀开裂(SSCC);与16Mn钢相比,16Mn(HIC)钢有更好的抗SSCC性能,钢中的C,Mn,P和S的含量降低有利于提高钢的抗SSCC性能.焊缝及热影响区在焊接过程中,产生的粗大魏氏组织、偏析、缩孔和夹杂等缺陷,降低了焊缝的抗SSCC能力.但是,通过焊后热处理可以适当提高焊缝的抗SSCC能力. |
| 关 键 词： | 16Mn钢 硫化物应力腐蚀开裂(SSCC) 焊缝 氢致开裂 热处理 硫化物应力腐蚀开裂 拉伸实验 研究 steel cracking resistance induced hydrogen stress corrosion cracking sulfide investigation 焊后热处理 能力 缺陷 缩孔 偏析 魏氏组织 焊接过程 焊缝及热影响区 含量 性能 |
| 修稿时间： | 2005-12-19 |
Experimental investigation on sulfide stress corrosion cracking of 16Mn hydrogen induced cracking resistance steel |
|
| LI Ming,LI Xiaogang,CHEN Gang,LIU Zhiyong.Experimental investigation on sulfide stress corrosion cracking of 16Mn hydrogen induced cracking resistance steel[J].Journal of University of Science and Technology Beijing,2007,29(3):282-287. | |
| Authors: | LI Ming LI Xiaogang CHEN Gang LIU Zhiyong |
| Institution: | 1 Materials Science and Engineering School, University of Science and Technology Beijing, Beijing 100083, China; 2 China Special Equipment Inspection and Research Center, Beijing 100013, China |
| Abstract: | Constant strain bend and slow strain rate tests (SSRT) were used to investigate the resistance to sulfide stress corrosion cracking (SSCC) of 16Mn and 16Mn hydrogen-induced cracking (HIC) resistance steels and their welded seams in acid solutions with saturated hydrogen sulfide gas. The results show that all of samples are sensitive to SSCC in the acidic solutions with H2S. The mechanism of cracking is HIC and most cracks are transgranular type. The resistance to SSCC of 16Mn(HIC) steel with low content elements C, Mn, P and S is better than that of 16Mn steel. Otherwise, the welded seams have less resistance to SSCC than their matrix because of big crystals, inclusions, vacancies and defects produced in the process of welding, but the work of post welding heat treatment (PWHT) can increase the resistance of their welded seams. |
| Keywords: | 16Mn steel sulfide stress corrosion cracking welded seams hydrogen-induced cracking heat treatment |