| 钒对中铬白口铸铁组织和性能的影响 |
| |
| 引用本文： | 刘克明,王福明,郝经伟,余煌.钒对中铬白口铸铁组织和性能的影响[J].北京科技大学学报,2004,26(6):604-607,626. |
| |
| 作者姓名： | 刘克明 王福明 郝经伟 余煌 |
| |
| 作者单位： | 北京科技大学冶金与生态工程学院,北京,100083 |
| |
| 基金项目： | VANITEC(国际钒技术委员会)资助项目 |
| |
| 摘 要： | 研究了钒对中铬白口铸铁的组织与性能的影响.采用SEM与EDS对试样进行了组织与成分分析,并测定了试样的冲击韧性、硬度等力学性能.结果表明:随着V含量的增加,中铬白口铸铁的组织得到细化,冲击韧性得到改善;当V的加入量增加至4%(质量分数)时,基体上弥散分布大量VC颗粒,使得材料有潜在的良好的耐磨性能.
|
| 关 键 词： | 钒 中铬白口铸铁 力学性能 中铬白口铸铁 铸铁组织 耐磨性能 影响 Cast Iron Chromium Medium Microstructure and Properties Effect 材料 颗粒 弥散分布 基体 质量分数 加入量 改善 含量 结果 力学性能 硬度 |
Vanadium Effect on Microstructure and Properties of Medium Chromium White Cast Iron |
| |
| LIU Kerning,WANG Fuming,HAO Jingwei,YU HuangMetallurgical and Ecological Engineering School,University of Science and Technology Beijing,Beijing ,China.Vanadium Effect on Microstructure and Properties of Medium Chromium White Cast Iron[J].Journal of University of Science and Technology Beijing,2004,26(6):604-607,626. |
| |
| Authors: | LIU Kerning WANG Fuming HAO Jingwei YU HuangMetallurgical and Ecological Engineering School University of Science and Technology Beijing Beijing China |
| |
| Institution: | LIU Kerning,WANG Fuming,HAO Jingwei,YU HuangMetallurgical and Ecological Engineering School,University of Science and Technology Beijing,Beijing 100083,China |
| |
| Abstract: | In order to study the effect of vanadium addition on the microstructure and properties of medium chromium white cast iron, the microstructure and composition of samples made of the cast iron were analyzed by SEM and EDS. The impact energy and Rockwell hardness of the samples were tested. The results indicate that with an increase in vanadium content, the microstructure of medium chromium white cast iron becomes finer and the impact energy values are enhanced. When the mass fraction of vanadium exceeds 4%, a large amount of VC precipitates occur, which make the cast iron have potentially favorable wear resistance. |
| |
| Keywords: | vanadium medium chromium white cast iron mechanical properties |