| Abstract: | In the present work, it was studied that nano-sized NiO electrodes doping with C and Co were prepared by electrochemical deposition in an ethanol solution containing nickel nitrate and cobalt nitrate and sintering processes. The capacitance performance of such electrodes was also studied. The results reveal that samples obtained by electrochemical deposition first on a porous nickel cathode in an ethanol solution contain 0.5 mol/L nitrates, in which Ni(NO3)2 and Co(NO3)2 were mixed in a molar proportion of 8:2. After sintering at 300 °C for 2 h, they exhibited the best performance. XRD analysis illustrates that the essential phase of the product is NiO doping with certain content of C and Co. The particles of product imaged a spherical morphology with sizes of 20–30 nm in diameter, and with an average crystal size of 4–5 nm. The capacitance measurement of the simulating C/NiO capacitors indicates that a single electrode can reach as high as 410.0 F/g, and still maintain the value of 323 F/g after 30 recycles showed as a stabilized value with increasing recycles, when it was discharged at a current of 5 mA. |