基于无机p型NiO缓冲层的钙钛矿发光二极管发光特性研究
引用本文:卢经文,袁文,李德怀,莫小明,周宇璐,欧阳义芳.基于无机p型NiO缓冲层的钙钛矿发光二极管发光特性研究[J].广西科学,2016,23(5):465-469.
作者姓名:卢经文  袁文  李德怀  莫小明  周宇璐  欧阳义芳
作者单位:广西大学物理科学与工程技术学院,广西南宁,530004
基金项目:国家自然科学基金项目(11504060),广西壮族自治区教育厅高等学校科学研究项目(KY2015ZD006),广西大学博士启动项目(XBZ160084)资助。
摘    要:【目的】研究如何提高溴基钙钛矿(CH3NH3PbBr3)发光二极管的发光亮度。【方法】通过在氧化铟锡(ITO)玻璃基底上引入无机p型NiO缓冲层与有机聚合物聚(3,4-亚乙二氧基噻吩)-聚(苯乙烯磺酸)(PEDOT∶PSS)形成有机/无机杂化空穴传输层,提高空穴注入效率,降低电子溢出。【结果】引入无机p型NiO缓冲层形成有机/无机杂化空穴传输层后,发光二极管的发光亮度提高了约1倍。【结论】该方法不仅可降低PEDOT∶PSS对ITO基底的腐蚀,还能显著提高空穴注入效率,提高发光二极管的发光亮度。

关 键 词:钙钛矿  空穴传输层  杂化  发光二极管
收稿时间:2016/9/9 0:00:00
修稿时间:2016/10/16 0:00:00

Improved Performance by Introducing Inorganic p-Type NiO Layer for Perovskite Light-emitting Diodes
LU Jingwen,YUAN Wen,LI Dehuai,MO Xiaoming,ZHOU Yulu and OUYANG Yifang.Improved Performance by Introducing Inorganic p-Type NiO Layer for Perovskite Light-emitting Diodes[J].Guangxi Sciences,2016,23(5):465-469.
Authors:LU Jingwen  YUAN Wen  LI Dehuai  MO Xiaoming  ZHOU Yulu and OUYANG Yifang
Institution:School of Physical Science and Technology, Guangxi University, Nanning, Guangxi, 530004, China,School of Physical Science and Technology, Guangxi University, Nanning, Guangxi, 530004, China,School of Physical Science and Technology, Guangxi University, Nanning, Guangxi, 530004, China,School of Physical Science and Technology, Guangxi University, Nanning, Guangxi, 530004, China,School of Physical Science and Technology, Guangxi University, Nanning, Guangxi, 530004, China and School of Physical Science and Technology, Guangxi University, Nanning, Guangxi, 530004, China
Abstract:Objective]How to improve the brightness of bromine-based perovskite (CH3 NH3 PbBr3 )light-emitting diodes (LEDs)has drawn increasingly extensive attention.Methods]A specially designed organic/inorganic hybrid layer composed of p-NiO and PEDOT:PSS on indium tin oxide (ITO)substrate is used as hole transport layer (HTL)to improve the hole inj ection efficiency as well as to reduce the current overflow effect.Results]By utilizing the p-NiO/PEDOT: PSS hybrid HTL,the emission intensity of the CH3 NH3 PbBr3-based LED has been improved nearly one fold.Conclusion]This method can be an effective route to improve the brightness and efficiency for the perovskite LEDs due to the improved hole injection efficiency by using the p-NiO/PEDOT:PSS hybrid HTL.
Keywords:perovskite  hole transport layer  hybrid  light-emitting diode