Glass-forming ability,microhardness, corrosion resistance,and dealloying treatment of Mg60-xCu40Ndx alloy ribbons |
| |
作者姓名: | Hao-yi Chi Zhen-gui Yuan Yan Wang Min Zuo De-gang Zhao Hao-ran Geng |
| |
作者单位: | Shandong Provincial Key Laboratory of Preparation and Measurement of Building Materials, School of Materials Science and Engineering, University of Jinan, Jinan 250022, China |
| |
摘 要: | The influence of Nd addition on the glass-forming ability (GFA), microhardness, and corrosion resistance of Mg60-xCu40Ndx (x=5, 10, 15, 20, and 25, at%) alloys were investigated by differential scanning calorimetry, Vickers-type hardness tests, and electrochemical methods. The results suggest that the GFA and microhardness of the amorphous alloys increase until the Nd content reaches 20at%. The corrosion potential and corrosion current density obtained from the Tafel curves indicate that the Mg35Cu40Nd25 ternary alloy exhibits the best corrosion resistance among the investigated alloys. Notably, nanoporous copper (NPC) was synthesized through a single-step dealloying of Mg60-xCu40Ndx (x=5, 10, 15, 20, and 25) ternary alloys in 0.04 mol·L-1 H2SO4 solution under free corrosion conditions. The influence of dealloying process parameters, such as dealloying time and temperature, on the microstructure of the ribbons was also studied using the surface diffusivity theory. The formation mechanism of dealloyed samples with a multilayered structure was also discussed.
|
关 键 词: | amorphous alloys glass-forming ability microhardness corrosion resistance dealloying |
本文献已被 SpringerLink 等数据库收录! |
| 点击此处可从《矿物冶金与材料学报》浏览原始摘要信息 |
| 点击此处可从《矿物冶金与材料学报》下载免费的PDF全文 |
|