Optimization of RPC technique for refining the intermediate transformation microstructure |
| |
Institution: | Materials Science and Engineering School, University of Science and Technology Beijing, Beijing 100083, China |
| |
Abstract: | The influence of processing parameters of relaxation-precipitation-controlling phase transformation (RPC) technique, finish rolling temperature, reduction ratio and relaxing time on the microstructurewas studied by thermo-simulation for a low carbon Nb and Ti containing micro-alloyed steel. The microstructure was investigated by optical microscope, transmission electron microscope and electron back scatterdiffraction (EBSD). The statistical results of the packet size were calculated. It shows that, after RPC process, the steel is a composite microstructure of bainite and matensite. The best thermo-simulation process for refinement in this experiment is deformation for 30% at 850℃, and then relaxing at this temperature for 60 s to 200 s. Increasing the reduction ratio from 30% to 60% or decreasing the deformation temperature to 800℃ would cause the best relaxation time to become shorter, increasing the deformation temperature to 900℃ would cause the refinement effect to be weak. |
| |
Keywords: | RPC technique microstructure refinement deformation temperature reduction |
本文献已被 万方数据 等数据库收录! |
| 点击此处可从《矿物冶金与材料学报》浏览原始摘要信息 |
| 点击此处可从《矿物冶金与材料学报》下载免费的PDF全文 |
|