超音速等离子喷涂制备的Al–25Si–4Cu–1Mg耐磨涂层的组织与性能 |
| |
作者单位: | 1)School of Materials Science and Engineering, Hebei University of Technology, Tianjin 300130, China |
| |
摘 要: | A high content silicon aluminum alloy (Al–25Si–4Cu–1Mg) coating was prepared on a 2A12 aluminum alloy by supersonic plasma spraying. The morphology and microstructure of the coating were observed and analyzed. The hardness, elastic modulus, and bonding strength of the coating were measured. The wear resistance of the coating and 2A12 aluminum alloy was studied by friction and wear test. The results indicated that the coating was compact and the porosity was only 1.5%. The phase of the coating was mainly composed of α-Al and β-Si as well as some hard particles (Al9Si, Al3.21Si0.47, and CuAl2). The average microhardness of the coating was HV 242, which was greater than that of 2A12 aluminum alloy (HV 110). The wear resistance of the coating was superior to 2A12 aluminum alloy. The wear mechanism of the 2A12 aluminum alloy was primarily adhesive wear, while that of the coating was primarily abrasive wear. Therefore, it is possible to prepare a high content silicon aluminum alloy coating with good wear resistance on an aluminum alloy by supersonic plasma spraying.
|
关 键 词: | ,,,,,,, |
|
| 点击此处可从《矿物冶金与材料学报》浏览原始摘要信息 |
| 点击此处可从《矿物冶金与材料学报》下载免费的PDF全文 |
|