半工艺无取向硅钢加临界变形的织构演变

测定了半工艺无取向电工钢热轧(终轧温度在Ar1以下)到成品各工序的织构,以取向分布函数(ODF)的形式对加临界变形的半工艺无取向硅钢的织构演变作了分析.发现其热轧板表层织构基本是典型的铁素体再结晶{111}组分,心部和1/4厚度处以铁素体剪切织构和轧制变形织构为主.冷轧变形后,心部和表层织构组分比较接近,{111}、{112}和{100}面织构都增加,但{111}组分增加最明显.软化退火后,{001}<110>与{112}<110>组分迅速降低,织构组分以γ纤维织构为主.通过增加临界变形,在最终去应力退火后,{111}不利面织构大量减少,高斯组分增加明显.Taylor因子可以表征不同取向晶粒对变形能的储存能力,从轧制变形时Taylor因子的分布可以解释该实验结果.

Texture evolution of semi-processed non-oriented silicon steel with temper rolling

Macrotextures of a semi-processed non-oriented silicon steel were measured in the production process from hot rolling (with the finish rolling temperature below Ar1) to final stress relief annealing, and the texture evolution were analyzed in the form of orientation distribution function. It was found that the main component in the surface layer of a hot rolled strip was {111} plane texture resulting from ferritic recrystallization; while shear texture and rolling texture were dominant at the center and at ...