雾化沉积Cu-13．5％Sn合金的显微组织和力学性能研究

本文采用雾化沉积工艺制备了Cu-13．5wt％Sn合金；研究其轧制性能；分析其轧制机理。结果表明：与传统铸造Cu—Sn合金相比，该合金晶粒细小，组织均匀，无宏观偏析，基体为单相α—Cu组织；Sn含量从8wt．％上升到13．5wt．％；轧制后表现出良好的综合力学性能，强度和塑性随着形变量的不同在一个较宽的范围内变化，可以满足不同使用需求；具有高强度（〉800MPa）低弹性模量（～88GPa）的特点。这在晶体金属材料领域是独一无二的，可以预测该合金将会在弹性元件领域具有广泛的应用前景。

Study on Microstructure and Mechanical Properties of Spray-deposited Cu-13.5% Sn Alloy

The Cu-13.5 wt% Sn alloy is prepared by spay deposition; the cold rolling characteristics and mechanism of this alloy are discussed. The results indicate that compared with the traditional as-cast ingot,this alloy has gotten a quite fine and homogeneous single-phase structure with single-phase α-Cu ; the content of Sn is improved from 8 wt. % to 13.5 wt. % ; excellent workability is shown ; the strength and plasticity change with the deformation in a wide range for different requirement. This alloy has a high flow stress over 800 MPa and a low elastic modulus about 88GPa. It is unique in the domain of metallic materials and could give a new possibilities in spring technology field.