焊接规范参数对带极堆焊电弧发生率的影响

采用焊接电压波形分析法，对影响宽带极（７５ｍｍ）电渣堆焊和高速带极堆焊电弧发生率的因素及其变化规律进行研究，结果表明：对这两种堆焊方法，影响堆焊过程电弧发生率的因素主要是焊接电流、电压和焊接速度，带极干伸长度和磁控电流在堆焊工艺所用的范围内变化时，对电弧发生率的影响较小。带极电渣堆焊和高速带极堆焊，随着焊接电流、电压和焊接速度的增加，电弧发生率随之增大，其中以焊接电压和焊接速度的影响最为显著。高速堆焊时，当焊接电压大于２８Ｖ或焊接速度高于３０ｃｍ／ｍｉｎ时，电弧发生率较高，堆焊过程不稳定。通过多次试验研究，得到了两种堆焊新工艺的最佳规范参数。在此规范参数下焊接，可获得优质堆焊焊道。

Effects of the Welding Condition Parameters on the ratio of Arc Generation in the Strip Surfacing Processes

By waveform analysis of the welding voltage , some factors influencing the ratioof arc generation and nature are investigated in the Electro-slag surfacing and high speed sur-facing with 75 mm strip. The experimental results show that show that these factors are mainly weld-ing current, voltage and speed of both surfacing processes. As the strip stick-out length andmagnetic control current are varied in the useful range of the stirfacing processes, the effecton the ratio is small. With increasing welding currout , voltage and speed, the ratio of arcgeneration is increased in the both surfacing processes, Among them, the effects of weldingvoltage and speed on it are very conspicuous . If welding voltage is increased up to 28 V orwelding speed up to 30 cm/min , the ratio will overgrow and the welding process will be in-stable in the high speed surfacing process. Based on experimental investigations the opti-mum welding condition parameters are given for these two new surfacing processes. Onthese conditions ,good weld quality can be obtained.