Formation and corrosion properties of Fe-based bulk metallic glasses |
| |
Authors: | Chun-lei Zhu Qing Wang Jie Zhang Ying-min Wang Chuang Dong |
| |
Affiliation: | 1.School of Material Science and Engineering,Dalian University of Technology,Dalian,China |
| |
Abstract: | Bulk metallic glass (BMG) formation was explored in the Fe-B-Si-Nb alloy system though combined use of the atomic cluster line approach and the minor alloying strategy. The basic ternary compositions in the Fe-B-Si system were determined by the intersection points of two cluster lines, namely, Fe-B cluster to Si and Fe-Si cluster to B. 3at%–4at% Nb was added to the quaternary Fe-B-Si-Nb alloy. The casting experiments revealed that good glass-forming ability (GFA) occurred at the (Fe73.4Si8.2B18.4)96Nb4 composition, and 3-mm diameter BMG samples were made. The glass transition temperature (T g), crystallization temperature (T x), and supercooled liquid region (ΔT x=T x−T g) of this BMG were measured to be 866, 889, and 23 K, respectively. The BMG shows a high Vickers hardness of about Hv 1164, a Young’s modulus of 180 GPa, and a good corrosion resistance in the solutions of 1 mol/L HCl and 3wt% NaCl. |
| |
Keywords: | |
本文献已被 万方数据 SpringerLink 等数据库收录! |
| 点击此处可从《矿物冶金与材料学报》浏览原始摘要信息 |
|
点击此处可从《矿物冶金与材料学报》下载免费的PDF全文 |
|