| 界面反应层厚度对Ti／ZrO2钎焊接头强度的影响 |
| |
| 引用本文： | 黄小丽,林实.界面反应层厚度对Ti／ZrO2钎焊接头强度的影响[J].河北理工学院学报,1998,20(4):6-10. |
| |
| 作者姓名： | 黄小丽 林实 |
| |
| 作者单位： | [1]北京信息工程学院 [2]北京科技大学 |
| |
| 摘 要： | 通过活性钎料Ａｇ６６Ｃｕ３０Ｔｉ４对ＺｒＯ２的浸润试验测定了钎料／陶瓷界面反应产物，浸润角和反应层厚度与温度的关系。将Ｔｉ和ＺｒＯ２在不同温度下进行钎焊连接，得出了接头强度和钎焊温度（即反应层厚度）的关系，存在一最佳厚度，此时可获得较高的连接强度。
|
| 关 键 词： | 钎焊 界面反应 钛 氧化锆 焊接接头 强度 |
THE EFFECT OF THICKNESS OF INTERFACIAL REACTION LAYER ON Ti ZrO 2 JOINT STRENGTH |
| |
| Huang Xiaoli.THE EFFECT OF THICKNESS OF INTERFACIAL REACTION LAYER ON Ti ZrO 2 JOINT STRENGTH[J].Journal of Hebei Institute of Technology,1998,20(4):6-10. |
| |
| Authors: | Huang Xiaoli |
| |
| Abstract: | The wetting test of active solder Ag 66 Cu 30 Ti 4 to ZrO 2 was studied in this paper.The interfacial product of solder ceramic was defined and the dependence of wetting angle and reaction layer thickness on temperature was obtained.Ti and ZrO 2 were bonded by traze at different temperature and the relationship of joint strength with temperature (i.e. reaction layer thickness) was found.There was a optimum thickness,when the higher joining strength was reached. |
| |
| Keywords: | ZrO 2 Active solder Braze welding Interfacial reaction |