| Synthesis of a NiTi2-AlNi-Al2O3 nanocomposite by mechanical alloying and heat treatment of Al-TiO2-NiO |
| |
| 作者姓名： | Reza Beygi Majid Zarezadeh Mehrizi Hossein Mostaan Mahdi Rafiei Ahmadreza Abbasian |
| |
| 作者单位： | Department of Materials Engineering and Metallurgy, Faculty of Engineering, Arak University, Arak 3815688349, Iran |
| |
| 摘 要： | The aim of the present study was to investigate the phases formed during ball milling of Al-TiO2-NiO. For this purpose, a mixture of Al-TiO2-NiO with a molar ratio of 6:1:1 was used. Characterization of the milled powders by X-ray diffraction, differential thermal analysis, field-emission scanning electron microscopy, and transmission electron microscopy showed the formation of nanocrystalline NiTi2 along with AlNi. A thermodynamical investigation confirmed that NiO was reduced by Al during ball milling, which consequently promoted TiO2 reduction and the formation of NiTi2. Al is capable of reducing NiO either during ball milling or at temperatures above the melting point of Al; by contrast, TiO2 can be reduced by Al only by milling.
|
| 关 键 词： | mechanical alloying NiTi2-AlNi nanocomposite reaction mechanism |
Synthesis of a NiTi2-AlNi-Al2O3 nanocomposite by mechanical alloying and heat treatment of Al-TiO2-NiO |
| |
| Reza Beygi,Majid Zarezadeh Mehrizi,Hossein Mostaan,Mahdi Rafiei,Ahmadreza Abbasian.Synthesis of a NiTi2-AlNi-Al2O3 nanocomposite by mechanical alloying and heat treatment of Al-TiO2-NiO[J].International Journal of Minerals,Metallurgy and Materials,2019,26(3):345-349. |
| |