| Microstructure s and mechanical properties of Ti3Al/Ni-based superalloy joints arc welded with Ti –Nb and Ti– Ni – Nb filler alloys |
| |
| 作者姓名： | Bingqing Chen Huaping Xiong Bingbing Sun Siyi Tang Borui Du Neng Li |
| |
| 作者单位： | Laboratory of Welding and Forging,Beijing Institute of Aeronautical Materials |
| |
| 摘 要： | Dissimilar joining of Ti3Al-based alloy to Ni-based superalloy has been carried out using gas tungsten arc(GTA) welding technology with Ti–Nb and Ti–Ni–Nb filler alloys.The joint welded with the Ti–Nb filler alloy contained much less interfacial brittle phases than the one using the Ti–Ni–Nb filler alloy.The average room-temperature tensile strength of the joint welded with Ti–Nb was 202 MPa and the strength value of the one welded with Ti–Ni–Nb was 128 MPa.For both fillers,the weak links of the dissimilar joints were the weld/In718 interfaces.The presence of TiNi,TiNi3 and Ni3Nb intermetallic compounds in the joint welded with Ti–Ni–Nb induced microcracks at the weld/In718 interface and deteriorated the mechanical properties of the joint.And the adoption of the Ti–Nb filler alloy decreased the formation tendency of interfacial brittle phases to some extent and thus enhanced the tensile strength of the joint.
|
| 关 键 词： | Ti3Al Ni-based superalloy Arc welding Interface Intermetallics Mechanical properties |
| 收稿时间： | 2014-03-26 |
| 本文献已被 维普 ScienceDirect 等数据库收录！ |
| 点击此处可从《自然科学进展(英文版)》浏览原始摘要信息 |
|
点击此处可从《自然科学进展(英文版)》下载全文 |