Investigation of the deterioration of passive films in H2S-containing solutions
Authors:Zhu Wang  Lei Zhang  Xian Tang  Zhao-yang Cui  Jun-peng Xue  Min-xu Lu
Affiliation:1. Institute of Advanced Materials and Technology, University of Science and Technology Beijing, Beijing 100083, China;2. Institute of Advanced Materials and Technology, University of Science and Technology Beijing, Beijing 100083, China;Safetech Research Institute, Beijing 100083, China
Abstract:The effect of H2S on the corrosion behavior of 316L stainless steel was investigated using electrochemical methods by changing the gas condition from CO2 to H2S and then back to CO2. The presence of H2S showed an acceleration effect on the corrosion of 316L stain-less steel in comparison with CO2. The acceleration effect remained even after the complete removal of H2S by CO2, indicating that the pas-sive film was irreversibly damaged. X-ray photoelectron spectroscopy (XPS) analysis indicated that the passive film was composed of Cr2O3, Fe2O3, and FeS2 after being immersed in H2S-containing solutions. The semiconducting property of the passive film was then investigated by using the Mott–Schottky approach. The presence of sulfides resulted in higher acceptor and donor densities and thus was responsible for the deterioration of passive films.
Keywords:stainless steel  passive films  hydrogen sulfide  corrosion
本文献已被 万方数据 等数据库收录!
设为首页 | 免责声明 | 关于勤云 | 加入收藏

Copyright©北京勤云科技发展有限公司  京ICP备09084417号