Microstructure and stress rupture properties of polycrystal and directionally solidified castings of nickel-based superalloys |
| |
Authors: | Bao-ping Wu Lin-han Li Jian-tao Wu Zhen Wang Yan-bin Wang Xing-fu Chen Jian-xin Dong Jun-tao Li |
| |
Institution: | 1. Central Iron & Steel Material Research Institute, Beijing, 100081, China 2. School of Materials Science and Engineering, University of Science and Technology Beijing, Beijing, 100083, China
|
| |
Abstract: | A new directionally solidified Ni-based superalloy DZ24, which is a modification of K24 alloy without rare and expensive elemental additions, such as Ta and Hf, was studied in this paper. The microstructure and stress rupture properties of conventionally cast and directionally solidified superalloys were comparatively analyzed. It is indicated that the microstructure of K24 alloy is composed of γ, γ′, γ/γ′ eutectics and MC carbides. Compared with the microstructure of K24 polycrystalline alloy, γ/γ′ eutectic completely dissolves into the γ matrix, the fine and regular γ′ phase reprecipitates, and MC carbides decompose to M6C/M23C6 carbides after heat treatment in DZ24 alloy. The rupture life of DZ24 alloy is two times longer than that of K24 alloy. The more homogeneous the size of γ′ precipitate, the longer the rupture life. The coarsening and rafting behaviors of γ′ precipitates are observed in DZ24 alloy after the stress-rupture test. |
| |
Keywords: | superalloys nickel alloys microstructure precipitation carbides mechanical properties |
本文献已被 维普 万方数据 SpringerLink 等数据库收录! |
| 点击此处可从《矿物冶金与材料学报》浏览原始摘要信息 |
| 点击此处可从《矿物冶金与材料学报》下载免费的PDF全文 |
|