| 焊接咬边导致锅炉管板开裂失效及其预防 |
| |
| 引用本文： | 李怀生. 焊接咬边导致锅炉管板开裂失效及其预防[J]. 科技情报开发与经济, 1997, 7(3): 40-41 |
| |
| 作者姓名： | 李怀生 |
| |
| 作者单位： | 大同市广灵县劳动服务公司 |
| |
| 摘 要： | 以一具体实例，详细分析了焊接咬边导致锅炉管板开裂的原因，并提出了预防措施
|
| 关 键 词： | 焊接咬边 焊接残余应力 应力集中 疲劳裂纹 锅炉 |
Prevention of Cracking of Boiler''s Tube and Plate Caused by Weld Undercutting |
| |
| Li Huaisheng. Prevention of Cracking of Boiler''s Tube and Plate Caused by Weld Undercutting[J]. Sci-Tech Information Development & Economy, 1997, 7(3): 40-41 |
| |
| Authors: | Li Huaisheng |
| |
| Affiliation: | Li Huaisheng |
| |
| Abstract: | Taking a boiler as an example,the reason of boiler tube's and plate's cracking caused by weld undercutting is analyzed,and prevention measures are suggested. |
| |
| Keywords: | weld undercutting welding residual stress stress concentration fatigue crack boiler |