| 12Cr1MoV连铸钢坯高温力学性能研究 |
| |
| 引用本文： | 康丽,王洋,王恩刚,赫冀成. 12Cr1MoV连铸钢坯高温力学性能研究[J]. 东北大学学报(自然科学版), 2007, 28(10): 1393-1396. DOI: - |
| |
| 作者姓名： | 康丽 王洋 王恩刚 赫冀成 |
| |
| 作者单位： | 1. 东北大学,材料电磁过程研究教育部重点实验室,辽宁,沈阳,110004
2. 首钢股份有限公司,北京,100043 |
| |
| 基金项目： | 国家自然科学基金，国家高技术研究发展计划(863计划) |
| |
| 摘 要： | 在Gleeble-1500热模拟机上进行了低合金钢12Cr1MoV热模拟实验,测试了从600℃到峰值温度,涵盖了连铸时从结晶器到输出辊道的整个温度范围,得出了12Cr1MoV在不同应变速率不同温度下的流变曲线、强度曲线和热塑性曲线,观察了不同温度下试样的断口形貌组织.实验结果表明:低合金钢12Cr1MoV的ZST为1425℃,ZDT为1400℃.在1100~1300℃范围内,钢的断面收缩率均大于60%,具有良好的塑性;脆性范围为1350℃到熔点和900℃以下.
|
| 关 键 词： | 连铸 低合金钢 高温力学性能 热塑性 热模拟 |
| 文章编号： | 1005-3026（2007）10-1393-04 |
| 修稿时间： | 2006-10-24 |
On High-Temperature Mechanical Properties of 12Cr1MoV Steel During Continuous Casting |
| |
| KANG Li,WANG Yang,WANG En-gang,HE Ji-cheng. On High-Temperature Mechanical Properties of 12Cr1MoV Steel During Continuous Casting[J]. Journal of Northeastern University(Natural Science), 2007, 28(10): 1393-1396. DOI: - |
| |
| Authors: | KANG Li WANG Yang WANG En-gang HE Ji-cheng |
| |
| Affiliation: | 1. Key Laboratory of National Education Ministry for Electromagnetic Processing of Materials, Northeastern University, Shenyang 110004, China; 2. Shougang Co. Ltd., Beijing 100043, China |
| |
| Abstract: | The high-temperature mechanical properties of the low-alloy steel 12Cr1MoV during continuous casting were tested on a Gleeble-1500 thermal simulator within the temperature range from mold to outlet rollers. As a result, the plastic flow and strength and thermal plasticity curves at different strain rates from 600°C to peak temperature were given, with fracture morphology of specimens observed at different temperature. The test results showed that the ZST and ZDT of the steel are 1425°C and 1400°C, respectively. The percentage reduction of area of the tested steel is greater than 60% within the range from 1100°C to 1300°C, thus showing that the steel has higher resistance to high-temperature cracking. Its brittle temperature range is 1350°C to melting point and below 900°C. |
| |
| Keywords: | continuous casting low-alloy steel high-temperature mechanical properties thermo-plasticity thermal simulation testing |