巯基功能化3DOM TiO2-SiO2吸附剂制备及吸附性能研究

 采用胶晶板法，以聚苯乙烯胶晶为膜板，钛酸丁酯和3-巯基-丙基-三甲氧基硅烷为前驱物一步共聚缩合，制备了巯基功能化的3DOM TiO₂-SiO₂有机-无机杂化材料。SEM、EDS和FTIR测试表明，适当控制前驱物比例，可以制得高度有序的巯基功能化三维大孔材料。对重金属汞离子的吸附容量、吸附动力学等测试表明，这种新型材料对汞离子吸附容量高，达到吸附平衡较快，吸附行为符合Freundlich方程，吸附活化能为30 kJ/mol, 扩散系数仅为10^-12～10^-13m²/s，表明吸附过程仍受一定扩散阻力影响。

Preparation and Adsorption Properties of Thiol Functioned 3DOM TiO2-SiO2 Adsorbents

Using polystyrene (PS) colloidal crystal as template, (3-mercaptopropyl) trimethoxysilane (MPTMS) and tetra-n-butyl titanate (TBT) as precusors, threedimensional ordered macroporous (3DOM) TiO₂-SiO₂-SH adsorbents were successfully fabricated via sol-gel method. The SEM, EDS and FTIR results show that by controlling the ratio of TBT to MPTMS, highly ordered three dimensional macroporous thio-groups functioned adsorbents can be btained. Adsorption properties of the adsorbents for mercury ion have been determinated,showing a higher capacity. The adsorption isotherms fit the Freundlich equation. The activation energy is 30 kJ/mol, and diffusion coefficient is only 10^-12～10^-13 m²/s. These results show that adsorption remains slower and a diffusion resistance in a certain extent.