| 20CrMnTi钢粒状贝氏体的消除 |
| |
| 引用本文： | 冉旭,董占丰.20CrMnTi钢粒状贝氏体的消除[J].吉林工学院学报,1999,20(2):15-20. |
| |
| 作者姓名： | 冉旭 董占丰 |
| |
| 作者单位： | [1]吉林工学院材料工程系 [2]长春水泵厂 |
| |
| 摘 要： | 经过实验室研究和一汽生产试验，通过化学分析和金相分析观察，找到了２０ＣｒＭｎＴｉ钢出现粒状贝氏体的原因是铬含量偏高和微量钼含量偏高；提出消除该钢种粒状贝氏体的等温退火最佳工艺，硬度和金相组织符合要求，解决了生产中的难题。
|
| 关 键 词： | 粒状贝氏体 淬透性 等温退火 钢 铬钢 |
Elimination of Granular Bainite in 20CrMnTi Steel |
| |
| Ran Xu,Chen Li,Wu Zhantian.Elimination of Granular Bainite in 20CrMnTi Steel[J].Journal of Jilin Institute of Technology,1999,20(2):15-20. |
| |
| Authors: | Ran Xu Chen Li Wu Zhantian |
| |
| Abstract: | The cause of the presence of granular bainite in the as normalized 20CrMnTi steel has been found through both laboratory work and production test in the First Auto Works. A higher Cr content than that required in the specification and an extra amount of Mo were found to be responsible. An optimum isothermal annealing process has been established to eliminate the granular bainite in the steel, with both the hardness and microstructure up to the standard. |
| |
| Keywords: | granular bainite hardenability isothermal annealing |