| 缓释型聚羧酸减水剂的合成和性能研究 |
| |
| 引用本文： | 崔子亮,王艳玲,陈义兴,罗三一,陈卫丰.缓释型聚羧酸减水剂的合成和性能研究[J].三峡大学学报(自然科学版),2014(1):64-67. |
| |
| 作者姓名： | 崔子亮 王艳玲 陈义兴 罗三一 陈卫丰 |
| |
| 作者单位： | [1]三峡大学化学与生命科学院,湖北宜昌443002 [2]宜昌力华混凝土有限公司,湖北宜昌443000 |
| |
| 基金项目： | 三峡大学人才启动基金项目（KJ2012B025） |
| |
| 摘 要： | 本文使用马来酸酐、丙烯酸羟乙酯和甲基烯丙基聚氧乙烯醚大单体通过水溶液自由基共聚法合成了一种缓释型聚羧酸减水剂,并讨论了原料配比和合成工艺对减水剂性能的影响.结果表明,当n（MA）∶n（TPEG）∶n（HEA）=3.5∶1∶1,引发剂用量为单体总质量的3.0％,反应温度为80℃,反应时间为4.5h,所合成的减水剂在掺量0.2％时,即使在35℃高温下,水泥净浆流动度初始达258 mm,1.5h时仅损失30 mm,达到了很好的缓释效果.
|
| 关 键 词： | 聚羧酸减水剂 缓释型 合成 |
Research on Synthesis and Performance of Sustained-Release Polycarboxylate Superplasticizer |
| |
| Cui Ziliang Wang Yanling Chen Yixing Luo Sanyi Chen Weifeng.Research on Synthesis and Performance of Sustained-Release Polycarboxylate Superplasticizer[J].Journal of China Three Gorges University(Natural Sciences),2014(1):64-67. |
| |
| Authors: | Cui Ziliang Wang Yanling Chen Yixing Luo Sanyi Chen Weifeng |
| |
| Institution: | Cui Ziliang Wang Yanling Chen Yixing Luo Sanyi Chen Weifeng (1. College of Chemistry ＆ Life Science, ChinaThree Gorges Univ. , Yichang 443002, China; 2. Yichang Li- hua Concrete Co. , Ltd. , Yichang 443000, China) |
| |
| Abstract: | A new kind of sustained-release type polycarboxylate superplasticizer was synthesized through radi- cal polymerization by using methyl allyl polyethenoxy ether（TPEG）, maleic anhydride and hydroxyethyl acry- late. The effect of the mole ratio of raw materials and synthesis process on its dispersion property was investi- gated. The results show that when n（MA） ： n（TPEG） ： n（HEA）=3.5 ： 1 ： 1, initiator dosage in an amount of 3% of the total mass of the monomer, the reaction temperature of 80℃, dropping monomer for 3-4 hours, the dispersion performance of the superplasticizer is the best. When cement is added 0.2% of the agent, even at 35℃, the fluidity of cement paste achieve 258 mm at first and lose of only 30 mm in 90 min; it is indicated that the agent has a good sustained-release effect. |
| |
| Keywords: | polycarboxylate superplasticizer sustained-release synthesis |