| Ni9铸钢沿晶断裂的研究 |
| |
| 引用本文： | 张伟 李隆盛. Ni9铸钢沿晶断裂的研究[J]. 大连理工大学学报, 1993, 33(2): 157-161 |
| |
| 作者姓名： | 张伟 李隆盛 |
| |
| 作者单位： | 大连理工大学材料工程系(张伟，李隆盛)，大连理工大学材料工程系(程骥) |
| |
| 摘 要： | 观察了Ｎｉ９铸钢的断口形貌，分析研究了沿晶断裂的形成原因，考察了稀土元素对沿晶断裂倾向的影响．结果表明Ｎｉ９铸钢中沿晶断裂的形成主要与杂质元素Ｈ、Ｐ在晶界偏聚有关．添加稀土后，钢的沿晶断裂倾向明显降低，脆性沿晶断裂消失．
|
| 关 键 词： | 晶界 Ni9铸钢 断裂 晶间裂纹 |
Study of intercrystalline fracture of cast steel Ni9 |
| |
| Zhang Wei,Li Longsheng,Cheng Ji. Study of intercrystalline fracture of cast steel Ni9[J]. Journal of Dalian University of Technology, 1993, 33(2): 157-161 |
| |
| Authors: | Zhang Wei Li Longsheng Cheng Ji |
| |
| Abstract: | The fracture morphology of cast steel Ni9 is observed. The cause of intercrystalline fracture formation is studied. The tendency of intercrystalline fracture of cast steel both with and without rare earth addition is also researched. The results show that intercrystalline fracture formation of the cast steel Ni9 seems to be mainly related to the segregation of contaminants H and P along boundaries. In the case of addition of rare earth in cast steel Ni9 ,the tendency of intercrystalline fracture is remarkably reduced ,and the brittle intercrystalline fracture is nearly eliminated. |
| |
| Keywords: | grain boundary intergranular crack segregation rare earth elements/cast steel Ni9 |