1 Results It is generally known that CuO2 planes of layered cuprate superconductors play a major role on the variation of critical temperature,Tc.In order to investigate their microscopic and electronic properties,preparation of such materials in single crystal form with highly structure orientation is very important.Crystal growth techniques for copper oxide materials have greatly improved since the discovery of high Tc superconductor materials[1].However,a strong reaction between CuO flux and crucible material has been a serious problem in crystal growth by using crucible,especially in a self-flux slow cooling method that needs long time.It is important to avoid the contamination from crucible material and also the ‘creeping out' problem of CuO flux during long time and high sintering temperature.In this study,we attempted to grew the GdBaSrCu3O7-δ single crystals via self-flux slow cooling technique.They were grown from CuO-rich nonstoichiometric solutions as similar as the YBCO case with approximately cation and powder ratio used as reported before[2-3].
|