一步法回收锂离子电池三元正极材料及其性能影响
引用本文:王媛,杨茹,缪建麟,赵瑞瑞.一步法回收锂离子电池三元正极材料及其性能影响[J].华南师范大学学报(自然科学版),2021,53(1):36-41.
作者姓名:王媛  杨茹  缪建麟  赵瑞瑞
作者单位:广州市能源检测研究院,广州511400;华南师范大学化学学院,广州510006
基金项目:国家质量监督检验总局科技计划项目2017QK146
摘    要:采用直接一步法回收废旧锂离子电池中的三元正极材料LiNi0.5Co0.2Mn0.3O2,将拆解得到的三元废料经分离、热解处理后进行酸浸,对酸浸溶液进行元素测定后补加Ni、Co、Mn源,使其物质的量之比符合n(Ni):n(Co):n(Mn)=5:2:3.调整后的溶液直接与草酸钠溶液进行共沉淀,得到草酸盐前驱体,最后与锂源...

关 键 词:锂离子电池  三元正极材料  一步法回收
收稿时间:2020-03-26

One-Step Recycling of Trinary Cathode Materials in Lithium Ion Batteries and the Impact on Their Performance
Institution:1.Guangzhou Energy Testing Institute, Guangzhou 511400, China2.School of Chemistry, South China Normal University, Guangzhou 510006, China
Abstract:A direct one-step recycling process was developed to recycle the trinary materials from the spent lithium ion batteries. The spent materials were collected after battery disassembling, electrode separation and pyrolysis and subjected to acid leaching. The element concentration in the obtained solution from the leaching process was determined with elemental analysis, and proper Ni, Co and Mn sources were added into the solution, achieving a ratio of n(Ni)∶n(Co)∶n(Mn)=5∶2∶3. The adjusted solution was directly used to co-precipitated with sodium oxalate and the obtained oxalate precipitates were mixed with Li sources. The trinary materials were obtained after sintering. The results exhibited that the recycled materials with this method could release a discharge capacity of 162 mAh/g and had a capacity retention ratio of 88% after 100 cycles. However, high-content impurity would affect the material performance, resulting in inferior electrochemical properties. This novel method can avoid the resource waste and energy loss in the traditional recycling process, whereby every metal is separated. The obtained materials through this process have higher additional value, promising an attractive commercial prospect.