蒙脱石负载硫掺杂赤铁矿复合材料的光芬顿催化性能及其增强机理研究
引用本文:何家鸿,吴宏海,卢鹏澄.蒙脱石负载硫掺杂赤铁矿复合材料的光芬顿催化性能及其增强机理研究[J].华南师范大学学报(自然科学版),2021,53(1):42-49.
作者姓名:何家鸿  吴宏海  卢鹏澄
作者单位:华南师范大学环境学院,广州510006;华南师范大学环境学院,广州510006;华南师范大学环境学院,广州510006
基金项目:国家自然科学基金项目42072046广东省自然科学基金项目2018B030311021
摘    要:采用水热联合煅烧法合成了一种蒙脱石负载S掺杂赤铁矿的高效新型非均相芬顿催化剂(S-α-Fe2 O3/Mnt).采用X射线衍射(XRD)、X射线光电子能谱(XPS)、电子顺磁共振(EPR)以及捕获测试方法对催化剂进行表征,并深入研究了催化性能及其增强机理.结果表明:S-α-Fe2 O3/Mnt的可见光芬顿催化性能良好,且...

关 键 词:光芬顿  硫掺杂  氧缺陷  赤铁矿  蒙脱石
收稿时间:2020-03-26

The Photo-Fenton Catalytic Property of the Sulfur-Doped Hematite over Montmorillonite Composite and Its Enhancement
Institution:School of Environment, South China Normal University, Guangzhou 510006
Abstract:A novel heterogeneous Fenton-catalyst (named S-α-Fe2O3/Mnt) was successfully synthesized by doping sulfur into hematite loaded over montmorillonite. The methods of XRD, XPS, EPR and capture test were used to characterize the catalyst for determination of its Fenton catalytic performance and the mechanism of its enhancement. S-α-Fe2O3/Mnt had an efficient photo-Fenton catalytic performance with phenol used as a model pollutant in a wide pH range. When pH was 3.0, the Fenton reaction was extremely rapid and 50 mg/L phenol could be 100% degraded in 10 min. When pH was 5.0, the phenol degradation rate was somewhat decreased, but 50 mg/L phenol could be still completely degraded within 60 min. The research results demonstrated that the sulfur doping had made the sulfur ions enter the structure of the α-Fe2O3 fraction in S-α-Fe2O3/Mnt and this led to a large number of oxygen vacancies formed in the catalyst, which could enhance its photocatalytic performance; on the other hand, the surface acidic sites of montmorillonite could widen the effective pH range of the novel catalyst. Therefore, S-α-Fe2O3/Mnt can be a promising heterogeneous Fenton-catalyst for the application in environmental remediation.
Keywords: