Mechanical properties and friction behaviors of CNT/AlSi10Mg composites produced by spark plasma sintering |
| |
| Authors: | Lin-zhi Wang Ying Liu Jiao-jiao Wu Xi Zhang |
| |
| Affiliation: | 1.Chongqing Key Laboratory of Additive Manufacturing Technology and Systems, Chongqing Institute of Green and Intelligent Technology,Chinese Academy of Sciences,Chongqing,China;2.College of Material Science and Engineering,Sichuan University,Chengdu,China;3.College of Material Science and Engineering,Southwest Jiaotong university,Chengdu,China |
| |
| Abstract: | The mechanical properties and friction behaviors of CNT/AlSi10Mg composites produced by spark plasma sintering (SPS) were investigated. The results showed that the densities of the sintered composites gradually increased with increasing sintering temperature and that the highest microhardness and compressive strength were achieved in the specimen sintered at 450°C. CNTs dispersed uniformly in the Al-Si10Mg matrix when the addition of CNTs was less than 1.5wt%. However, when the addition of CNTs exceeded 1.5wt%, the aggregation of CNTs was clearly observed. Moreover, the mechanical properties (including the densities, compressive strength, and microhardness) of the composites changed with CNT content and reached a maximum value when the CNT content was 1.5wt%. Meanwhile, the minimum average friction coefficient and wear rate of the CNT/AlSi10Mg composites were obtained with 1.0wt% CNTs. |
| |
| Keywords: | |
| 本文献已被 SpringerLink 等数据库收录！ |
| 点击此处可从《矿物冶金与材料学报》浏览原始摘要信息 |
|
点击此处可从《矿物冶金与材料学报》下载免费的PDF全文 |
|