Reaction mechanism for in-situ β-SiAlON formation in Fe3Si-Si3N4-Al2O3 composites

In this work, Fe₃Si-Si₃N₄-Al₂O₃ composites were prepared at 1300℃ in an N₂ atmosphere using fused corundum and tabular alumina particles, Al₂O₃ fine powder, and ferrosilicon nitride (Fe₃Si-Si₃N₄) as raw materials and thermosetting phenolic resin as a binder. The effect of ferrosilicon nitride with different concentrations (0wt%, 5wt%, 10wt%, 15wt%, 20wt%, and 25wt%) on the properties of Fe₃Si-Si₃N₄-Al₂O₃ composites was investigated. The results show that the apparent porosity varies between 10.3% and 17.3%, the bulk density varies from 2.94 g/cm3 and 3.30 g/cm3, and the cold crushing strength ranges from 67 MPa to 93 MPa. Under the experimental conditions, ferrosilicon nitride, whose content decreases substantially, is unstable; part of the ferrosilicon nitride is converted into Fe₂C, whereas the remainder is retained, eventually forming the ferrosilicon alloy. Thermodynamic assessment of the Si₅AlON₇ indicated that the ferrosilicon alloy accelerated the reactions between Si₃N₄ and α-Al₂O₃ fine powder and that Si in the ferrosilicon alloy was nitrided directly, forming β-SiAlON simultaneously. In addition, fused corundum did not react directly with Si₃N₄ because of its low reactivity.