| Cu-Zn-Al-Ni合金的组织与性能 |
| |
| 引用本文： | 温燕宁,肖来荣,张喜民,李威,郑英鹏,耿占吉.Cu-Zn-Al-Ni合金的组织与性能[J].中南大学学报(自然科学版),2011,42(4). |
| |
| 作者姓名： | 温燕宁 肖来荣 张喜民 李威 郑英鹏 耿占吉 |
| |
| 作者单位： | 1. 中南大学材料科学与工程学院,湖南长沙,410083;中南大学有色金属材料科学与工程教育部重点实验室,湖南长沙,410083
2. 中南大学材料科学与工程学院,湖南长沙,410083 |
| |
| 基金项目： | 国家"十一五"支撑计划项目 |
| |
| 摘 要： | 采用熔铸和轧制的方法,在Cu-Zn-Al铝黄铜中添加Ni及自制晶粒细化剂,制备出一种新型弹性合金,通过扫描电子显微镜(SEM)和光学显微镜(OM)等对Cu-Zn-A1-Ni铝黄铜的微观组织进行观察、分析,并对其抗拉强度、延伸率、弹性模量等相关参数进行研究.研究结果表明:在合金铸态组织中,Ni,Al和Ti以三元金属间化合物形式主要分布在晶界上,在轧制过程中阻碍基体变形和晶界移动,从而提高合金强度:在均匀化退火过程中,合金中出现层片状A13Ni相,弥散分布在基体内,在冷轧加工后转变为颗粒状;合金再结晶开始温度为350℃,低于再结晶温度退火时,冷轧态合金存在低温退火硬化效应,于250℃退火,硬度达到峰值;冷轧态板材最终退火后,其抗拉强度为731 MPa,延伸率为15%,弹性模量为120 GPa.
|
| 关 键 词： | Cu-Zn-A1-Ni铝黄铜 Ni 显微组织 性能 |
Microstructures and properties of Cu-Zn-Al-Ni alloy |
| |
| WEN Yan-ning,XIAO Lai-rong,ZHANG Xi-min,LI Wei,ZHENG Ying-peng,ENG Zhan-ji.Microstructures and properties of Cu-Zn-Al-Ni alloy[J].Journal of Central South University:Science and Technology,2011,42(4). |
| |
| Authors: | WEN Yan-ning XIAO Lai-rong ZHANG Xi-min LI Wei ZHENG Ying-peng ENG Zhan-ji |
| |
| Institution: | WEN Yan-ning1,2,XIAO Lai-rong1,ZHANG Xi-min1,LI Wei1,ZHENG Ying-peng1,GENG Zhan-ji1 (1.School of Materials Science and Engineering,Central South University,Changsha 410083,China,2.Key Laboratory of Non-Ferrous Metal Materials Science and Engineering,Ministry of Education Central South University,China) |
| |
| Abstract: | A new elastic alloy Cu-Zn-Al aluminum brass containing Ni and grain refiner was produced by casting and rolling.The microstructures of studied alloy were investigated by means of OM and SEM;the tensile strength,hardness and elastic modulus were studied.The results show that Ni and Ti can combine with Al to generate intermetallic compound which mainly distributes on the grain boundaries in as-cast structure.They can improve the mechanical properties of the studied alloy by preventing the deformation of matri... |
| |
| Keywords: | Cu-Zn-Al-Ni aluminum brass nickel microstructure performance |