Microstructural evolution and mechanical behavior of metastable β-type Ti–30Nb–1Mo–4Sn alloy with low modulus and high strength
作者姓名:Shun Guo  Qingkun Meng  Xiaonong Cheng  Xinqing Zhao
摘    要:A metastable P-type Ti-30Nb-lMo-4Sn alloy with ultralow elastic modulus and high strength was fabricated.Under the solution treatment state,the Ti-30Nb-1Mo-4Sn alloy possesses low yield strength of about 130 MPa owing to the presence of the coarse α " martensitic laths.Upon a cold rolling and annealing process,the martensitic transformation from β to α" is significantly retarded due to the inhibitory effect of grain boundaries and dislocations.As a result,the metastable β phase with low total amount of β-stabilizers is retained to room temperature,giving rise to a low modulus of 45 GPa.Meanwhile,nano-sized a precipitates and dislocation tangles play a key role in strengthening the Ti-30Nb-1Mo-4Sn alloy,resulting in a high tensile strength of ~ 1000 MPa.With low elastic modulus and high strength,the metastable P-type Ti-30Nb-1Mo-4Sn alloy could be a potential candidate for biomedical materials.

关 键 词:Metastable  β  Ti  alloy    β  stability    Martensitic  transformation    Low  modulus    High  strength
本文献已被 CNKI 等数据库收录!
点击此处可从《自然科学进展(英文版)》浏览原始摘要信息
点击此处可从《自然科学进展(英文版)》下载免费的PDF全文
设为首页 | 免责声明 | 关于勤云 | 加入收藏

Copyright©北京勤云科技发展有限公司  京ICP备09084417号