| 淬火加热温度对65Mn硬度的影响 |
| |
| 引用本文： | 朱晓东.淬火加热温度对65Mn硬度的影响[J].成都大学学报(自然科学版),2012,31(3):274-275,283. |
| |
| 作者姓名： | 朱晓东 |
| |
| 作者单位： | 成都大学工业制造学院,四川成都,610106 |
| |
| 摘 要： | 对65Mn热处理试样进行不同加热温度的淬火处理,测试其硬度并采用金相显微镜分析其金相组织.结果表明,当加热温度为830℃时,硬度最高,其金相组织为比较细小的回火托氏体.
|
| 关 键 词： | Mn 淬火 硬度 |
Impact of Quenching Temperature on Hardness of 65Mn |
| |
| ZHU Xiaodong.Impact of Quenching Temperature on Hardness of 65Mn[J].Journal of Chengdu University (Natural Science),2012,31(3):274-275,283. |
| |
| Authors: | ZHU Xiaodong |
| |
| Institution: | ZHU Xiaodong (School of Industrial and Manufacturing, Chengdu University, C＇hengdu 610106, China) |
| |
| Abstract: | 65Mn heat treatment samples were quenched at different heating temperatures in order to test their hardness. The metallographic structure of these samples was analyzed by a metallurgical microscope. The results show when the heating temperature of quenching is 830 ~C, their hardness reaches the highest and the metallographic structure is relatively exiguous tempered troostite. |
| |
| Keywords: | 65Mn quenching hardness |