Enhanced mechanical properties of AZ31 magnesium alloy sheets by continuous bending process after V-bending |
|
| Authors: | Tingzhuang Han Guangsheng Huang Yougen Wang Guangang Wang Yanchun Zhao Fusheng Pan |
| Affiliation: | State Key Laboratory of Mechanical Transmission, College of Materials Science and Engineering, Chongqing University, Chongqing 400044 China;State Key Laboratory of Mechanical Transmission, College of Materials Science and Engineering, Chongqing University, Chongqing 400045 China;State Key Laboratory of Mechanical Transmission, College of Materials Science and Engineering, Chongqing University, Chongqing 400046 China;State Key Laboratory of Mechanical Transmission, College of Materials Science and Engineering, Chongqing University, Chongqing 400047 China;State Key Laboratory of Mechanical Transmission, College of Materials Science and Engineering, Chongqing University, Chongqing 400048 China;State Key Laboratory of Mechanical Transmission, College of Materials Science and Engineering, Chongqing University, Chongqing 400049 China |
| Abstract: | The effects of V-bending process, continuous bending process and combination process on the microstructure and mechanical properties and formability of an AZ31 magnesium alloy sheet were investigated. The experimental results showed that no twins were found in the microstructure of all samples after processes due to the fine grain. The V-bending and continuous bending processes were proved to be an effective approach to modify the mechanical properties and formability. While the samples after the combination process exhibited better mechanical properties and formability than the single processed sample. The yield strength significantly decreased with the value of 100 MPa and the fracture elongation enhanced to 18.3% at room temperature. The Erichsen value was 5.0 mm which was significantly increased by 117% compared with as-received sample. The superior formability of combination processed samples was mainly attributed to the smaller r-value and n-value. |
| Keywords: | AZ31 magnesium alloy Continuous bending V-bending Mechanical properties Formability |
| 本文献已被 CNKI 等数据库收录！ | |
| 点击此处可从《自然科学进展(英文版)》浏览原始摘要信息 | |
| 点击此处可从《自然科学进展(英文版)》下载全文 | |