Kinetics of recrystallization for twin-roll casting AZ31 magnesium alloy during homogenization |
| |
Authors: | Hu Zhao Pei-jie Li Liang-ju He |
| |
Affiliation: | (1) EPSRC Centre for Innovative Manufacturing in Liquid Metal Engineering and BCAST, Brunel University, Uxbridge, Middlesex, UB8 3PH, United Kingdom;(2) Corrosion and Protection Centre, School of Materials, University of Manchester, Manchester, M13 9PL, United Kingdom; |
| |
Abstract: | The kinetics of recrystallization for twin-roll casting AZ31 magnesium alloy with different thicknesses during homogenization was analyzed. It is shown that fine grains are first formed at the boundaries of deformed bands in the twin-roll casting slab. The recrystallized grains with no strain are gradually substituted for the deformed microstructure of twin-roll casting AZ31 magnesium alloy. The incubation temperature and time for the recrystallization of a twin-roll casting AZ31 magnesium alloy strip with a thickness of 3 mm are lower and shorter than those of the 6-mm thick strip, respectively. The 3-mm thick twin-roll casting magnesium alloy has finer grains than the 6-mm thick strip. The activation energies of recrystallization for twin-roll casting AZ31 magnesium alloy slabs with the thickness of 3 and 6 mm are 88 and 69 kJ/mol, respectively. The kinetics curves of recrystallization for twin-roll casting AZ31 magnesium alloy were obtained. |
| |
Keywords: | |
本文献已被 SpringerLink 等数据库收录! |
| 点击此处可从《矿物冶金与材料学报》浏览原始摘要信息 |
|
点击此处可从《矿物冶金与材料学报》下载免费的PDF全文 |
|