水包水CPAM乳液的制备和结构形态表征 |
| |
引用本文: | 周细濠,黄佩坚,许家友,林培洪,陈国牛.水包水CPAM乳液的制备和结构形态表征[J].广州大学学报(自然科学版),2011,10(6):34-37. |
| |
作者姓名: | 周细濠 黄佩坚 许家友 林培洪 陈国牛 |
| |
作者单位: | 1. 广州大学化学化工学院,广东广州,510006 2. 广东恒业精细化工有限公司,广东顺德,528325 |
| |
摘 要: | 研究通过分散聚合法制备水包水聚丙烯酰胺乳液(CPAM),结果表明,引发剂、单体和分散剂用量分别为0.05%、7.50%和1.25%时能得到较高特性粘度η]的乳液;用IR、^1H—NMR和光学显微镜对CPAM的结构和形态进行表征.结果表明:聚合得到的聚合物为单体丙烯酰胺(AM)和甲基丙烯酰氧乙基三甲基氯化铵(DMC)的...
|
关 键 词: | 聚丙烯酰胺 分散聚合法 水包水 分散剂 乳液 |
Study on structure and morphology of water-in-water polyacrylamide emulsion |
| |
Abstract: | Water in water polyacrylamide emulsion (CPAM) was prepared by dispersion polymerization. The dosage to get higher characteristic viscosity η] emulsion is that the initiator, monomer and dispersant are 0.05% , 7.50% and 1.25% respeetively. The structure and morphology of CPAM were characterized by IR, 1^H-NMR and optieal microscopy. The results showed that eopolymer is polymeried by AM and DMC, CPAM was dispersed in the emulsion in the shade of sphere. |
| |
Keywords: | polyacrylamide dispersion polymerization water-in-water dispersant emulsion |