| Pb-Zn多孔电极电还原顺丁烯二酸 |
| |
| 引用本文： | 王森林,李彩彩. Pb-Zn多孔电极电还原顺丁烯二酸[J]. 华侨大学学报(自然科学版), 2012, 33(3): 280-284 |
| |
| 作者姓名： | 王森林 李彩彩 |
| |
| 作者单位： | 华侨大学材料科学与工程学院,福建厦门,361021 |
| |
| 摘 要： | 在甲磺酸镀液中电沉积Pb-Zn镀层,采用体积分数为10%的H2SO4腐蚀镀层使锌溶出,得到Pb-Zn多孔电极.通过线性扫描伏安法和恒电位阶跃实验分析多孔Pb-Zn电极的电化学性质,表明电极对顺丁烯二酸电还原合成丁二酸具有较好的电催化活性.研究无膜电合成丁二酸,探讨硫酸浓度、电流密度、初始顺丁烯二酸浓度、温度对电流效率的影响,得到合适的阴极电解条件,即在硫酸浓度为1.0mol·L-1,初始顺丁烯二酸浓度为1.0～1.5mol·L-1,电流密度为100mA·cm-2,反应温度为50～60℃时,电流效率超过88%.
|
| 关 键 词： | Pb-Zn多孔电极 顺丁烯二酸 丁二酸 电还原 |
Electrocatalytic Reduction of Butanedioic Acid on the Porous Pb-Zn Electrode |
| |
| WANG Sen-lin , LI Cai-cai. Electrocatalytic Reduction of Butanedioic Acid on the Porous Pb-Zn Electrode[J]. Journal of Huaqiao University(Natural Science), 2012, 33(3): 280-284 |
| |
| Authors: | WANG Sen-lin LI Cai-cai |
| |
| Affiliation: | (College of Materials Science and Engineering,Huaqiao University,Xiamen 361021,China) |
| |
| Abstract: | The Pb-Zn coating was electro-plated from methyisulfonic acid bath.Then,the coating was corroded by volume fraction 10% H2SO4 solution to dissolve zinc.Thus,the Pb-Zn porous electrode was prepared.Electrochemical performance of the Pb-Zn porous electrode was investigated by linear sweep voltammetry and constant potential step experiments.The obtained results show that the Pb-Zn porous electrode has an excellent electrocatalytic activity for reduction of cis-butenedioic acid to succinic acid.The electrochemical synthesis of succinic-acid technique with non-membrane cell was studied.The influence of sulphuric acid concentration,current density,initial cis-butenedicic concentration and temperature to current efficiency were discussed and the available eletrolysis conditions were obtained.The current efficiency is over 88% under the condition of 1.0 mol·L-1 H2SO4 solution,1.0~1.5 mol·L-1 cis-butenedioic acid,temperature 50~60 ℃ and the cathodic current density 100 mA·cm-2. |
| |
| Keywords: | Pb-Zn porous electrode cis-butenedioic acid succinic acid electro-reduction |