18wt%Cr–8wt%Ni不锈钢中增塑性MnO–Al2O3–SiO2基非金属夹杂物的演变及其浸泡性能 |
| |
引用本文: | Jing Guo,Xing-run Chen,Shao-wei Han,Yan Yan,Han-jie Guo. 18wt%Cr–8wt%Ni不锈钢中增塑性MnO–Al2O3–SiO2基非金属夹杂物的演变及其浸泡性能[J]. 矿物冶金与材料学报, 2020, 27(3): 328-339. DOI: 10.1007/s12613-019-1945-z |
| |
作者姓名: | Jing Guo Xing-run Chen Shao-wei Han Yan Yan Han-jie Guo |
| |
作者单位: | 1)School of Metallurgical and Ecological Engineering, University of Science and Technology Beijing, Beijing 100083, China |
| |
基金项目: | financially supported by the National Science Foundation for Young Scientists of China(No.5170402);the China Postdoctoral Fund(No.2018M630071);the Fundamental Research Funds for the Central Universities(No.RF-TP-19-030A2);the Joint Funds of the National Natural Science Foundation of China(No.U1560203) |
| |
摘 要: | The properties of MnO–Al2O3–SiO2-based plasticized inclusion are likely to change during soaking process due to its low melting point. In this study, the evolution of the MnO–Al2O3–SiO2-based inclusion of 18wt%Cr?8wt%Ni stainless steel under isothermal soaking process at 1250°C for different times was investigated by laboratory-scale experiments and thermodynamic analysis. The results showed that the inclusion population density increased at the first stage and then decreased while their average size first decreased and then increased. In addition, almost no Cr2O3-concentrated regions existed within the inclusion before soaking, but more and more Cr2O3 precipitates were formed during soaking. Furthermore, the plasticity of the inclusion deteriorated due to a decrease in the amount of liquid phase and an increase in the high-melting-point-phase MnO–Cr2O3 spinel after the soaking process. In-situ observations by high-temperature confocal laser scanning microscopy (CLSM) confirmed that liquid phases were produced in the inclusions and the inclusions grew rather quickly during the soaking process. Both the experimental results and thermodynamic analysis conclude that there are three routes for inclusion evolution during the soaking process. In particular, Ostwald ripening plays an important role in the inclusion evolution, i.e., MnO–Al2O3–SiO2-based inclusions grow by absorbing the newly precipitated smaller-size MnO–Cr2O3 inclusions.
|
关 键 词: | ; ; ; |
Evolution of plasticized MnO–Al2O3–SiO2-based nonmetallic inclusion in 18wt%Cr-8wt% Ni stainless steel and its properties during soaking process |
| |
Abstract: | The properties of MnO–Al2O3–SiO2-based plasticized inclusion are likely to change during soaking process due to its low melting point. In this study, the evolution of the MnO–Al2O3–SiO2-based inclusion of 18 wt%Cr-8 wt%Ni stainless steel under isothermal soaking process at 1250°C for different times was investigated by laboratory-scale experiments and thermodynamic analysis. The results showed that the inclusion population density increased at the first stage and then decreased while their average size first decreased and then increased. In addition, almost no Cr2O3-concentrated regions existed within the inclusion before soaking, but more and more Cr2O3 precipitates were formed during soaking. Furthermore, the plasticity of the inclusion deteriorated due to a decrease in the amount of liquid phase and an increase in the high-melting-pointphase MnO–Cr2O3 spinel after the soaking process. In-situ observations by high-temperature confocal laser scanning microscopy(CLSM) confirmed that liquid phases were produced in the inclusions and the inclusions grew rather quickly during the soaking process. Both the experimental results and thermodynamic analysis conclude that there are three routes for inclusion evolution during the soaking process. In particular, Ostwald ripening plays an important role in the inclusion evolution, i.e., MnO–Al2O3–SiO2-based inclusions grow by absorbing the newly precipitated smaller-size MnO–Cr2O3 inclusions. |
| |
Keywords: | nonmetallic inclusion soaking process Ostwald ripening stainless steel |