| 再碳化后再碱化钢筋混凝土（水泥砂浆）的电化学研究 | |
| 引用本文： | 王昆,屈文俊,张俊喜,鲁进亮. 再碳化后再碱化钢筋混凝土（水泥砂浆）的电化学研究[J]. 同济大学学报(自然科学版), 2012, 40(7): 1058-1063 |
| 作者姓名： | 王昆 屈文俊 张俊喜 鲁进亮 |
| 作者单位： | 1. 同济大学土木工程学院,上海200092;江苏科技大学土木与建筑工程学院,江苏镇江212003 2. 同济大学土木工程学院,上海,200092 3. 上海电力学院能源与环境工程学院,上海,200090 4. 浙江工业大学建筑工程学院,浙江杭州,310014 |
| 基金项目： | 国家自然科学基金，“十一五”国家科技支撑计划，国家“九七三”重点基础研究发展计划 |
| 摘 要： | 为模拟再碱化钢筋混凝土结构的耐久性,对再碱化后的钢筋-砂浆试件进行加速碳化试验,碳化的时间采用试件进行再碱化前第1次碳化所用的时间.采用交流阻抗谱、极化曲线和pH测试等测试方法研究再碳化过程中钢筋电化学和水泥砂浆碱性的变化.试验结果表明:在本试验条件下,再碳化后试件的pH值仍然大于10.00;再碳化后钢筋的腐蚀电流虽然有所增大,但仍小于再碱化前的腐蚀电流密度,钢筋的腐蚀电位负移,但仍大于再碱化前的腐蚀电位.研究结果表明:再碱化后的混凝土结构对CO2具有较好的抵抗侵蚀的作用. |
| 关 键 词： | 再碱化 再碳化 砂浆 钢筋锈蚀 |
| 收稿时间： | 2011-05-09 |
| 修稿时间： | 2012-05-07 |
The electrochemical study of realkalisated reinforced concrete (cement mortar) after re-carbonation |
|
| WANG Kun , Qu Wenjun , ZHANG Junxi , LI Peihao. The electrochemical study of realkalisated reinforced concrete (cement mortar) after re-carbonation[J]. Journal of Tongji University(Natural Science), 2012, 40(7): 1058-1063 | |
| Authors: | WANG Kun Qu Wenjun ZHANG Junxi LI Peihao |
| Affiliation: | 1.College of Civil Engineering,Tongji University,Shanghai 200092,China;2.School of Civil Engineering and Architecture,Jiangsu University of Science and Technology,Zhenjiang 212003,China;3.Institute of Engergy and Enviroment Engineering,Shanghai University of Electric Power,Shanghai 200090,China;4.College of Civil Engineering and Architecture,Zhejiang University of Technology,Hangzhou 310014,China) |
| Abstract: | A re carbonation test of re alkalized steel mortar was carried out for the simulation on the durability of realkalisated reinforced concrete. The re carbonation time was the same as the first carbonation time before re alkalisation. The electrochemistry of steel and the alkaline of the cement mortar was studied with electrochemical impedance spectroscopy (EIS), polarization curve and the measurement of pH. The test results show that under the experimental conditions, the pH of cement mortar is above 10.00 after re carbonation; after re carbonation, the corrosion current density of steel increases, which is less than that before re alkalisation; the corrosion potential of steel decreases, which is more than that before re alkalisation. |
| Keywords: | re alkalisation re carbonation mortar steel corrosion |