| 轻烧粉-氢氧化钠法制备氢氧化镁的研究 |
| |
| 引用本文： | 赵 华,陈向民,杜振雷,纪俊荣,崔文豪,胡永琪,刘润静,刘宝树,胡庆福. 轻烧粉-氢氧化钠法制备氢氧化镁的研究[J]. 河北科技大学学报, 2009, 30(3): 253-256,270 |
| |
| 作者姓名： | 赵 华 陈向民 杜振雷 纪俊荣 崔文豪 胡永琪 刘润静 刘宝树 胡庆福 |
| |
| 作者单位： | 河北科技大学化学与制药工程学院,河北石家庄,050018;河北科技大学研究生学院,河北石家庄,050018;河北科技大学河北省分析测试研究中心,河北石家庄,050018;河北科技大学化学与制药工程学院,河北石家庄,050018;中国无机盐工业协会钙镁盐分会,河北石家庄,050018 |
| |
| 摘 要： | 以轻烧粉经酸化、氧化除铁等精制过程得到的氯化镁溶液为原料,以氢氧化钠为沉淀剂制备氢氧化镁。研究了pH值对轻烧粉酸化除铁的影响,考察了原料的物质的量比、反应温度、加料时间、陈化时间等因素对产品质量的影响,得到了轻烧粉精制和反应制备氢氧化镁的最佳工艺条件。采用扫描电子显微镜（SEM）、X射线粉末衍射仪（XRD）和激光粒度分布测试仪等对实验产品进行表征。结果表明,该工艺制备的氢氧化镁纯度达到98%以上,CaO质量分数低于0.1%,颗粒呈片状结构,粒度分布均匀,形貌规则。
|
| 关 键 词： | 氢氧化镁 轻烧粉 氢氧化钠 |
| 收稿时间： | 2009-03-27 |
| 修稿时间： | 2009-04-28 |
Preparation of magnesium hydroxide with light calcined powder and sodium hydroxide |
| |
| ZHAO Hu,CHEN Xiang-min,DU Zhen-lei,JI Jun-rong,CUI Wen-hao,HU Yong-qi,LIU Run-jing,LIU Bao-shu and HU Qing-fu. Preparation of magnesium hydroxide with light calcined powder and sodium hydroxide[J]. Journal of Hebei University of Science and Technology, 2009, 30(3): 253-256,270 |
| |
| Authors: | ZHAO Hu CHEN Xiang-min DU Zhen-lei JI Jun-rong CUI Wen-hao HU Yong-qi LIU Run-jing LIU Bao-shu HU Qing-fu |
| |
| Affiliation: | ZHAO Hua ,CHEN Xiang min ,DU Zhen-lei ,JI Jun-rong ,CUI Wen-hao, HU Yong-qi, LIU Run-jing ,LIU Bao-shu, HU Qing-fu (1. College of Chemical and Pharmaceutical Engineering, Hebei University of Science and Technology, Shijiazhuang Hebei 050018, China ; 2. College of Graduate, Hebei University of Science and Technology, Shijiazhuang Hebei 050018, China ; 3. Hebei Research Centre of Analysis and Testing, Hebei University of Science and Technology, Shijiazhuang Hebei 050018, China; 4. Branch of Calcium and Magnesium Salt,China Inorganic Salt Industry Association, Shijiazhuang Hebei 050018, China) |
| |
| Abstract: | Magnesium hydroxide was prepared with sodium hydroxide as precipitant and magnesium chloride as raw material.Magnesium chloride was prepared through light calcined powder acidified by hydrochloride acid.The influence of pH value on the content of Fe in magnesium chloride was investigated;the effects of the ratio of raw materials,reaction temperature,feeding time and aging time on the purity of magnesium hydroxide were studied.And optimal operation conditions were obtained.The product was characterized by sc... |
| |
| Keywords: | magnesium hydroxide light calcined powder sodium hydroxide |