| 钒钛磁铁精矿的预氧化研究 |
| |
| 引用本文： | 陈德胜,王丽娜,齐涛,宋波.钒钛磁铁精矿的预氧化研究[J].湖南科技大学学报(自然科学版),2011(3). |
| |
| 作者姓名： | 陈德胜 王丽娜 齐涛 宋波 |
| |
| 作者单位： | 北京科技大学冶金与生态工程学院;湿法冶金清洁生产技术国家工程实验室;中国科学院过程工程研究所绿色过程与工程院重点实验室; |
| |
| 基金项目： | 中国科学院知识创新工程重要方向项目(KGCX2-YW-214); 国家自然科学基金资助项目(51004091,51090380,21006115); 国家重点基础研究发展计划(973计划)(2007CB613501) |
| |
| 摘 要： | 研究了钒钛磁铁精矿在等温预氧化条件下的物相组成及其转变情况,并将钒钛磁铁精矿原矿和预氧化后的样品以煤粉为还原剂进行直接还原,利用XRD和ICP-AES对产物进行物相和成份分析.研究结果表明:预氧化能够加速还原过程,提高金属化率,较为适宜的预氧化条件为:预氧化温度为900℃,预氧化时间为30 min;预氧化矿在1 200℃下还原60 min,比钒钛磁铁精矿原矿金属化率提高了14.0%.其强化还原的机理是:在预氧化过程中Fe3O4被氧化成Fe2O3,FeTiO3被氧化成Fe2O3.FeTiO3固溶体、Fe2O3和TiO2,破坏了钒钛磁铁精矿的结构,矿粉内部形成了大量孔隙,改善了还原反应的动力学条件,加速了还原过程.
|
| 关 键 词： | 钒钛磁铁精矿 预氧化 还原机理 |
Study on preoxidation of vanadium-bearing titanomagnetite concentrates |
| |
| CHEN De-sheng,,WANG Li-na,QI Tao,SONG Bo.Study on preoxidation of vanadium-bearing titanomagnetite concentrates[J].Journal of Hunan University of Science & Technology(Natural Science Editon),2011(3). |
| |
| Authors: | CHEN De-sheng WANG Li-na QI Tao SONG Bo |
| |
| Institution: | CHEN De-sheng1,2,3,WANG Li-na2,QI Tao2,SONG Bo1(1.School of Metallurgical and Ecological Engineering,University of Science and Technology Beijing,Beijing 100083,China,2.National Engineering Laboratory for Hydrometallurgical Cleaner Production Technology,Beijing 100190,3.Key Laboratory of Green Process and Engineering,Institute of Process Engineering,Chinese Academy of Sciences,China) |
| |
| Abstract: | The isothermal preoxidation of vanadium-bearing titanomagnetite concentrates was performed in present investigation.The corresponding phase composition and transformation of the preoxidized samples were investigated.With the pulverized coal as a reductant,the vanadium-bearing titanomagnetite concentrates and preoxidized samples were reduced.XRD and ICP-AES techniques were employed to identify the main phases and chemical composition of the samples.The results showed that preoxidation accelerate the reductio... |
| |
| Keywords: | vanadium-bearing titanomagnetite concentrates preoxidation reduction mechanism |