Effect of heat treatment on microstructures and properties of a novel Al-Zn-Mg-Cu alloy for oil drilling

In view of the special requirements for strength, heat resistance and corrosion resistance of Al-Zn-Mg-Cu alloy for oil drilling, the Al-6.2 Zn-2.5 Mg-1.6 Cu alloy was prepared by increasing Cu content on basis of Russian Series 1953 alloy. The effect of heat treatment on the microstructures and properties of the alloy was characterized by optical microscope(OM), scanning electron microscope(SEM) and transmission electron microscope(TEM), and investigated by tensile test at room temperature, thermal exposure test and corrosion test. The results show that the strength after T6 aging treatment exhibit a decrease trend as an increase of the solution temperature from465 °C to 480 °C. After the solution treated by the rate of 470 °C/1 h, second phases dissolve into the matrix very well and the strength property reaches optimum. The alloy has better comprehensive properties treated by a solution treatment of 470 °C/1 h and then followed by an aging treatment of 120 °C/24 h + 170 °C/1 h + 120 °C/24 h. Under the aging state, the precipitated phases inside the grains are suitable in size, while on the grain boundary distribute discontinuously and the precipitate-free zone is obvious. Besides, the alloy still maintain high tensile properties. The yield strength, tensile strength and elongation are 650 MPa, 686 MPa,12.0%, respectively. The yield strength retention after heat exposure is 92%. The alloy has good corrosion resistance and the exfoliation corrosion degree. The average corrosion rate in the H_2S and CO_2 environment is 0.0024 mm/a, which is far less than the required 0.12 mm/a. It is insensitive to H_2S and CO_2 environments.     

基于修正斜压场的RC框架边节点剪切性能分析

为研究钢筋屈服强度和混凝土抗压强度对钢筋混凝土(RC)框架边节点剪切性能的影响规律,基于修正斜压场理论(MCFT),对某框架边节点的剪切应力-应变骨架曲线进行数值模拟,并与试验结果进行对比.在验证MCFT算法的精度后,研究钢筋屈服强度和混凝土抗压强度两个参数变化对RC框架边节点剪切应力-应变骨架曲线和峰值剪切应力的影响规律.结果表明:基于MCFT可以较好地模拟RC框架边节点的剪切应力-应变关系曲线; RC框架边节点的峰值剪切应力对混凝土抗压强度的变化更为敏感,但当试件的钢筋(HRB400)屈服应力下降幅度超过16.45%时,对钢筋屈服应力的变化更为敏感;当试件的钢筋(HRB400)屈服应力下降幅度超过10%时,节点发生钢筋滑移破坏,此时峰值剪切应力会大幅下降.     

三维打印器件后处理液研究

分析了不同的填充强化剂(后处理A液)、不同的后处理B液基料、后处理B液中水性环氧乳液的掺量及后处理液浸泡时间对石膏基打印器件耐水性、抗压强度、尺寸偏差、表面微观结构的影响.结果表明:经纳米硅超硬固化剂处理后的打印器件抗压强度大幅提高,纳米硅超硬固化剂最适宜作为后处理A液;水性聚氨酯乳液PU-202B最适宜作为后处理B液的基料;后处理B液中加入水性环氧乳液,处理后打印器件的抗压强度增加、吸水率降低,但水性环氧乳液含量增加到一定程度后会出现尺寸偏差;后处理A、B液最佳浸泡时间分别为130 s和35 s;先浸泡后处理A液、后浸泡后处理B液的打印器件具有抗压强度高、吸水率小、表面较光滑、不脱粉等优良性能.     

运用试验设计法优化某军品压铸弹尾工艺

根据某军品部件出现的问题，应用试验设计法成功地找出了最优组合，提高了该部件的强度，解决了该强度问题，使生产得以正常进行。     

智能高速罐身电阻焊机数字化控制系统

提出了以国产MCT80 0 0F8运动控制器为核心的智能高速罐身电阻焊机数字化控制系统 ,并介绍了系统的组成、工作原理、硬件接口、电机控制方法以及伺服电机的运动关系数学模型 .新的系统有利于提高罐身电阻焊机的制罐生产速度 ,并具有功能全面、可靠性高、控制精确、开放性好以及成本较低等优点     

NIPA类共聚温敏水凝胶中水的状态和耐热性

用N-异丙基丙烯酰胺（NIPA）与丙烯酸钠（SA）及甲基丙烯酸钠（SMA）共聚合成了两个系列的水凝胶，研究了共聚组成与水凝胶基本性质的关系，并用示差扫描量热法（DSC）和热失重法（TG）研究了此类水凝胶中水的状态和耐热性。     

关于水泥砂浆墙面起砂问题的防治

分析了水泥砂浆墙面起砂的原因，并提出了预防措施和处理办法。     

电磁场中带电粒子束运动的力学模拟

研究以不同初速度进入互相垂直的匀强磁场和均强电场中的带电粒子束的运动情形，并同相似的力学运动相比拟，建立了直观的力学模型。     

钢纤维混凝土桥面铺装试验研究与工程应用

针对桥面铺装层的受力状况和破坏原因 ,重点对钢纤维砼材料进行了抗弯强度试验和耐磨损试验 ,并进行了钢纤维砼弯曲性能分析 ,闸述了钢纤维砼的耐磨机理 ;结合 130 76m2 的实际工程应用 ,进行了钢纤维砼桥面铺装施工技术总结 ,分析了采用钢纤维砼作为桥面铺装层所带来的效益 ,可供类似工程参考应用     

关于差分式放大器输入电阻的研究

差分式放大器在实际应用方面非常广泛,其理论分析方法的深入研究,对生产实践和教学都有重要的意义。采用电路理论分析、差放理论分析、“虚短”理论分析及实验的方法对差分式放大电路进行了研究。