双层钙钛矿Sr2FeMoO6，Ba2FeMoO6的电磁性质研究

分析了双层钙钛矿结构的锰氧化合物Sr2FeMoO6,Ba2FeMoO6物相结构和电磁学性质,对巨磁阻效应进行了探讨,揭示了Sr2FeMoO6样品为半导体导电性,Ba2FeMoO6样品为金属导电性.     

双金属氧化物和氧化物载体组分间的相互作用

讨论了一些过渡金属氧化物（NiO,CuO或MoO3)在经改性所得复合载体（TiO2-γ-Al2O3，MoO3-t-ZrO2或NiO-t-ZrO2)上的分散作用，这些三地体系中实验测定的氧化物分散容量与研究负载型二元氧化物体系所得嵌入模型的估算值基本相符；样品的表面组成、结构和性能与载体的表面结构、过渡金属氧化物的负载量和加料顺序以及焙烧温度密切相关。     

Nitric oxide suppresses stomatal opening by inhibiting inward-rectifying K_(in)~ channels in Arabidopsis guard cells

We explore nitric oxide (NO) effect on K in channels in Arabidopsis guard cells. We observed NO inhib- ited K in currents when Ca2 chelator EGTA (Ethylene glycol-bis(2-aminoethylether)-N,N,N′,N′-tetraacetic acid) was not added in the pipette solution; K in currents were not sensitive to NO when cytosolic Ca2 was chelated by EGTA. NO inhibited the Arabidopsis stomatal opening, but when EGTA was added in the bath solution, inhibition effect of NO on stomatal opening vanished. Thus, it implies that NO ele- vates cytosolic Ca2 by activating plasma membrane Ca2 channels firstly, then inactivates K in chan- nels, resulting in stomatal opening suppressed subsequently.     

电子束熔化成形与锻造Ti6Al4V合金的腐蚀行为对比研究

本工作采用电化学工作站研究了电子束熔化技术（EBM）成形TC4样品和传统锻造TC4在3.5wt% NaCl溶液中的电化学腐蚀行为. 结果表明EBM成形TC4样品的非平衡微观结构使其与传统锻造的TC4相比,表现出不同的耐腐蚀性. EBM成形TC4样品与锻件TC4相比,EBM成形样品不同平面存在耐蚀性差异,而且EBM水平面大于锻件,EBM垂直面小于锻件. EBM成形TC4样品垂直面出现的腐蚀性能的各向异性主要是β柱状晶导致的. 在腐蚀的过程中,点蚀优先发生在α晶界,因为晶界能量较高,形成多孔的钝化层. 本项工作有助于丰富增材制造制备TC4合金在航空钛合金领域的腐蚀性能研究.     

Nitric oxide-related pancreatic endocrine responses to hyperglycaemia in the conscious calf

Mean plasma insulin concentration was reduced and mean plasma glucose concentration increased following the administration of N-nitro-L-arginine methyl ester (L-NAME; 100 mol kg^–1 i.a.) in conscious calves given continuous infusions of exogenous glucose (30–60 mol min^–1 kg^–1 i.v.). It is concluded that the rise in plasma insulin concentration which occurs in these animals in response to glucose is mediated, at least in part, by a nitric oxide-related factor (NOx).     

对电子束蒸发沉积的ZnO：Al膜电学性能的研究

使用电子束蒸发法沉积了铝掺杂的氧化锌透明导电膜。     

方波脉冲电沉积氧化锌薄膜的研究

以0.1mol·dm-3的Zn(NO3)2水溶液为电解质溶液,以99.9%Zn片作阳极,采用方波脉冲电流法在氧化锡铟(ITO)导电玻璃基底上阴极电沉积,得到了透明的ZnO薄膜.采用X射线衍射分析、扫描电镜和荧光光谱技术,测试了薄膜的结构、表面形貌和光学特性.用同样方法在多孔硅衬底上电沉积ZnO薄膜,经过1000℃氧气氛下热处理1h,在紫外光照射下可发射强绿色荧光.     

H2O2氧化降解壳聚糖的动力学

为制备分子量分布较窄的可溶性低分子量壳聚糖，研究了简单均相体系下双氧水降解壳聚糖的过程与机理，考察了温度、双氧水浓度和时间对降解反应的影响，实验结果显示均相条件下壳聚糖的氧化降解符合无规降解动力学规律．同一降解体系中，同一反应时刻下，水解产物的分子量的倒数与反应温度成正比．     

固体氧化物燃料电池系统零排放新思路研究

提出了固体氧化物燃料电池零排放新思路设计,该设计具有高发电效率、温室气体零排放、回收利用二氧化碳以及使用环境友好的可再生循环二氧化碳吸收材料等优点.此外,还介绍了电池构件材料以及二氧化碳吸收材料的制备,最后测试了材料的二氧化碳吸附性能.结果表明最大体积吸收比可高达993倍,最佳吸收温度为700 ℃,同时可实现在800 ℃以上2 h内将所吸附的二氧化碳完全解析.     

氢对Ti—Al—Zr钛合金管材的组织和性能的影响

分析和试验了Ti -Al -Zr单相α -钛合金管材的化学成分、金相组织和室温机械性能后 ,采用人工吸氢法使该种钛合金材料获得了不同的氢含量。进而 ,测出了其延伸率随氢含量变化的关系曲线 ,从而认识到氢对该材料的塑性指标会造成显著的影响。随后 ,用氢含量为 132× 10 -6、342× 10 -6和 80 8× 10 -6的 3种试样和它们的拉伸断口分别进行了金相和SEM分析。观察到了不同氢含量的样品中氢化物的金相形态及其分布特征 ;由对拉伸断口的分析工作 ,得出氢化物呈薄片状析出的特点 ,而惯析面为α相 (hcp结构 )的基面、近基面和其它易滑移面。最后 ,讨论了氢化物的种类、析出特征 ,并对氢化物在无织构的钛合金管材内的分布特点对其氢损伤的影响程度作了说明