Synthesis and Properties of Novel Copolymers Based on Fluorene and Thiophene

1 Results In this contribution we present the synthesis and characterization of novel copolymers based on fluorene and thiophene (see Scheme 1).They were synthesized by the Pd-catalyzed Suzuki coupling reaction of 9,9-dihexylfluorene-2,7-diboronic acid bis(1,3-propanediol) ester and 3-substituted (R=3-methylbutyl,hexyl,2-(pyren-1-yl)vinyl) 2,5-dibromothiophenes and characterized by GPC,IR and NMR techniques.UV-vis absorption,photoluminescence (PL) and electrochemical behavior of these polymers were also...     

The concentration quenching characteristics of ~5D_3-~7F_J and ~5D_4-~7F_J (J=0―6) transitions of Tb~(3 ) in YBO_3:Tb~(3 ) phosphor

The photoluminescence quenching behaviors of 5D3-7FJ and 5D4-7FJ (J = 0―6) transitions of Tb3 in YBO3:Tb under 130―290 nm excitation were systematically investigated. The results revealed that the quenching concentrations of both 5D3-7FJ and 5D4-7FJ transitions of Tb3 in YBO3:Tb were mainly de-pendent on excitation wavelength. Particularly,the quenching concentrations of 5D4-7FJ transitions of Tb3 under 130―290 nm excitation were correlated with excitation bands of YBO3:Tb. The quenching concentrations of 5D3-7FJ transitions remained at low concentration (2%) under 186―290 nm excitation and then increased gradually with energy of incoming excitation photon when excited at 130―186 nm. This dependence should be involved in their excitation mechanisms and quenching pathway in particular excitation region.     

W_(18)Cr_4V钢真空油淬白亮层、熔化层形成原因的试验研究

W_(18)Cr_4V钢真空加热油淬后,表面出现白亮层和熔化层等异常现象。本文利用金相显微镜,显微硬度计、扫描电子显微镜和电子探针等手段对白亮层和熔化层进行了分析研究。试验表明,白亮层、熔化层均是真空油淬增碳的结果。本文对白亮层、溶化层形成原因进行了比较深入的分析探讨提出了产生白亮层必须同时具备的三个条件。     

多孔硅的形成及可见光发射

多孔硅是晶体硅片在氢氟酸溶液中进行阳极氧化，在硅衬底上形成多孔态的硅材料。本文介绍了多孔硅的形成和结构形貌，对其光学性质和发光机制进行了扼要讨论，并介绍了当前多孔硅研究中的一些热点问题。     

一种含5-硝基间苯二甲酸和菲咯啉配体的超分子化合物：结构表征，光致发光和电化学性能

采用水热法合成了含混合配体的铜配合物[CuClPhen]⁺·[HL]^-·2H₂O（HL=5-硝基间苯二甲酸,Phen=1,10-菲咯啉）,其结构由单晶X射线晶体学确定。标题化合物在三斜空间群P-1的晶体化合物。标题化合物的晶体数据：C₃₂H₂₄ClN₅CuO₈,M_r = 704.54,a = 10.4044(5),b = 12.3912(9),c = 12.4632(9)Å,α = 73.859(6),β = 85.036(5),γ = 78.202(5)^°,V = 1510.09(17) ų,Z = 2, T = 293(2) K,D_c = 1.549 g/cm³,μ(MoKα) = 0.874 mm^-1,F(000) = 720.0,R = 0.0554,wR = 0.1434,GOF = 1.098。当用作超级电容器电极材料时,所制备的配合物具有高比电容、良好的循环稳定性和优良的倍率性能。在1mol/L KOH溶液中,最大比电容可达到69 F/g。在2 A/g电流密度下,10000次循环后比电容保持率为72%。标题化合物是一种潜在的红色光致发光材料。     

瓶盖加工模具的失效分析

对瓶盖加工模具在生产使用中突然出现的裂纹及崩刃等现象进行了分析,指出失效的主要原因是原热处理工艺不当使其硬度偏高所致．鉴于此,本文对其进行了实验研究,并制定了新工艺．     

方波脉冲电沉积氧化锌薄膜的研究

以0.1mol·dm-3的Zn(NO3)2水溶液为电解质溶液,以99.9%Zn片作阳极,采用方波脉冲电流法在氧化锡铟(ITO)导电玻璃基底上阴极电沉积,得到了透明的ZnO薄膜.采用X射线衍射分析、扫描电镜和荧光光谱技术,测试了薄膜的结构、表面形貌和光学特性.用同样方法在多孔硅衬底上电沉积ZnO薄膜,经过1000℃氧气氛下热处理1h,在紫外光照射下可发射强绿色荧光.     

45钢零件淬火过程温度场的ansys模拟

ansys有限元软件在温度场的模拟过程中，很好地结合了材料变温过程材料热物性参数的变化，特别适用于钢件淬火过程温度场的准确计算。通过利用ansys有限元分析软件对几何外形复杂的45钢零件淬火过程温度进行有限元模拟，得到了零件温度随淬火时间的分布关系。模拟结果与实际过程一致，且运算速度较快，适用于淬火液的选取及淬火工艺的优化，并为精确计算淬火过程中的热应力、残余应力做好了准备工作。     

TiAl自蔓延高温合成反应的机理

用燃烧波淬熄法研究了大颗粒Ti粉和Al粉制备TiAl金属间化合物的自蔓延高温合成反应机理.通过电镜观察和能谱分析发现:反应过程可用毛细铺展 界面反应机制解释.熔融的Al在整个反应过程中起着主要作用,首先熔融的Al液通过Ti粉间的毛细管作用以薄膜的形式铺展在Ti粉表面,并在接触面生成TiAl3.反应放出的热量有利于加速反应的进行,促使TiAl3与Ti进一步反应生成TiAl.但是生成的TiAl3层阻碍了Al液与Ti粉的接触,制约了反应的进行.最后,在试样中可以同时看到完全反应的Ti粉和未完全反应的Ti粉.     

动力学荧光猝灭法测定污水中的对硝基酚

建立了动力学荧光法测定对硝基酚的新方法。在盐酸介质中，对硝基酚可以活化钒（V），催化氯酸钾氧化罗丹明6G的反应，使其荧光猝灭。该方法的线性范围为5-50μg/L，检测限为2.5μg/L，回收率为96.5%，可直接用于污水中对硝基酚的测定。