酚醛树脂泡沫材料的填充改性及其性能研究

用氢氧化铝粉末对泡沫酚醛树脂材料进行填充改性,并对其主要性能进行研究．结果表明,填充改性能提高酚醛泡沫材料的抗压强度,其导热系数随温度和密度的升高而增大,泡沫材料在深冷情况下表现出优异的绝热性能．同时对酚醛泡沫材料的燃烧性能进行了考察,其临界氧指数高达４７,在高于１５０℃环境温度中有自燃的危险,１５０℃以下可安全使用．     

电氧化法处理高浓度酚钠废水

为了改善强碱性废水的可生化性,采用电氧化法处理高浓度酚钠废水.结果表明：电氧化法对废水的色度和S（重铬酸钾化学耗氧量）具有良好的去除效果,电解过程中余氯的产生对色度和S的去除有决定性作用.实验确定的高浓度酚钠废水电氧化处理条件是：电流密度为714 A/m^2、电压为10 V、电解时间为30min,采用中和→电氧化→生化工艺去除色度和S.     

鲁米诺-铁氰化钾流动注射化学发光体系研究

采用流动注射-化学发光(FI-CL)联用技术系统研究了19种酚类化合物对鲁米诺-铁氰化钾(lumi-nol-K3Fe(CN)6)体系化学发光的影响,发现其大部分能抑制或增强体系化学发光强度,且抑制或增强化学发光强度的能力与化学发光体系溶液的介质、pH值以及酚类化合物的浓度、分子结构等有关;根据化学发光光谱和紫外-可见吸收谱,讨论了体系化学发光强度抑制或增强的机理,推测抑制或增强可能是由于酚类化合物的氧化反应及瞬时产物影响了鲁米诺化学发光反应通道;若联接分离技术,鲁米诺-铁氰化钾流动注射化学发光体系具有同时测定数个酚类有机化合物的潜力.     

改性酚醛树脂碳化制备玻璃碳的研究

文章探索以一种自制的新型改性酚醛树脂为原料制备玻璃碳的工艺。研究了固化、碳化工艺条件与产品性能的关系。所用改性酚醛树脂具有室温下粘度低,高温固化时小分子易逸出;快速升温固化、碳化后得到的产品气孔较少等特点。     

分级多孔纳米炭纤维的结构及电容性能

以酚醛树脂为碳源、PVP为纺丝助剂、纳米MgO颗粒为模板剂,通过静电纺丝法制得酚醛树脂基纳米炭纤维,经过炭化、KOH活化、酸洗后得到分级多孔纳米炭纤维,利用SEM、XRD、XPS、拉曼光谱仪及氮气吸脱附实验,对所制多孔纳米炭纤维的结构和形貌进行表征,并将其作为模拟电容器的电极,利用循环伏安、恒电流充放电及交流阻抗方法测试了材料的电化学性能。结果表明,KOH活化引入了数量可观的微孔,所得纳米炭纤维表现出明显的"微孔-中孔-大孔"分级孔分布的特点,其比表面积达到1058.4m~2/g,总孔容为1.64cm~3/g。电化学测试结果表明,所制分级多孔纳米炭纤维在6mol/L KOH电解液中显示出优异的电容性能,在0.2A/g的电流密度下,其放电比容量达到198F/g,在20A/g电流密度下,电容保持率达到65%。     

A gas chromatography/mass spectrometry method for the simultaneous analysis of 50 phenols in wastewater using deconvolution technology

Phenolic compounds exist widely in the influents and effluents of sewage treatment plants (STPs) and most are un-regulated. In this study, a gas chromatography-mass spectrometry (GC-MS) method for the simultaneous analysis of 50 phenolic compounds in wastewater was developed. Deconvolution technology was used to identify contaminants that are covered by co-extracted materials. A mass spectral library containing all 50 silylated phenolic compounds was first established and used for deconvolution. Twelve typical phenolic compounds were selected to optimize the sample preparation procedures. Solid-phase extraction using a C18 cartridge coupled with an HLB cartridge was used for pre-concentration and dichloromethane was used for elution. The solutes were derivatized and analyzed by GC-MS. The blank and matrix spike recoveries ranged from 57.46% to 136.4% and 47.87% to 114.8%, respectively. Method detection limits ranged from 3.64 to 97.64 ng L⁻¹. The relative standard deviations of all the recovery experiments were lower than 13.6%. The instrument limits of quantification ranged from 0.7 to 87.7 pg. The method has been applied to analyze the influents and effluents of 5 Chinese STPs. Except for regulated phenolic compounds (phenol and 2,4,6-trichlorophenol), three un-regulated phenolic compounds, including 2-chlorophenol, 2,5-dichlorophenol and 2,4-dichloro-3-ethyl-6-nitrophenol were identified in the effluent wastewater. The detected concentrations of un-regulated phenolic compounds could possibly cause environmental effects, indicating that immediate attention is required to prevent complications.     

桐油改性酚醛树脂的制备及其性能

利用桐油改性酚醛树脂(PF),制备高性能摩阻材料用树脂基体.综合热分析表明改性PF在100～320 ℃间失重7.30%, 320～600 ℃间失重61.10%,普通PF分别失重15.94%和73.51%;普通PF热分解峰为400～425 ℃和540～600 ℃,桐油改性PF热分解峰为400～450 ℃和560～600 ℃.桐油改性PF热稳定性能得到很大提高,但耐热性能未有明显改善.FTIR分析表明桐油成为聚合物结构的一部分;力学测试结果表明桐油改性较大程度地改善了PF的韧性;掺杂质量分数40%的桐油改性PF和60%的硼改性PF的试样综合力学性能较好,更适合作为摩阻材料的树脂基体.     

萜烯酚树脂的研制

研究了马尾松松节油和苯酚反应的规律,选定了较为理想的Lewis酸催化剂体系,获得了最佳工艺条件。用甲苯为溶剂,催化剂量为总原料的4％,松节油和苯酚的摩尔比控制在1:0.5～1:0.7的范围内,在25～50℃下进行Friedel-Craft's反应,经水洗、蒸馏等工序,可得加特纳色阶为7～9的淡黄色树脂,其得率在90％以上(以总反应物料重量计),软化点达115℃以上。本研究得到的萜烯酚树脂经应用试验表明,在橡胶、保护膜胶带等工业中可提供特有的性能,具国外同类产品水平。并为实现萜烯酚树脂工业生产提供了可靠依据。     

胜利黄岛原油深度电脱盐的研究：Ⅰ.破乳剂组成的影响

根据胜利黄岛原油的性质，在筛选了几十种破乳剂的基础上，选择了酚醛树脂和环氧环烷，环氧乙烷的嵌段共聚物作破乳剂，探讨了破乳剂组成对原油脱水，脱盐以及界面张力的影响，通过静态脱盐，脱水试验，得到了适合黄岛原油的最佳破乳剂组成。     

无石棉摩阻材料的研究——Ⅰ.玻璃纤维增强摩阻材料

本文选用热分解温度为461℃,700℃时残留物为63%的硼改性酚醛(P树脂)与丁腈橡胶共混后作为基体,以玻璃纤维作增强剂。对该体系制成的摩阻材料进行了配方、制备工艺及复合机理等较系统的研究。结果表明,在33%基体含量中,丁腈橡胶占4～7%时具有良好的增韧性及其它综合性能。含21%玻璃纤维的无石棉摩阻材料离合器片,其性能已符合国家标准,可以进行扩大生产。