稀土在催化中的应用研究进展

稀土在催化中的研究和应用重要而广泛.文章分别从稀土氧化物、稀土金属间化合物及稀土分子筛3个方面对稀土在催化中的应用研究做了综述,并简要地分析了稀土催化剂的发展方向.     

Preparation of three-dimensionally ordered macroporous perovskite materials

In this paper,we use La0.8Sr0.2MnO3 and La0.7Ca0.2Sr0.1MnO3 as examples to demonstrate a preparation method for threedimensionally ordered macroporous(3DOM) perovskite thermochromic materials.Polystyrene spheres with an average diameter of 220 nm were self-assembled into a three-dimensionally ordered colloidal crystal template.A mixed metal nitrate solution prepared using La(NO3) 3·6H2O,Ca(NO3) 2·4H2O,Sr(NO3) 2,Mn(CH3COO) 2·4H2O and an ethanol precursor was used to fill the interstitial voids of the polystyrene colloidal crystal templates.3DOM La0.8Sr0.2MnO3 and La0.7Ca0.2Sr0.1MnO3 materials were then obtained after the sphere templates were removed via drying and calcination.The results show that the framework of the 3DOM materials can have different thicknesses and pore shrinkage rates by varying the filling times.In addition,the Curie temperatures of the 3DOM and bulk La0.8Sr0.2MnO3 materials can be varied by altering the preparation method.     

四氯合金属(Ⅱ)酸双烷基铵的合成、结构和相变研究 I.(n-C_(12)H_(25)NH_3)_2MCI_4(M=Zn、Cu)

合成了二维片层化合物(n-C_(12)H_(25)NH_3)_2MCl_4(M=Zn、Cu),并且用元素分析和富里叶变换红外光谱对其进行了表征、用热分析法确定了它们的分解温度、相变温度和相变焓。     

数据科学范式下的钙钛矿结构铁电新材料研究

 材料基因组计划倡导预测式新材料研发理念，推进高通量数据生产和利用技术，关注材料全生命周期价值。因此，材料基因组计划的执行需要在材料科学系统工程的框架下，集成统一计算、实验和理论等研究方法，以数据科学新范式为牵引、协同运用实验观测、理论建模和计算仿真研究范式，最终建立相关材料体系的性能与材料基因（原子系统的组成与结构）、工艺参数与使役条件之间的量化关系和数据库，实现新材料的按需设计和应用。本文在简单探讨科学研究范式、材料基因组计划和材料科学系统工程基本概念和方法的基础上，以钙钛矿结构氧化物铁电压电材料研究为例，探讨了数据科学范式下的新材料研究实践。结果表明，数据挖掘驱动的新材料设计确实可以降低探索时间和实验任务，加快新材料的发现和应用进程。     

双钙钛矿型Ba2YSbO6的水热合成和结构表征

报道了温和条件下双钙钛矿型复合氧化物Ba2YSbO6的水热合成,并通过XRD、IR、ICP、XPS对产物物相、组成、结构、锑离子价态等进行了表征.Ba2YSbO6产物为立方钙钛矿结构,属于Fm3m空间群,晶胞参数为a=0.840955(7)nm,V=0.594727(8)nm3,Y和Sb呈岩盐型有序排列,锑为 5价.     

钙钛矿型催化剂La_(0.7)K_(0.3)CoO_3催化合成甲基二氯化膦

研究了以钙钛矿型催化剂La0.7K0.3CoO3为催化剂,以甲烷和三氯化磷为原料合成甲基二氯化膦的反应,考察了影响反应的几种因素.结果表明,反应物n(CH4):n(PCl3)=5:1,反应温度300℃,催化剂粒径425～850μm为较适宜的反应条件.     

钙钛矿锰氧化物Nd_(0.5)Sr_(0.3)Ba_(0.2)MnO_3多晶的磁性和相分离

通过固相反应法合成Nd0.5Sr0.3Ba0.2MnO3多晶样品,采用粉末X射线衍射(XRD)、超导量子磁强计(SQUID)和电子自旋共振谱仪(ESR),对样品的结构和磁性进行了研究.XRD检测结果表明,样品为单相,空间群为Pbnm.磁性测量和ESR结果表明,在降温过程中,样品经历了铁磁有序转变(TC=250K)、电荷有序转变(TCO=190K)和反铁磁转变(TN=120K).通过ESR谱线的参数随温度的变化可以观察到各个磁有序转变温度,TN相似文献   

n-Pentylamine-intercalated layered perovskite-type oxide

A novel n-pentylamine-intercalated layered perovskite-type oxide, C5H11NH3-Sr2Nb3O10, was prepared and characterized by using XRD, FT-IR, Raman spec-trascopy, and elemental analysis. It was shown that the intercalated n-pentylamine adopted a bilayer formation with some overlap and tilt, and the lattice of the perovskite layer was distorted due to the intercalation of n-pentylamine. The as-prepared sample gave clear electric hysteresis loop and did not show fatigue after 1011 switching circles, and therefore, could be considered as a new kind of fatigue-free ferroelectric materials.     

储存NOx催化剂BaZrO3的结构和性能研究

用溶胶—凝胶法制备了钙钛矿型BaZrO3催化剂，再用等量浸渍法制备了Rh／BaZrO3样品．并制备了Rh／BaZrO3／γ-Al2O3和Pt／BaZrO3／γ-Al2O3．通过DTA，XRD，XPS等方法研究了它们的结构及其对性能的影响，并对催化剂的储氮量(NSC)及其抗硫性能进行测试．结果表明，BaZrO3催化剂具有良好的储氮及抗硫性能，直接加入贵金属会使NSC降低，而混合γ-Al2O3后再加Rh，Pt则大大提高NSC，并且不论何种方式引入贵金属都使抗硫性能改善．     

稀土钙钛矿型L_aM_nO_(3 λ)催化剂的结构及对水汽转化反应活性的对比研究

在真空和空气氛中合成了两个稀土复合氧化物LaMnO3和LaMnO3.12，利用XROD测定了其晶体结构，并利用随机程序TREOR计算了晶胞参数，测试了对水汽转化反应的催化活性。并与铁铬中变催化剂进行了比较。初步解释了催化活性与结构的关系，并对其反应机理进行了推测。认为该反应属表面内反应。催化剂的晶格氧参与了反应。